US5215645A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Electrodeposited foil with controlled properties for printed circuit board applications and procedures and electrolyte bath solutions for preparing the same
Assignee: Gould Electronics Inc
•
Filing: 1989-09-13
•
Granted: 1993-06-01
•
Expires: 2009-09-13
Abstract
Abstract Copper conductive foil for use in preparing printed circuit boards is electrodeposited from an electrolyte solution containing copper ions, sulphate ions, animal glue and thiourea. The thiourea operates to decrease the roughness of the foil, to enable operation at higher current densities and/or to modify the ductility characteristics of the foil.
Inventors
- 👤 Dino F. DiFranco
- 👤 Sidney J. Clouser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:34
CPC Classifications
H; H05; H05K; H05K1/00; H05K1/02; H05K1/09; C; C25; C25D; C25D1/00; C25D1/04; C25D3/00; C25D3/02; C25D3/38; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; Y; Y10; Y10T; Y10T428/00; Y10T428/12
Claims Analysis
Total Claims: 41
Claim 1
Independent Claim
158 words
A process for electrolytically forming copper foil for use in printed circuit board applications comprising: A) providing an electrolyte solution containing copper ions and sulfate ions wherein said electrolyte solution has immersed therein an anode and a cathode; B) continuously supplying to said electrolyte solution a quantity of a gelatin component consisting essentially of high-protein polymers of amino acids linked by peptide chains having molecular weights in the range of from about 10,000 to about 300,000 and a quantity of an active sulfur containing component having a bivalent sulfur atom wherein both bonds of which are directly connected to a carbon atom together with one or more nitrogen atoms also directly connected to the carbon atom wherein said quantities are sufficient to produce an IPC-CF-150E Class 1 copper foil; and C) applying a voltage across said anode and cathode immersed in said electrolyte solution to thereby cause the electrodeposition of a Class 1 copper foil at said cathode.
Claim 2
Dependent Claim
158 words
A process for electrolytically forming copper foil for use in printed circuit board applications comprising: A) providing an electrolyte solution containing copper ions and sulfate ions wherein said electrolyte solution has immersed therein an anode and a cathode; B) continuously supplying to said electrolyte solution a quantity of a gelatin component consisting essentially of high-protein polymers of amino acids linked by peptide chains having molecular weights in the range of from about 10,000 to about 300,000 and a quantity of an active sulfur containing component having a bivalent sulfur atom wherein both bonds of which are directly connected to a carbon atom together with one or more nitrogen atoms also directly connected to the carbon atom wherein said quantities are sufficient to produce an IPC-CF-150E Class 1 copper foil; and C) applying a voltage across said anode and cathode immersed in said electrolyte solution to thereby cause the electrodeposition of a Class 1 copper foil at said cathode.
Claim 3
Dependent Claim
158 words
A process for electrolytically forming copper foil for use in printed circuit board applications comprising: A) providing an electrolyte solution containing copper ions and sulfate ions wherein said electrolyte solution has immersed therein an anode and a cathode; B) continuously supplying to said electrolyte solution a quantity of a gelatin component consisting essentially of high-protein polymers of amino acids linked by peptide chains having molecular weights in the range of from about 10,000 to about 300,000 and a quantity of an active sulfur containing component having a bivalent sulfur atom wherein both bonds of which are directly connected to a carbon atom together with one or more nitrogen atoms also directly connected to the carbon atom wherein said quantities are sufficient to produce an IPC-CF-150E Class 3 copper foil; and C) applying a voltage across said anode and cathode immersed in said electrolyte solution to thereby cause the electrodeposition of a Class 3 copper foil at said cathode.
