Lead-free mirrors and environmentally safe manufacture thereof
Assignee: Cardinal CG Co
•
Filing: 1992-10-08
•
Granted: 1993-06-01
•
Expires: 2012-10-08
Abstract
Abstract Mirrors are formed in an environmentally compatible and substantially pollution-free manner by a sputtering process in which a transparent substrate such as glass has first sputtered upon it a primer layer and then a reflective layer of silver or other bright reflective metal. A barrier layer is provided over the reflective layer to protect the latter from corrosive environments. If the transmittance of the reflective layer is greater than zero percent, the barrier layer includes a different bright reflective metal sufficient to reduce the transmittance of the combined reflective and barrier layers to zero percent. The mirror includes a lead free polymeric protective layer spaced further from the transparent substrate than the barrier layer. The inclusion of zinc pigment in the polymeric coating provides sulfiding protection, and the use of an outer sputtered on film of zinc or zinc oxide provides substantial adhesion thereto of the polymeric coating.
Inventors
- 👤 Zephuren J. Hughes
- 👤 Marion M. Jeskey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:45
CPC Classifications
G; G02; G02B; G02B5/00; G02B5/08; G02B5/0816; G02B5/085; G02B5/0858; G02B5/0866; C; C03; C03C; C03C17/00; C03C17/34; C03C17/36; C03C17/3602; C03C17/3613; C03C17/3618; C03C17/3626; C03C17/3639; C03C17/3644; C03C17/3652; C03C17/3657; C03C17/3663; C03C17/3689; C03C17/3692; C23; C23C; C23C14/00; C23C14/06; C23C14/10; C23C14/14; C23C14/18; G02B1/105; G02B1/00; G02B1/10; G02B1/14; G02B5/0808; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12549; Y10T428/12556; Y10T428/12569; Y10T428/12576; Y10T428/12597; Y10T428/12611; Y10T428/12993
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
155 words
A mirror comprising a transparent substrate, a sputtered primer layer carried on the transparent substrate, a reflective layer comprising a bright, reflective metal sputtered onto the primer layer, and a barrier layer spaced further from the transparent substrate than the reflective layer and comprising one or more metal compounds different from the metal of the reflective layer, the barrier layer being of sufficient thickness to protect the reflective layer from corrosive environments, the barrier layer including a sufficient amount of a bright, reflective metal different from the reflective metal of the reflective layer to reduce the transmittance of the combined reflective layer and barrier layer to zero percent if the transmittance of the reflective layer is greater than zero percent, and the barrier layer including an outer sputtered-on zinc-containing layer, the mirror including, over the zinc-containing layer and tightly adherent thereto, a hydrolysis and solvent-resistant, hard, pigmented polymeric protective layer applied from an aqueous composition.
Claim 2
Dependent Claim
155 words
A mirror comprising a transparent substrate, a sputtered primer layer carried on the transparent substrate, a reflective layer comprising a bright, reflective metal sputtered onto the primer layer, and a barrier layer spaced further from the transparent substrate than the reflective layer and comprising one or more metal compounds different from the metal of the reflective layer, the barrier layer being of sufficient thickness to protect the reflective layer from corrosive environments, the barrier layer including a sufficient amount of a bright, reflective metal different from the reflective metal of the reflective layer to reduce the transmittance of the combined reflective layer and barrier layer to zero percent if the transmittance of the reflective layer is greater than zero percent, and the barrier layer including an outer sputtered-on zinc-containing layer, the mirror including, over the zinc-containing layer and tightly adherent thereto, a hydrolysis and solvent-resistant, hard, pigmented polymeric protective layer applied from an aqueous composition.
Claim 3
Dependent Claim
25 words
The mirror of claim 1 wherein the sputtered-on, zinc containing layer comprises an outer surface of zinc oxide in contact with the polymeric protective layer.
Claim 4
Dependent Claim
27 words
The mirror of claim 2 wherein the pigmented polymeric protective layer includes one or more zinc-containing pigments sufficient to improve the resistance of the mirror to sulfiding.
Claim 5
Dependent Claim
12 words
The mirror of claim 3 wherein the zinc pigment includes zinc phosphate.
Claim 6
Dependent Claim
18 words
The mirror of any one of claims 1-4 including a separate outer coating of a non-pigmented polymeric coating.
Claim 7
Dependent Claim
18 words
The mirror of any of claims 1-4 wherein the outer polymeric protective layer is a crosslinked acrylic resin.
Claim 8
Dependent Claim
169 words
A mirror comprising a transparent substrate, a sputtered primer layer carried on the transparent substrate, a reflective layer comprising a bright, reflective metal sputtered onto the primer layer, and a barrier layer spaced further from the transparent substrate than the reflective layer and comprising one or more metal compounds different from the metal of the reflective layer, the barrier layer being of sufficient thickness to protect the reflective layer from corrosive environments, the barrier layer including a sufficient amount of a bright, reflective metal different from the reflective metal of the reflective layer to reduce the transmittance of the combined reflective layer and barrier layer to zero percent if the transmittance of the reflective layer is greater than zero percent, and the barrier layer including an outer sputtered-on zinc-containing layer having a zinc oxide outer surface, the mirror including, over the zinc-containing layer and tightly adherent thereto, a hydrolysis and solvent-resistant, hard, cross-linked acrylic protective layer including zinc-containing pigment sufficient to improve the resistance of the mirror to sulfiding.
