Method for controlling thickness of single crystal thin-film layer in soi substrate
Assignee: Shin-Etsu Handotai Co Ltd
•
Filing: 1991-11-27
•
Granted: 1993-06-29
•
Expires: 2011-11-27
Abstract
Abstract A method for controlling the thickness of a single crystal thin-film silicon layer bonded on a dielectric substrate in a SOI substrate thereby effecting conversion of said single crystal silicon layer to a thin film is disclosed. To be more precise, said method comprises selectively and hypothetically dividing the entire surface of said single crystal silicon layer destined to undergo a chemical vapor-phase corrosion reaction for the sake of said conversion into necessary minute sections and, at the sametime, taking preparatory measurement of the thickness of said single crystal silicon layer in each of said minute sections, and effecting on each of said minute sections said conversion to a thin film by a chemical vapor-phase corrosion reaction adjusted in accordance with the measured thickness of layer. The conversion to a thin film is attained with the dispersion of thickness of the single crystal silicon layer controlled with high accuracy.
Inventors
- 👤 Yutaka Ohta
- 👤 Masatake Katayama
- 👤 Takao Abe
- 👤 Yasuaki Nakazato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 04:54
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/02; C30B29/06; C30B33/00; G; G01; G01B; G01B11/00; G01B11/02; G01B11/06; G01B11/0616; G01B11/0683; H; H10; H10P; H10P50/00; H10P50/20; H10P50/24; H10P50/242; H10P74/00; H10P74/20; H10P74/203; H10P74/23; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10P90/1914; H10W; H10W10/00; H10W10/10; H10W10/181
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
125 words
A method for controlling the thickness of a single crystal thin-film silicon layer bonded on a dielectric substrate in a SOI substrate thereby effecting conversion of said single crystal silicon layer to a thin film, comprising: dividing the entire surface of said single crystal silicone layer destined to undergo a chemical vapor-phase corrosion reaction for the sake of said conversion into necessary minutes sections; taking preparatory measurement of the thickness of said single crystal silicon layer in each of said minute sections; effecting on each of said minute sections said conversion to a thin film by a chemical vapor-phase corrosion reaction adjusted in accordance with the measured thickness of layer; and attaining control of the dispersion of thickness of said thin-film layer with high accuracy.
Claim 2
Independent Claim
125 words
A method for controlling the thickness of a single crystal thin-film silicon layer bonded on a dielectric substrate in a SOI substrate thereby effecting conversion of said single crystal silicon layer to a thin film, comprising: dividing the entire surface of said single crystal silicone layer destined to undergo a chemical vapor-phase corrosion reaction for the sake of said conversion into necessary minutes sections; taking preparatory measurement of the thickness of said single crystal silicon layer in each of said minute sections; effecting on each of said minute sections said conversion to a thin film by a chemical vapor-phase corrosion reaction adjusted in accordance with the measured thickness of layer; and attaining control of the dispersion of thickness of said thin-film layer with high accuracy.
Claim 3
Dependent Claim
30 words
A method according to claim 1, wherein said measurement of the thickness of said single crystal silicon layer and said adjusted chemical vapor-phase corrosion are repeated a plurality of times.
Claim 4
Dependent Claim
14 words
A method according to claim 1, wherein said dielectric substrate is quartz glass substrate.
Claim 5
Dependent Claim
59 words
A method according to claim 1, wherein said dielectric substrate is a silicon substrate having a thermal oxide film formed thereon and another single crystal substrate bonded thereto through the medium of said thermal oxide film is subjected on the exposed surface side thereof to said chemical vapor-phase corrosion for the sake of said conversion to a thin film.
Claim 6
Dependent Claim
88 words
A method according to claim 1, wherein as single crystal or polycrystalline silicon substrate is used in the place of said dielectric substrate, bonding to said single crystal or polycrystalline silicon substrate a single crystal silicon substrate having a thermal oxide film formed thereon, subsequently to said bonding, removing said oxide film from the exposed surface of said latter single crystal silicon substrate, and subjecting the exposed surface of said single crystal layer to a chemical vapor-phase corrosion for the sake of said conversion to a thin film.
Claim 7
Dependent Claim
47 words
A method according to claim 1, wherein said chemical reaction is adapted to generate fluorine or chlorine radicals by irradiation of an ultraviolet light and said conversion of said single-crystal silicon layer is effected by said chemical vapor-phase corrosion reaction induced by said fluorine or chlorine radicals.
Claim 8
Dependent Claim
49 words
A method according to claim 6, wherein an excimer laser is used as said ultraviolet light and the amount of vapor-phase corrosion of said single crystal silicon substrate by said chemical vapor-phase corrosion reaction on the laser-irradiated surface is controlled by the number of irradiating pulse of said laser.
