Composite block & process for manufacturing

Claim 2

The molded composite paving block of claim 1, wherein said elastomeric material is chosen from the group of rubber and flexible polyvinylchloride.

Claim 3

The molded composite paving block of claim 1, wherein said asphalt is in a proportion of about 40% by volume, said polyethylene is in a proportion of about 25% by volume, said monofilament fibre material is in a proportion of about 20% by volume, and said elastomeric material is in a proportion of 15% by volume.

Claim 4

The molded composite paving block of claim 1, wherein said asphalt is a size of -4 mesh, said polyethylene is of a size of -10 mesh, said elastomeric material is of a size of -12 mesh.

Claim 5

The molded composite paving block of claim 1, wherein said polyethylene is recycled polyethylene, said elastomeric material is reclaimed elastomeric material, and said monofilament fibre material is reclaimed monofilament fibre material.

Claim 6

The molded composite paving block of claim 5, wherein said elastomeric material is reclaimed rubber from scrap tires.

Claim 7

The molded composite paving block of claim 5, wherein said elastomeric material is reclaimed flexible polyvinylchloride.

Claim 8

The molded composite paving block of claim 1, wherein said monofilament fibre material is reclaimed monofilament fibre material and is chosen from the group of rayon, nylon, and polyesters.

Claim 9

The molded composite paving block of claim 1, wherein said monofilament fibre material has a strand length of about 1/8" to about 3/8".

Claim 10

The molded composite paving block of claim 1, wherein said monofilament fibre material is obtained from the cords of scrap tires.

Claim 11

Molded composite paving blocks for use in paving roads, parking lots and driveways, comprising: reclaimed asphalt in a proportion of about 25% to about 55% by volume, phenolic resin in a proportion of about 10% to about 40% by volume, monofilament fibre material in a proportion of about 5% to about 35% by volume, and elastomeric material in a proportion of 5% to about 30% by volume.

Claim 12

The molded composite paving block of claim 1, wherein said block has a compressive strength of about 7,000 p.s.i..

Claim 13

A process for manufacturing molded composite paving blocks, comprising the steps of: placing reclaimed asphalt and polyethylene into a heated blending drum; blending and heating said asphalt and said polyethylene at a temperature of about 130° F. until a relatively uniform mixture is obtained; adding an amount of elastomeric material and an amount of a monofilament fibre material to said mixture to obtain a composite material that is subsequently formed into said composite paving blocks; discharging portions of said composite material into a heating oven; allowing said composite material to temperature stabilize in said heating oven at a temperature of about 325° F. to 375° F.; and discharging said portions of said composite material from said heating oven and depositing said portions of composite material into a molding system and molding said portions of material into molded paving blocks.

Claim 14

The process of claims 13, wherein said heating oven is a continuous feed oven with a traveling belt that uses infrared heaters spaced along said oven so as to provide relatively even heating of said mixture as it travels through said oven.

Claim 15

The process of claim 13, further including the step of: applying a pressure of about 750 p.s.i. to each mold until said portion of composite material has set.

Claim 16

The process of claim 13, wherein said asphalt is waste reclaimed asphalt, said polyethylene is recycled polyethylene, said elastomeric material is reclaimed elastomeric material, and said monofilament fibre material is reclaimed monofilament fibre material.

Claim 17

The process of claim 13, wherein said elastomeric material is reclaimed rubber from scrap tires.

Claim 18

The process of claim 13, wherein said monofilament fibre material is obtained from the cords of scrap tires.

Claim 19

The process of claim 13, wherein said elastomeric material is reclaimed flexible polyvinylchloride.

Claim 20

A process for manufacturing molded composite paving blocks, comprising the steps of: placing reclaimed asphalt and polyethylene into a heated blending drum; blending and heating said asphalt and said polyethylene at a temperature of about 130° F. until a relatively uniform mixture is obtained; adding an amount of elastomeric material and an amount of a monofilament fibre material to said mixture to obtain a composite material that is subsequently formed into said composite paving blocks; discharging a continuous ribbon of said composite material into a heating oven; allowing said composite material to temperature stabilize in said heating oven at a temperature of about 325° F. to 375° F.; and discharging said continuous ribbon of said composite material from said heating oven and depositing said composite material into an extruder; pre-plasticizing and extruding said composite material; cutting said extruded composite material into a slug of desired size as it exits said extruder; and depositing said slug into a molding system and molding said material into molded paving blocks.

Claim 21

The process of claim 20, wherein said extruder is a heated extruder that keeps said mixture at a temperature of about 325° F. to about 375° F. thereby allowing it to be more easily extruded.

Claim 22

The process of claim 20, wherein said extruder is a linear extruder.

Claim 23

The process of claim 20, wherein said extruder is a screw extruder.

Claim 24

A process for manufacturing molded composite paving blocks, comprising the steps of: placing reclaimed asphalt and phenolic resin into a heated blending drum; blending and heating said asphalt and said phenolic resin at a temperature of about 130° F. until a relatively uniform mixture is obtained; adding an amount of elastomeric material and an amount of a monofilament fibre material to said mixture to obtain a composite material that is subsequently formed into said composite paving blocks; discharging portions of said composite material into a heating oven; allowing said composite material to temperature stabilize in said heating oven at a temperature of about 325° F. to 375° F.; and discharging said portions of said composite from said heating oven and depositing said portion of composite material into a molding system and molding said portion of material into a molded paving block.

Claim 25

A process for manufacturing molded composite paving blocks, comprising the steps of: placing reclaimed asphalt and phenolic resin into a heated blending drum; blending and heating said asphalt and said phenolic resin at a temperature of about 130° F. until a relatively uniform mixture is obtained; adding an amount of elastomeric material and an amount of a monofilament fibre material to said mixture to obtain a composite material that is subsequently formed into said composite paving blocks; discharging a continuous ribbon of said composite material into a heating oven; allowing said composite material to temperature stabilize in said heating oven at a temperature of about 325° F. to 375° F.; and discharging said continuous ribbon of said composite material from said heating oven and depositing said composite material into an extruder; extruding said composite material; cutting said extruded composite material into a slug of desired size as it exits said extruder; and depositing said slug into a molding system and molding said material into molded paving blocks.

Claim 26

A construction material, comprising: reclaimed asphalt in a proportion of about 25% to about 55% by volume, polyethylene in a proportion of about 10% to about 40% by volume. monofilament fibre material in a proportion of about 5% to about 35% by volume, and elastomeric material in a proportion of 5% to about 30% by volume.