US5226210A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of forming metal fiber mat/polymer composite
Assignee: 3M Co
•
Filing: 1992-01-21
•
Granted: 1993-07-13
•
Expires: 2012-01-21
Abstract
Abstract The present invention provides a metal/polymer composite comprising a polymeric substrate and a sintered mat of randomly-oriented metal fibers embedded therein, the fibers having a substantially circular cross-section and a diameter of about 10 to 200 μm. The polymeric substrate is typically a thin, flexible sheet-like material having a pair of planar surfaces. The polymeric substrate is preferably thermoformable. If thermoformability is desired the metal will have a melting point of less than the thermoforming temperature of the polymeric substrate. The thermoformable metal/polymer composite of the present invention may be stretched to at least 20%, and often can be stretched at least 200% of its original dimensions, at least in certain regions, without loss of electrical continuity or EMI shielding properties. The present invention also provides a method of making a metal/polymer composite and a sintered mat of randomly-oriented metal fibers.
Inventors
- 👤 David C. Koskenmaki
- 👤 Clyde D. Calhoun
- 👤 Pamela S. Tucker
- 👤 Robert L. Lambert, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 07:08
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/20; H01B1/22; B; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/08; B29C70/086; B29C70/088; B29C70/10; B29C70/12; B29C70/28; B29C70/40; B29C70/50; B29C70/504; B29C70/508; B29C70/88; B29C70/882; B29C70/885; B32; B32B; B32B15/00; B32B15/02; H05; H05K; H05K9/00; H05K9/0073; H05K9/0081; H05K9/009; B29K; B29K2105/00; B29K2105/06; B29K2105/12; B29K2305/00; B29K2705/00; B29K2995/00; B29K2995/0003; B29K2995/0005; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/4998; Y10T29/49988; Y10T428/00; Y10T428/12; Y10T428/12347; Y10T428/12444; Y10T428/12493; Y10T428/12535; Y10T428/12583; Y10T442/00; Y10T442/60; Y10T442/654; Y10T442/655
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
120 words
A method of forming a metal/polymer composite comprising the steps of: (a) providing a polymeric substrate; and (b) squirting at least one fine stream of a molten metal from at least one orifice into an atmosphere; (c) solidifying said at least one stream as a plurality of metal strands in the atmosphere above said substrate; (d) collecting said solidified metal strands on the substrate as a loose mat of a randomly intersecting pattern of metal strands; and (e) simultaneously embedding the loose mat into the substrate and sintering the strands of metal together at the points of intersection by passing the substrate and mat between heated rollers under pressure at a temperature less than the melting temperature of said metal.
Claim 2
Independent Claim
120 words
A method of forming a metal/polymer composite comprising the steps of: (a) providing a polymeric substrate; and (b) squirting at least one fine stream of a molten metal from at least one orifice into an atmosphere; (c) solidifying said at least one stream as a plurality of metal strands in the atmosphere above said substrate; (d) collecting said solidified metal strands on the substrate as a loose mat of a randomly intersecting pattern of metal strands; and (e) simultaneously embedding the loose mat into the substrate and sintering the strands of metal together at the points of intersection by passing the substrate and mat between heated rollers under pressure at a temperature less than the melting temperature of said metal.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein said molten metal is squirted from said at least one orifice at a pressure greater than P c .
Claim 4
Dependent Claim
29 words
The method of claim 1 wherein said substrate is a thermoformable polymer and said metal having a melting point of less than the thermoforming temperature of said polymeric substrate.
Claim 5
Dependent Claim
15 words
The method of claim 1 wherein said strands have a diameter of about 25-100 μm.
Claim 6
Dependent Claim
15 words
The method of claim 4 wherein said strands have a diameter of about 25-100 μm.
Claim 7
Dependent Claim
48 words
The method of claim 1 wherein said metal is selected from the group consisting of tin, lead, bismuth, cadmium, indium, gallium, mixtures thereof and alloys of said metals containing one or more metals selected from the group consisting of zinc, aluminum, copper, silver, gold, nickel, cobalt, and iron.
Claim 8
Dependent Claim
13 words
The method of claim 1 further including the step of thermoforming said composite.
Claim 9
Dependent Claim
27 words
The method of claim 7 wherein said composite is stretched in certain regions at least 20% in one direction during thermoforming without losing substantial electromagnetic shielding properties.
Claim 10
Dependent Claim
29 words
The method of claim 7 wherein said composite is stretched in certain regions at least 20% in more than one direction during thermoforming without losing substantial electromagnetic shielding properties.
Claim 11
Independent Claim
128 words
A method of forming a metal/polymer composite comprising the steps of: (a) squirting at least one fine stream of a molten metal from at least one orifice into an atmosphere; (b) solidifying said at least one stream as a plurality of metal strands in the atmosphere above the substrate; (c) collecting said solidified metal strands on a support forming a loose mat of a randomly intersecting pattern of metal strands; (d) passing said loose mat between two heated rollers at a temperature which is less than the melting temperature of the metal thereby sintering the strands of metal together at points of intersection to form a sintered mat; and (e) laminating said sintered mat to a polymeric substrate at a temperature below the melting temperature of said metal.
Claim 12
Independent Claim
128 words
A method of forming a metal/polymer composite comprising the steps of: (a) squirting at least one fine stream of a molten metal from at least one orifice into an atmosphere; (b) solidifying said at least one stream as a plurality of metal strands in the atmosphere above the substrate; (c) collecting said solidified metal strands on a support forming a loose mat of a randomly intersecting pattern of metal strands; (d) passing said loose mat between two heated rollers at a temperature which is less than the melting temperature of the metal thereby sintering the strands of metal together at points of intersection to form a sintered mat; and (e) laminating said sintered mat to a polymeric substrate at a temperature below the melting temperature of said metal.
Claim 13
Dependent Claim
26 words
The method of claim 10 wherein said substrate is thermoformable, said metal having a melting point of less than the thermoforming temperature of said polymeric substrate.
References Cited (Backward Citations)
US2798093A
Cited
US3091262A
Cited
US3087233A
Cited
US3506526A
Cited
US3485595A
Cited
US3410936A
Cited
US3556914A
Cited
US3713787A
Cited
US3727292A
Cited
US3888711A
Cited
US3713477A
Cited
DE2057053A1
Cited
FR2186312A1
Cited
US3811976A
Cited
US4001357A
Cited
US3996167A
Cited
US4107363A
Cited
JPS5336061A
Cited
US4269800A
Cited
DE2829035A1
Cited
JPS5634449A
Cited
JPS56131665A
Cited
JPS574766A
Cited
JPS5737462A
Cited
JPS57135155A
Cited
JPS59187847A
Cited
JPS60132742A
Cited
JPS60216453A
Cited
JPS60231764A
Cited
EP0194406A1
Cited
JPS61289200A
Cited
JPS62122746A
Cited
EP0227131A1
Cited
US4642244A
Cited
GB2189740A
Cited
US5028490A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-07-12 | 1997-01-11 | 1997-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-07-12 | 2001-01-11 | 2001-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-07-12 | 2005-01-11 | 2005-07-13 | $7700.00 | Window Closed / Lapsed |