Claim 4
Dependent Claim
158 words
A process for electrolytically forming copper foil for use in printed circuit board applications comprising: A) providing an electrolyte solution containing copper ions and sulfate ions wherein said electrolyte solution has immersed therein an anode and a cathode; B) continuously supplying to said electrolyte solution a quantity of a gelatin component consisting essentially of high-protein polymers of amino acids linked by peptide chains having molecular weights in the range of from about 10,000 to about 300,000 and a quantity of an active sulfur containing component having a bivalent sulfur atom wherein both bonds of which are directly connected to a carbon atom together with one or more nitrogen atoms also directly connected to the carbon atom wherein said quantities are sufficient to produce an IPC-CF-150E Class 3 copper foil; and C) applying a voltage across said anode and cathode immersed in said electrolyte solution to thereby cause the electrodeposition of a Class 3 copper foil at said cathode.
Claim 5
Dependent Claim
39 words
The process as set forth in claim 1, wherein said quantity of said active sulphur containing component is sufficient for decreasing the roughness of a 1 oz. electrodeposited copper foil to an R tm of less than about 5.0.
Claim 6
Dependent Claim
28 words
The process as set forth in claim 1, wherein said quantity of said active sulphur containing component is sufficient for increasing the tensile strength of the electrodeposited foil.
Claim 7
Dependent Claim
45 words
The process as set forth in claim 1, wherein said quantity of said active sulphur containing component is sufficient to enable increasing the current for electrolytically forming said copper foil to greater than about 500 ASF without substantially altering the basic characteristics of the foil.
Claim 8
Dependent Claim
41 words
The process as set forth in claim 5, wherein said quantity of said active sulphur containing component is sufficient to enable increasing said current from about 500 ASF to about 1500 ASF without substantially altering the basic characteristics of the foil.
Claim 9
Dependent Claim
63 words
The process as set forth in claim 2, wherein said quantity of gelatine component is present in an amount sufficient to facilitate the production of an IPC Class 3 foil and said quantity of said active sulphur containing component is sufficient for decreasing the roughness of a 1 oz. electrodeposited IPC Class 3 foil to an R tm of less than about 7.0.
Claim 10
Dependent Claim
70 words
The process as set forth in claim 7, wherein said quantity of said gelatine component is present in an amount sufficient to facilitate the production of an IPC Class 3 foil and said quantity of said active sulphur containing component is sufficient to enable increasing the current for electrolytically forming said copper foil to greater than about 500 ASF without substantially altering the basic Class 3 characteristics of the foil.
Claim 11
Dependent Claim
41 words
The process as set forth in claim 8, wherein said quantity of said active sulphur containing component is sufficient to enable increasing said current from about 500 ASF to about 1500 ASF without substantially altering the basic characteristics of the foil.
Claim 12
Dependent Claim
15 words
The process as set forth in claim 1, wherein said gelatine component comprises animal glue.
Claim 13
Dependent Claim
16 words
The process as set forth in claim 10, wherein said active sulphur containing component comprises thiourea.
Claim 14
Dependent Claim
55 words
The process as set forth in claim 11, wherein said animal glue is added to said solution at a rate in the range of from about 0.2 mg/min.kA to about 20 mg/min.kA and said thiourea is added to said solution at a rate in the range of from about 1.25 mg/min.kA to about 50 mg/min.kA.
Claim 15
Dependent Claim
55 words
The process as set forth in claim 11, wherein said animal glue is added to said solution at a rate in the range of from about 5 mg/min.kA to about 20 mg/min.kA and said thiourea is added to said solution at a rate in the range of from about 10 mg/min.kA to about 50 mg/min.kA.
Claim 16
Dependent Claim
55 words
The process as set forth in claim 11, wherein said animal glue is added to said solution at a rate in the range of from about 8 mg/min.kA to about 10 mg/min.kA and said thiourea is added to said solution at a rate in the range of from about 20 mg/min.kA to about 30 mg/min.kA.
Claim 17
Dependent Claim
50 words
The process as set forth in claim 2, wherein said gelatine component is animal glue and is added to said solution at a rate less than about 5 mg/min.kA and said active sulfur component is thiourea and is added to said solution at a rate less than about 10 mg/min.kA.
