Abstract
Abstract The present invention is directed to a heat shrink clad core optical conduit and to an optical conduit having either a thermoplastic, thermoset or liquid, light transmitting core surrounded by, preferably a fluoropolymer cladding which is in turn surrounded by a tight-fitting, finish polymer jacket which may be either transparent or translucent, and is preferably made of a polyvinyl chloride, polycarbonate, acrylic or silicone material. Numerous fillers and inserts may be used in the finish jacket polymer and the finish jacket polymer may be formed into various shapes. Bondable jacket materials may be used. The preferred method of forming the manufacturing jacket around a heat shrinkable fluoropolymer cladding is by extruding a low extrusion temperature polymer over a heat shrink clad in its expanded form into which an increased interior pressure is maintained to prevent shrinkage during the extrusion process. The preferred method of forming the finish jacket around a base clad core material is by an extrusion process where the finish jacket material is extruded over a heat shrink type fluoropolymer clad, in its expanded form, cured thermoset core thereby simultaneously shrinking the clad.
Inventors
- 👤 John A. Robbins
- 👤 Jamshid J. Zarian
- 👤 Sandford R. Willford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:01
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/02; G02B6/032; B; B29; B29C; B29C48/00; B29C48/03; B29C48/06; B29C48/09; G02B6/02033; G02B6/24; G02B6/36; G02B6/38; G02B6/3801; G02B6/3803; G02B6/44; G02B6/4439; G02B6/4471; G02B6/4476; G02B6/3616; G02B6/3628; G02B6/3632; G02B6/3644; Y; Y10; Y10S; Y10S264/00; Y10S264/71
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
68 words
A method of making a linear light conduit comprising the steps of: selecting a length of light transmitting monofilament core surrounded with an expanded, heat shrinkable fluoropolymer cladding as a base conduit; selecting a polymer as a finish jacket material; and extruding the polymer over the length of base conduit at a temperature sufficient to shrink the heat shrinkable cladding and to form a finish jacket optical conduit.
Claim 2
Independent Claim
68 words
A method of making a linear light conduit comprising the steps of: selecting a length of light transmitting monofilament core surrounded with an expanded, heat shrinkable fluoropolymer cladding as a base conduit; selecting a polymer as a finish jacket material; and extruding the polymer over the length of base conduit at a temperature sufficient to shrink the heat shrinkable cladding and to form a finish jacket optical conduit.
Claim 3
Independent Claim
78 words
A method of making a linear light conduit comprising the steps of: selecting a plurality of lengths of light transmitting monofilament cores each surrounded with an expanded, heat shrinkable fluoropolymer cladding; splicing the plurality of lengths to each other to form a single length of spliced base conduit; selecting a polymer as a finish jacket material; and extruding the polymer over the single length of spliced base conduit at a temperature sufficient to shrink the heat shrinkable cladding.
Claim 4
Independent Claim
78 words
A method of making a linear light conduit comprising the steps of: selecting a plurality of lengths of light transmitting monofilament cores each surrounded with an expanded, heat shrinkable fluoropolymer cladding; splicing the plurality of lengths to each other to form a single length of spliced base conduit; selecting a polymer as a finish jacket material; and extruding the polymer over the single length of spliced base conduit at a temperature sufficient to shrink the heat shrinkable cladding.
Claim 5
Dependent Claim
16 words
The method of claim 1 or 2 wherein the monofilament core is a thermoset optical polymer.
Claim 6
Dependent Claim
24 words
The method of claim 1 or 2 wherein the polymer is selected from the group consisting essentially of acrylic, polycarbonate, polyvinyl chloride and silicone.
Claim 7
Dependent Claim
136 words
The process of making a flexible, clad monofilament linear light conduit comprising the steps of: selecting a tubular heat shrink fluoropolymer cladding having a pre-expanded first inner diameter which is less than an ultimate outer diameter of a flexible cylindrical core, and said cladding having been expanded so that it has a second inner diameter greater than the ultimate outer diameter of the core; extruding over the expanded cladding, a manufacturing jacket consisting essentially of a low extrusion temperature polymer and at a temperature which is less than that required to effectuate shrinkage of the heat shrink clad; placing a polymerizable monomer mixture inside the cladding; polymerizing the mixture to form the flexible cylindrical core; removing the jacket; and applying heat to the cladding effective to shrink the cladding around the outer periphery of the core.
