Water sensitive hot melt adhesives for nonwoven applications
Assignee: National Starch and Chemical Investment Holding Corp
•
Filing: 1991-05-07
•
Granted: 1993-06-08
•
Expires: 2011-05-07
Abstract
Abstract Nonwoven assemblies bonded with water dispersible or sensitive hot melt adhesives comprising 50-100 parts of a graft copolymer of about 40-85% of at least one vinyl monomer and about 15-60% of at least one water soluble polyalkylene oxide polymer, and about 0-50 parts by weight of tackifying resin. The compositions may also be employed as water sensitive binders in the manufacture of the nonwoven. Vinyl acetate is the preferred vinyl monomer whereas ethylene oxide homo- or copolymers are the preferred polyalkylene oxide. The use of tackifying resin is optional and may be undesirable for many of the applications.
Inventors
- 👤 Francis Brady
- 👤 Gary Raykovitz
- 👤 Paul Puletti
- 👤 Thomas Kauffman
- 👤 Jules Schoenberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:01
CPC Classifications
C; C09; C09J; C09J151/00; C09J151/08; C08; C08F; C08F283/00; C08F283/06; D; D04; D04H; D04H1/00; D04H1/40; D04H1/42; D04H1/4282; D04H1/4291; D04H1/58; D04H1/587; D04H1/593; D04H1/60; Y; Y10; Y10T; Y10T442/00; Y10T442/60; Y10T442/659; Y10T442/674; Y10T442/678; Y10T442/693
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
121 words
A process for bonding nonwoven fabric substrates to similar or dissimilar substrates comprising the steps of applying to at least one substrate a molten hot melt adhesive composition, said adhesive having a Tg of -40° to +40° C. comprising 50-100% of a graft copolymer comprising (a) 40-85 weight percent of at least one vinyl monomer and (b) 15-60 weight percent of at least one polyalkylene oxide polymer having a molecular weight greater than 3000 and a polymerized ethylene oxide content of at least 50% by weight, and 0-50 parts by weight of a compatible tackifying resin; and bonding another substrate thereto; the process being characterized in that the bond of the resulting construction will release when exposed to ambient temperature water.
Claim 2
Dependent Claim
121 words
A process for bonding nonwoven fabric substrates to similar or dissimilar substrates comprising the steps of applying to at least one substrate a molten hot melt adhesive composition, said adhesive having a Tg of -40° to +40° C. comprising 50-100% of a graft copolymer comprising (a) 40-85 weight percent of at least one vinyl monomer and (b) 15-60 weight percent of at least one polyalkylene oxide polymer having a molecular weight greater than 3000 and a polymerized ethylene oxide content of at least 50% by weight, and 0-50 parts by weight of a compatible tackifying resin; and bonding another substrate thereto; the process being characterized in that the bond of the resulting construction will release when exposed to ambient temperature water.
Claim 3
Dependent Claim
14 words
The process of claim 1 wherein the dissimilar substrate is a low density polyolefin.
Claim 4
Dependent Claim
14 words
The process of claim 1 wherein the adhesive comprises 100% of the graft copolymer.
Claim 5
Dependent Claim
24 words
The process of claim 1 wherein the adhesives comprises 50-95% of the graft copolymer and 5-50 parts by weight of a compatible tackifying resin.
Claim 6
Dependent Claim
26 words
The process of claim 1 wherein a superabsorbent particulate polymer is bonded to a nonwoven substrate and wherein the adhesive comprises 100% of the graft copolymer.
Claim 7
Dependent Claim
17 words
The process of claim 1 wherein the adhesive is applied in a spray or melt blown pattern.
Claim 8
Dependent Claim
64 words
The process of claim 1 wherein the adhesive additionally comprises up to 25% by weight of a diluent selected from the group consisting of glycerol mono-and distearate, synthetic long chain linear polymeric alcohols, stearic acid, high acid number waxlike materials of mono- or dicarboxylic acids, acid wax derived from montan wax, stearyl alcohol, hydrogenated castor oil, ethoxylated alcohols, 12(OH) stearic acid and stearic-cetyl alcohol.
Claim 9
Dependent Claim
9 words
An article produced by the process of claim 1.
Claim 10
Dependent Claim
9 words
The article of claim 8 comprising a disposable diaper.
Claim 11
Dependent Claim
110 words
A process for the production of a nonwoven substrate comprising the step of bonding nonwoven fibers with a binder composition having a Tg of -40° to +40° C. comprising 50-100% of a graft copolymer comprising (a) 40-85 weight percent of at least one vinyl monomer and (b)15-60 weight percent of at least one polyalkylene oxide polymer having a molecular weight greater than 3000 and a polymerized ethylene oxide content of at least 50% by weight and 0-50 parts by weight of a compatible tackifying resin, and bonding another substrate thereto; the process being characterized in that the bond of the resulting construction will release when exposed to ambient temperature water.
Claim 12
Dependent Claim
110 words
A process for the production of a nonwoven substrate comprising the step of bonding nonwoven fibers with a binder composition having a Tg of -40° to +40° C. comprising 50-100% of a graft copolymer comprising (a) 40-85 weight percent of at least one vinyl monomer and (b)15-60 weight percent of at least one polyalkylene oxide polymer having a molecular weight greater than 3000 and a polymerized ethylene oxide content of at least 50% by weight and 0-50 parts by weight of a compatible tackifying resin, and bonding another substrate thereto; the process being characterized in that the bond of the resulting construction will release when exposed to ambient temperature water.