Claim 9
Dependent Claim
169 words
A mirror comprising a transparent substrate, a sputtered primer layer carried on the transparent substrate, a reflective layer comprising a bright, reflective metal sputtered onto the primer layer, and a barrier layer spaced further from the transparent substrate than the reflective layer and comprising one or more metal compounds different from the metal of the reflective layer, the barrier layer being of sufficient thickness to protect the reflective layer from corrosive environments, the barrier layer including a sufficient amount of a bright, reflective metal different from the reflective metal of the reflective layer to reduce the transmittance of the combined reflective layer and barrier layer to zero percent if the transmittance of the reflective layer is greater than zero percent, and the barrier layer including an outer sputtered-on zinc-containing layer having a zinc oxide outer surface, the mirror including, over the zinc-containing layer and tightly adherent thereto, a hydrolysis and solvent-resistant, hard, cross-linked acrylic protective layer including zinc-containing pigment sufficient to improve the resistance of the mirror to sulfiding.
Claim 10
Dependent Claim
156 words
Method of manufacturing mirrors in a substantially pollution-free manner, comprising the steps of a. sputtering onto a transparent substrate a primer layer, a bright, reflective metallic layer, and a barrier layer spaced further from the transparent substrate than the reflective layer, the barrier layer including a sufficient amount of a bright, reflective metal different from the reflective metal of the reflective layer to reduce the transmittance of the combined reflective layer and barrier layer to zero percent if the transmittance of the reflective layer is greater than zero percent, the barrier layer containing a final layer having a zinc oxide outer surface, b. applying to the zinc oxide outer surface an aqueous coating composition comprising a heat-curable polymer system, the coating composition thoroughly wetting the zinc oxide surface, and c. evaporating water from the coating and curing the coating onto the zinc oxide surface to provide the latter with a hard, tenaceously adherent, protective polymeric overcoat.
Claim 11
Dependent Claim
156 words
Method of manufacturing mirrors in a substantially pollution-free manner, comprising the steps of a. sputtering onto a transparent substrate a primer layer, a bright, reflective metallic layer, and a barrier layer spaced further from the transparent substrate than the reflective layer, the barrier layer including a sufficient amount of a bright, reflective metal different from the reflective metal of the reflective layer to reduce the transmittance of the combined reflective layer and barrier layer to zero percent if the transmittance of the reflective layer is greater than zero percent, the barrier layer containing a final layer having a zinc oxide outer surface, b. applying to the zinc oxide outer surface an aqueous coating composition comprising a heat-curable polymer system, the coating composition thoroughly wetting the zinc oxide surface, and c. evaporating water from the coating and curing the coating onto the zinc oxide surface to provide the latter with a hard, tenaceously adherent, protective polymeric overcoat.
Claim 12
Dependent Claim
28 words
The substantially pollution free method of claim 8 including the step of providing over said polymeric layer a second polymeric coating composition, and heat curing the latter coating.
Claim 13
Dependent Claim
36 words
The substantially pollution-free method of claim 9 wherein said second polymeric coating composition is applied over the first coating while the first coating is wet, and the coatings are cured together in a single curing step.
Claim 14
Dependent Claim
28 words
The substantially pollution-free method of claim 8 including the step of providing in the coating composition sufficient zinc pigments to increase the resistance of the mirror to sulfiding.
Claim 15
Dependent Claim
128 words
Method of manufacturing mirrors in a substantially pollution-free manner, comprising the steps of a. sputtering onto a transparent substrate a bright, reflective metallic layer, and a barrier layer spaced further from the transparent substrate than the reflective layer, the barrier layer containing a final layer having a zinc oxide outer surface, b. applying to the zinc oxide outer surface an aqueous coating composition comprising a heat-curable polymer system comprising an acrylic resin and a curing agent therefor, the coating composition thoroughly wetting the zinc oxide surface and including sufficient zinc pigments to increase the resistance of the mirror to sulfiding, and c. evaporating water from the coating and heat-curing the coating onto the zinc oxide surface to provide the latter with a hard, tenaceously adherent, protective polymeric overcoat.
Claim 16
Dependent Claim
128 words
Method of manufacturing mirrors in a substantially pollution-free manner, comprising the steps of a. sputtering onto a transparent substrate a bright, reflective metallic layer, and a barrier layer spaced further from the transparent substrate than the reflective layer, the barrier layer containing a final layer having a zinc oxide outer surface, b. applying to the zinc oxide outer surface an aqueous coating composition comprising a heat-curable polymer system comprising an acrylic resin and a curing agent therefor, the coating composition thoroughly wetting the zinc oxide surface and including sufficient zinc pigments to increase the resistance of the mirror to sulfiding, and c. evaporating water from the coating and heat-curing the coating onto the zinc oxide surface to provide the latter with a hard, tenaceously adherent, protective polymeric overcoat.
Claim 17
Dependent Claim
34 words
The substantially pollution-free method of claim 12 including the step of providing over the agent-containing polymeric layer a coating of an aqueous, pigment-free, heat curable polymeric coating composition, and heat curing the latter coating.
Claim 18
Dependent Claim
32 words
The substantially pollution-free method of claim 13 in which the pigment-free coating composition is applied as a wet film over the pigmented coating while the latter is in a wet film stage.
References Cited (Backward Citations)
US1977639A
Cited
US2123049A
Cited
FR1258659A
Cited
US4009947A
Cited
US4340646A
Cited
JPS58149002A
Cited
US4563400A
Cited
US4692389A
Cited
US4948677A
Cited
US4780372A
Cited
US4707405A
Cited
US4666263A
Cited
US4690871A
Cited
US4880668A
Cited
US4898790A
Cited
US4883721A
Cited
US4902580A
Cited
US4898789A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-05-31 | 1996-11-30 | 1997-06-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-05-31 | 2000-11-30 | 2001-06-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-05-31 | 2004-11-30 | 2005-06-01 | $7700.00 | Window Closed / Lapsed |