Claim 8
Dependent Claim
136 words
The process of making a flexible, clad monofilament linear light conduit comprising the steps of: selecting a tubular heat shrink fluoropolymer cladding having a pre-expanded first inner diameter which is less than an ultimate outer diameter of a flexible cylindrical core, and said cladding having been expanded so that it has a second inner diameter greater than the ultimate outer diameter of the core; extruding over the expanded cladding, a manufacturing jacket consisting essentially of a low extrusion temperature polymer and at a temperature which is less than that required to effectuate shrinkage of the heat shrink clad; placing a polymerizable monomer mixture inside the cladding; polymerizing the mixture to form the flexible cylindrical core; removing the jacket; and applying heat to the cladding effective to shrink the cladding around the outer periphery of the core.
Claim 9
Dependent Claim
14 words
The process of claim 5 wherein the low extrusion temperature polymer is poly(vinyl acetate).
Claim 10
Dependent Claim
14 words
The process of claim 5 wherein the low extrusion temperature polymer is a co-polymer.
Claim 11
Dependent Claim
12 words
The process of claim 7 wherein the co-polymer is ethylene-vinyl acetate co-polymer.
Claim 12
Dependent Claim
156 words
The process of making a flexible, clad monofilament linear light conduit comprising the steps of: selecting a tubular heat shrink fluoropolymer cladding having a pre-expanded first inner diameter which is less than a final outer diameter of a flexible cylindrical core, and said cladding having been expanded so that it has a second inner diameter greater than the predetermined outer diameter of the core; pressurizing the inside of the cladding above the pressure outside the cladding to establish a pressure differential; maintaining the pressure differential; extruding over the expanded cladding a manufacturing jacket consisting essentially of a low extrusion temperature polymer and at a temperature which is less than that required to effectuate shrinkage of the heat shrink cladding. placing a polymerizable monomer mixture inside the cladding; polymerizing the mixture to form the flexible core; removing the jacket; and applying heat to the cladding effective to shrink the cladding around the outer periphery of the core.
Claim 13
Dependent Claim
156 words
The process of making a flexible, clad monofilament linear light conduit comprising the steps of: selecting a tubular heat shrink fluoropolymer cladding having a pre-expanded first inner diameter which is less than a final outer diameter of a flexible cylindrical core, and said cladding having been expanded so that it has a second inner diameter greater than the predetermined outer diameter of the core; pressurizing the inside of the cladding above the pressure outside the cladding to establish a pressure differential; maintaining the pressure differential; extruding over the expanded cladding a manufacturing jacket consisting essentially of a low extrusion temperature polymer and at a temperature which is less than that required to effectuate shrinkage of the heat shrink cladding. placing a polymerizable monomer mixture inside the cladding; polymerizing the mixture to form the flexible core; removing the jacket; and applying heat to the cladding effective to shrink the cladding around the outer periphery of the core.
Claim 14
Dependent Claim
30 words
The process of claim 9 wherein the internal pressure of the cladding is maintained at about 40 to 100 pounds per square inch above the external pressure around the cladding.
Claim 15
Dependent Claim
16 words
The process of claim 9 or 10 wherein the low extrusion temperature polymer is poly(vinyl acetate).
Claim 16
Dependent Claim
15 words
The process of claim 9 or 10 wherein the low extrusion temperature polymer is poly(ethylene).
Claim 17
Dependent Claim
16 words
The process of claim 9 or 10 wherein the low extrusion temperature polymer is a co-polymer.
Claim 18
Dependent Claim
14 words
The process of claim 9 or 10 wherein the polymer is ethylene-vinyl acetate co-polymer.
Claim 19
Dependent Claim
172 words
The process of making a flexible, clad monofilament linear light conduit comprising the steps of: selecting a tubular heat shrink fluoropolymer cladding having a pre-expanded first inner diameter which is less than an ultimate outer diameter of a flexible cylindrical core, and said cladding having been expanded so that it has a second diameter greater than the ultimate outer diameter of the core; extruding over the expanded cladding a manufacturing jacket consisting essentially of a low extrusion temperature polymeric material which extrudes at a temperature which is less than that which would cause the heat shrink clad to shrink to a third diameter equal to or less than the ultimate outer diameter of the core; placing a polymerizable monomer mixture inside the cladding; polymerizing the mixture to form the flexible core; removing the jacket; and applying heat to the cladding effective to shrink the cladding to a third diameter and effective to relatively and uniformly minimize any gap between the outer periphery of the core and the inner periphery of the cladding.