Claim 13
Dependent Claim
125 words
A process for bonding nonwoven fabric substrates to similar or dissimilar substrates comprising the steps of applying to at least one substrate a molten hot melt adhesive composition, said adhesive having a Tg of -40° to +40° C. comprising 50-70 weight percent of a graft copolymer, said copolymer comprising (a) 40-85 weight percent of at least one vinyl monomer and (b) 15-60 weight percent of at least one polyalkylene oxide polymer having a molecular weight greater than 3000 and a polymerized ethylene oxide content of at least 50% by weight, and 30-50 parts by weight of a compatible tackifying resin, and bonding another substrate thereto; the process being characterized in that the bond of the resulting construction will release when exposed to ambient temperature water.
Claim 14
Dependent Claim
125 words
A process for bonding nonwoven fabric substrates to similar or dissimilar substrates comprising the steps of applying to at least one substrate a molten hot melt adhesive composition, said adhesive having a Tg of -40° to +40° C. comprising 50-70 weight percent of a graft copolymer, said copolymer comprising (a) 40-85 weight percent of at least one vinyl monomer and (b) 15-60 weight percent of at least one polyalkylene oxide polymer having a molecular weight greater than 3000 and a polymerized ethylene oxide content of at least 50% by weight, and 30-50 parts by weight of a compatible tackifying resin, and bonding another substrate thereto; the process being characterized in that the bond of the resulting construction will release when exposed to ambient temperature water.
Claim 15
Dependent Claim
28 words
The process of claim 11 wherein the polyalkylene oxide polymer in the hot melt adhesive comprises an ethylene oxide propylene oxide copolymer containing at least 75% ethylene oxide.
Claim 16
Dependent Claim
99 words
A process for bonding nonwoven fabric substrates to similar or dissimilar substrates comprising the steps of applying to at least one substrate a molten hot melt adhesive composition, said adhesive having a Tg of -40° to +40° C. comprising 50-100% of a graft copolymer wherein the graft copolymer comprises 20-80% vinyl acetate, 5-65% vinyl 2-ethylhexanoate or butyl acrylate and 15-60% of at least one polyalkylene oxide polymer and 0-50% of a compatible tackifying resin, and bonding another substrate thereto; the process being characterized in that the bond of the resulting construction will release when exposed to ambient temperature water.
Claim 17
Dependent Claim
99 words
A process for bonding nonwoven fabric substrates to similar or dissimilar substrates comprising the steps of applying to at least one substrate a molten hot melt adhesive composition, said adhesive having a Tg of -40° to +40° C. comprising 50-100% of a graft copolymer wherein the graft copolymer comprises 20-80% vinyl acetate, 5-65% vinyl 2-ethylhexanoate or butyl acrylate and 15-60% of at least one polyalkylene oxide polymer and 0-50% of a compatible tackifying resin, and bonding another substrate thereto; the process being characterized in that the bond of the resulting construction will release when exposed to ambient temperature water.
Claim 18
Dependent Claim
28 words
The process of claim 13 wherein the polyalkylene oxide polymer in the hot melt adhesive comprises an ethylene oxide propylene oxide copoylmer containing at least 75% ethylene oxide.
Claim 19
Dependent Claim
112 words
A disposable product containing incorporated therein superabsorbent particulate polymers, wherein the polymers are bonded into the disposable product using a hot melt adhesive having a Tg of -40° to +40° C. and comprising 50-100% by weight of a graft copolymer comprising (a) 40-85 weight percent of at least one vinyl monomer and (b) 15-60 weight percent of at least one polyalkylene oxide polymer having a molecular weight greater than 3000 and a polymerized ethylene oxide content of at least 50% by weight, and 0-50 parts by weight of a compatible tackifying resin; the product being characterized in that the bond of the resulting construction will release when exposed to ambient temperature water.
Claim 20
Dependent Claim
112 words
A disposable product containing incorporated therein superabsorbent particulate polymers, wherein the polymers are bonded into the disposable product using a hot melt adhesive having a Tg of -40° to +40° C. and comprising 50-100% by weight of a graft copolymer comprising (a) 40-85 weight percent of at least one vinyl monomer and (b) 15-60 weight percent of at least one polyalkylene oxide polymer having a molecular weight greater than 3000 and a polymerized ethylene oxide content of at least 50% by weight, and 0-50 parts by weight of a compatible tackifying resin; the product being characterized in that the bond of the resulting construction will release when exposed to ambient temperature water.
Claim 21
Dependent Claim
20 words
The disposable product of claim 15 wherein the polymers are bonded with an adhesive comprising 100% of the graft copolymer.
References Cited (Backward Citations)
US3033841A
Cited
GB922457A
Cited
US3369948A
Cited
US3666595A
Cited
US3891584A
Cited
US4675209A
Cited
GB2133345A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-07 | 1996-12-07 | 1997-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-07 | 2000-12-07 | 2001-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-07 | 2004-12-07 | 2005-06-08 | $7700.00 | Window Closed / Lapsed |