Assignee: NTN Corp
•
Filing: 1991-11-08
•
Granted: 1993-06-29
•
Expires: 2011-11-08
Abstract
Abstract A steel having such a good machinability that it can be directly cut without being annealed and a good induction hardenability. The steel consists essentially of C: 0.37-0.45%, Si: up to 0.35%, Mn: more than 1.0% - up to 1.5%, B: 0.0005-0.0035%, Ti: 0.01-0.05%, Al: 0.01-0.06% and the balance of Fe, the content of N being up to 0.022 and has a fine structure of ferrite crystal grain size number 6 or more as defined by JIS-G0552. In addition to the above basic composition, the alloy may further contain some optional alloying elements. The material is suitable for manufacturing machine structural parts such as drive shafts of automobiles.
Inventors
- 👤 Tatsumi Urita
- 👤 Kunio Namiki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:09
CPC Classifications
C; C22; C22C; C22C38/00; C22C38/14; C22C38/08
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
65 words
A steel for induction hardening, which consists essentially of alloying elements, C: 0.37-0.45%, Si: up to 0.35%, Mn: more than 1.0% and up to 1.5%, B: 0.0005-0.0035%, Ti: 0.01-0.05% and Al: 0.01-0.06%, and the balance of Fe, the content of N being up to 0.022%, and has a fine structure of ferrite crystal grain size number of No. 6 or higher as defined by JIS-G0552.
Claim 2
Dependent Claim
65 words
A steel for induction hardening, which consists essentially of alloying elements, C: 0.37-0.45%, Si: up to 0.35%, Mn: more than 1.0% and up to 1.5%, B: 0.0005-0.0035%, Ti: 0.01-0.05% and Al: 0.01-0.06%, and the balance of Fe, the content of N being up to 0.022%, and has a fine structure of ferrite crystal grain size number of No. 6 or higher as defined by JIS-G0552.
Claim 3
Dependent Claim
42 words
A steel for induction hardening according to claim 1, wherein the steel, in addition to the alloying elements set forth in claim 1, further contains one or more of Cr: up to 1.0%, Mo: up to 0.20% and Ni: up to 1.0%.
Claim 4
Dependent Claim
39 words
A steel for induction hardening according to claim 1 an wherein the steel, in addition to the alloying elements set forth in claim 1, further contains one or two of V: up to 0.30% and Nb: up to 0.10%.
Claim 5
Dependent Claim
41 words
A steel for induction hardening according to claim 1, wherein the steel, in addition to the alloying elements set forth in claim 1, further further contains one or more of Pb: 0.01-0.20%, S: 0.005-0.30%, Bi: 0.01-0.10%, Te: 0.0005-0.10% and Ca: 0.0003-0.005%.
Claim 6
Dependent Claim
38 words
A steel for induction hardening according to claim 2, wherein the steel, in addition to the alloying elements set forth in claim 2, further contains one of two of V: up to 0.30% and Nb: up to 0.10%.
Claim 7
Dependent Claim
40 words
A steel for induction hardening according to claim 2, wherein the steel, in addition to the alloying elements set forth in claim 2, further contains one or more of Pb: 0.01-0.20%, S: 0.005-0.30%, Bi: 0.01-0.10%, Te: 0.0005-0.10% and Ca: 0.0003-0.005%.
Claim 8
Dependent Claim
40 words
A steel for induction hardening according to claim 3, wherein the steel, in addition to the alloying elements set forth in claim 3, further contains one or more of Pb: 0.01-0.20%, S: 0.005-0.30%, Bi: 0.01-0.10%, Te: 0.0005-0.10% and Ca: 0.0003-0.005%.
Claim 9
Dependent Claim
91 words
A steel for induction hardening, which consists essentially of allying elements, C: 0.37-0.45%, Si: up to 0.35%, Mn: 1.0-1.5%, B: 0.0005-0.0035%, TiP 0.01-0.05% and Al: 0.01-0.06%, and the balance of Fe, the content of N being up to 0.022%, said steel having a fine structure of ferrite crystal grain size as defined by JIS-G0552 of No. 6 or hither and being prepared by rolling at a temperature of up to 1,100° C., finishing at a temperature of up to 950° C., and under a reduction of area of 70% or more.
Claim 10
Dependent Claim
91 words
A steel for induction hardening, which consists essentially of allying elements, C: 0.37-0.45%, Si: up to 0.35%, Mn: 1.0-1.5%, B: 0.0005-0.0035%, TiP 0.01-0.05% and Al: 0.01-0.06%, and the balance of Fe, the content of N being up to 0.022%, said steel having a fine structure of ferrite crystal grain size as defined by JIS-G0552 of No. 6 or hither and being prepared by rolling at a temperature of up to 1,100° C., finishing at a temperature of up to 950° C., and under a reduction of area of 70% or more.
References Cited (Backward Citations)
SU645977A1
Cited
JPS5465115A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-28 | 1996-12-28 | 1997-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-28 | 2000-12-28 | 2001-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-28 | 2004-12-28 | 2005-06-29 | $7700.00 | Window Closed / Lapsed |