Claim 9
Dependent Claim
95 words
A method according to claim 6, wherein one member selected from the group consisting of mercury lamp, halogen lamp, metal halide lamp, and mercury-xenon lamp is used as the source for said ultraviolet light, adjusting the time for irradiation with the ultraviolet light from said lamp by controlling the opening and shutting of a mechanical shutter serving a relevant minute section, and controlling the amount of vapor-phase corrosion of said single crystal silicon substrate by adjusting said chemical vapor-phase corrosion reaction proceeding on a relevant minute section in consequence of said irradiation with the light.
Claim 10
Independent Claim
307 words
A method for controlling the thickness of a single crystal thin-film silicon layer bonded on a dielectric substrate in a SOI substrate thereby effecting conversion of said single crystal silicon layer to a thin film comprising: dividing the entire surface of said single crystal silicon layer destined to undergo a chemical vapor-phase corrosion reaction for the sake of said conversion into necessary minute sections; taking preparatory measurement of the thickness of said single crystal silicon layer in each of said minute sections; effecting on each of said minute sections said conversion to a thin film by a chemical vapor-phase corrosion reaction adjusted in accordance with the measured thickness of layer; thereby attaining control of the dispersion of thickness of said thin-film layer with high accuracy; adapting said chemical reaction to generate fluorine or chlorine radicals by irradiation of an ultraviolet light; connecting said single crystal silicon layer by said chemical vapor-phase corrosion reaction induced by said fluorine or chlorine radicals; selecting one member from the group consisting of mercury lamp, halogen lamp, metal halide lamp, and mercury-xenon lamp as the source for said ultraviolet light; adjusting the time for irradiation with the ultraviolet light from said lamp by controlling the opening and shutting of a mechanical shutter serving a relevant minute section; controlling the amount of vapor-phase corrosion of said single crystal silicon substrate by adjusting said chemical vapor-phase corrosion reaction proceeding on a relevant minute section in consequence of said irradiation with the light; using an excimer laser for said ultraviolet light; controlling the amount of vapor-phase corrosion of said single crystal silicon substrate by said chemical vapor-phase corrosion reaction on the laser-irradiated surface by the number of irradiating pulsed of said laser, and repeating a plurality of times the measurement of the thickness of said single crystal silicon layer and said adjusted chemical vapor-phase corrosion.
Claim 11
Independent Claim
307 words
A method for controlling the thickness of a single crystal thin-film silicon layer bonded on a dielectric substrate in a SOI substrate thereby effecting conversion of said single crystal silicon layer to a thin film comprising: dividing the entire surface of said single crystal silicon layer destined to undergo a chemical vapor-phase corrosion reaction for the sake of said conversion into necessary minute sections; taking preparatory measurement of the thickness of said single crystal silicon layer in each of said minute sections; effecting on each of said minute sections said conversion to a thin film by a chemical vapor-phase corrosion reaction adjusted in accordance with the measured thickness of layer; thereby attaining control of the dispersion of thickness of said thin-film layer with high accuracy; adapting said chemical reaction to generate fluorine or chlorine radicals by irradiation of an ultraviolet light; connecting said single crystal silicon layer by said chemical vapor-phase corrosion reaction induced by said fluorine or chlorine radicals; selecting one member from the group consisting of mercury lamp, halogen lamp, metal halide lamp, and mercury-xenon lamp as the source for said ultraviolet light; adjusting the time for irradiation with the ultraviolet light from said lamp by controlling the opening and shutting of a mechanical shutter serving a relevant minute section; controlling the amount of vapor-phase corrosion of said single crystal silicon substrate by adjusting said chemical vapor-phase corrosion reaction proceeding on a relevant minute section in consequence of said irradiation with the light; using an excimer laser for said ultraviolet light; controlling the amount of vapor-phase corrosion of said single crystal silicon substrate by said chemical vapor-phase corrosion reaction on the laser-irradiated surface by the number of irradiating pulsed of said laser, and repeating a plurality of times the measurement of the thickness of said single crystal silicon layer and said adjusted chemical vapor-phase corrosion.
Claim 12
Dependent Claim
14 words
A method according to claim 9, wherein said dielectric substrate is quartz glass substrate.
Claim 13
Dependent Claim
59 words
A method according to claim 9, wherein said dielectric substrate is a silicon substrate having a thermal oxide film formed thereon and another single crystal substrate bonded thereto through the medium of said thermal oxide film is subjected on the exposed surface side thereof to said chemical vapor-phase corrosion for the sake of said conversion to a thin film.
Claim 14
Dependent Claim
88 words
A method according to claim 9, wherein a single crystal or polycrystalline silicon substrate is used in the place of said dielectric substrate, bonding to said single crystal of polycrystalline silicon substrate a single crystal silicon substrate having a thermal oxide film formed thereon, subsequently to said bonding, removing said oxide film from the exposed surface of said latter single crystal silicon substrate, and subjecting the exposed surface of said single crystal layer to a chemical vapor-phase corrosion for the sake of said conversion to a thin film.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-28 | 1996-12-28 | 1997-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-28 | 2000-12-28 | 2001-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-28 | 2004-12-28 | 2005-06-29 | $7700.00 | Window Closed / Lapsed |