Claim 20
Dependent Claim
172 words
The process of making a flexible, clad monofilament linear light conduit comprising the steps of: selecting a tubular heat shrink fluoropolymer cladding having a pre-expanded first inner diameter which is less than an ultimate outer diameter of a flexible cylindrical core, and said cladding having been expanded so that it has a second diameter greater than the ultimate outer diameter of the core; extruding over the expanded cladding a manufacturing jacket consisting essentially of a low extrusion temperature polymeric material which extrudes at a temperature which is less than that which would cause the heat shrink clad to shrink to a third diameter equal to or less than the ultimate outer diameter of the core; placing a polymerizable monomer mixture inside the cladding; polymerizing the mixture to form the flexible core; removing the jacket; and applying heat to the cladding effective to shrink the cladding to a third diameter and effective to relatively and uniformly minimize any gap between the outer periphery of the core and the inner periphery of the cladding.
Claim 21
Dependent Claim
14 words
The process of claim 15 wherein the low extrusion temperature polymer is poly(vinyl acetate).
Claim 22
Dependent Claim
29 words
The process of claim 15 wherein the first inner diameter of the heat shrink clad is about ninety percent or less of the ultimate outer diameter of the core.
Claim 23
Dependent Claim
14 words
The process of claim 15 wherein the low extrusion temperature polymer is a co-polymer.
Claim 24
Dependent Claim
12 words
The process of claim 18 wherein the co-polymer is ethylene-vinyl acetate co-polymer.
Claim 25
Dependent Claim
211 words
The process of making a flexible, clad monofilament linear light conduit comprising the steps of: selecting a tubular heat shrink fluoropolymer cladding having a pre-expanded first inner diameter which is less than a ultimate diameter of a flexible cylindrical core, and said cladding having been expanded so that it has a second diameter greater than the ultimate outer diameter of the core; pressurizing and maintaining pressure inside of the cladding, in an expanded form, at a pressure sufficient to prevent shrinkage during an extrusion process to a third diameter which is equal to or less than the ultimate outer diameter of the core; while maintaining the pressure inside the cladding, extruding over the cladding a manufacturing jacket consisting essentially of a low extrusion temperature polymer material which will extrude at a temperature which is high enough to cause shrinking the heat shrink cladding, said pressure inside the cladding preventing said shrinking; placing a polymerizable monomer mixture inside the cladding; polymerizing the mixture to form the flexible core; removing the jacket; and applying heat to the cladding effective to shrink the cladding around the third diameter and effective to relatively and uniformly minimize any gap which may exist between the outer periphery of the core, and the inner periphery of the cladding.
Claim 26
Dependent Claim
211 words
The process of making a flexible, clad monofilament linear light conduit comprising the steps of: selecting a tubular heat shrink fluoropolymer cladding having a pre-expanded first inner diameter which is less than a ultimate diameter of a flexible cylindrical core, and said cladding having been expanded so that it has a second diameter greater than the ultimate outer diameter of the core; pressurizing and maintaining pressure inside of the cladding, in an expanded form, at a pressure sufficient to prevent shrinkage during an extrusion process to a third diameter which is equal to or less than the ultimate outer diameter of the core; while maintaining the pressure inside the cladding, extruding over the cladding a manufacturing jacket consisting essentially of a low extrusion temperature polymer material which will extrude at a temperature which is high enough to cause shrinking the heat shrink cladding, said pressure inside the cladding preventing said shrinking; placing a polymerizable monomer mixture inside the cladding; polymerizing the mixture to form the flexible core; removing the jacket; and applying heat to the cladding effective to shrink the cladding around the third diameter and effective to relatively and uniformly minimize any gap which may exist between the outer periphery of the core, and the inner periphery of the cladding.
Claim 27
Dependent Claim
23 words
The process of claim 20 wherein the pressure inside of the cladding is maintained at about 40 to 100 pounds per square inch.
Claim 28
Dependent Claim
16 words
The process of claim 20 or 21 where the low extrusion temperature polymer is poly(vinyl acetate).
Claim 29
Dependent Claim
15 words
The process of claim 20 or 21 where the low extrusion temperature polymer is poly(ethylene).
Claim 30
Dependent Claim
29 words
The process of claim 20 or 21 wherein the inner first diameter of the cladding is about ninety percent or less than the ultimate outer diameter of the core.
Claim 31
Dependent Claim
16 words
The process of claim 20 or 21 wherein the low extrusion temperature polymer is a co-polymer.
Claim 32
Dependent Claim
12 words
The process of claim 25 wherein the co-polymer is ethylene-vinyl acetate co-polymer.
References Cited (Backward Citations)
US3641332A
Cited
US3810802A
Cited
US3919037A
Cited
US4195980A
Cited
US4753509A
Cited
US4804246A
Cited
US4865412A
Cited
US4844578A
Cited
US4957347A
Cited
US5052778A
Cited
US5067831A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-21 | 1996-12-21 | 1997-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-21 | 2000-12-21 | 2001-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-21 | 2004-12-21 | 2005-06-22 | $7700.00 | Window Closed / Lapsed |