Claim 18
Dependent Claim
39 words
The process as set forth in claim 15, wherein said animal glue is added to said solution at a rate of about 0.3 mg/min.kA and said thiourea is added to said solution at a rate of about 5 mg/min.kA.
Claim 19
Dependent Claim
110 words
An electrolytic bath for electrodepositing copper foil for printed circuit board applications comprising an aqueous solution containing copper ions, sulphate ions, a quantity of a gelatine component consisting essentially of high protein polymers of amino acids linked by peptide chains having molecular weights in the range of from about 10,000 to about 300,000 and a roughness decreasing quantity of an active sulphur containing component having a bivalent sulfur atom wherein both bonds of which are directly connected to a carbon atom together with one or more nitrogen atoms also connected to the carbon atom wherein said quantities are sufficient to produce an IPC-CF-150E Class 1 or Class 3 copper foil.
Claim 20
Dependent Claim
110 words
An electrolytic bath for electrodepositing copper foil for printed circuit board applications comprising an aqueous solution containing copper ions, sulphate ions, a quantity of a gelatine component consisting essentially of high protein polymers of amino acids linked by peptide chains having molecular weights in the range of from about 10,000 to about 300,000 and a roughness decreasing quantity of an active sulphur containing component having a bivalent sulfur atom wherein both bonds of which are directly connected to a carbon atom together with one or more nitrogen atoms also connected to the carbon atom wherein said quantities are sufficient to produce an IPC-CF-150E Class 1 or Class 3 copper foil.
Claim 21
Dependent Claim
17 words
An electrolytic bath as set forth in claim 17, wherein said active sulphur containing component is thiourea.
Claim 22
Dependent Claim
16 words
An electrolytic bath as set forth in claim 17, wherein said gelatine component is animal glue.
Claim 23
Dependent Claim
27 words
An electrolytic bath as set forth in claim 19, wherein said animal glue is present in an amount ranging from about 0.044 ppm to about 4.4 ppm.
Claim 24
Dependent Claim
27 words
An electrolytic bath as set forth in claim 18, wherein said quantity of thiourea present in said bath ranges from about 0.28 ppm to about 11.1 ppm.
Claim 25
Dependent Claim
32 words
A 2 oz. copper foil as set forth in claim 17 having a tensile strength of at least 25,000 psi and an elongation of greater than 5% as measured at 180° C.
Claim 26
Dependent Claim
22 words
A copper foil as set forth in claim 17, wherein said foil is electrolytically deposited at a current density of 1100 ASF.
Claim 27
Dependent Claim
30 words
A copper foil as set forth in claim 17 having a tensile strength of at least 65,000 psi and an elongation of greater than 12% as measured at room temperature.
Claim 28
Dependent Claim
25 words
A 2 oz. copper foil for printed circuit board applications having IPC-CF-150E Class 1 properties and an R tm of less than about 8.0 μm.
Claim 29
Dependent Claim
25 words
A 2 oz. copper foil for printed circuit board applications having IPC-CF-150E Class 1 properties and an R tm of less than about 8.0 μm.
Claim 30
Dependent Claim
24 words
A 1 oz. copper foil for printed circuit applications having IPC-CF-150E Class 1 properties and an R tm of less than about 5 μm.
Claim 31
Dependent Claim
24 words
A 1 oz. copper foil for printed circuit applications having IPC-CF-150E Class 1 properties and an R tm of less than about 5 μm.
Claim 32
Dependent Claim
25 words
A 1/2 oz. copper foil for printed circuit board applications having IPC-CF-150E Class 1 properties and an R tm of less than about 4.6 μm.
Claim 33
Dependent Claim
25 words
A 1/2 oz. copper foil for printed circuit board applications having IPC-CF-150E Class 1 properties and an R tm of less than about 4.6 μm.
Claim 34
Dependent Claim
15 words
A low profile copper foil for printed circuit board applications having IPC-CF-150E Class 3 properties.
Claim 35
Dependent Claim
15 words
A low profile copper foil for printed circuit board applications having IPC-CF-150E Class 3 properties.
Claim 36
Dependent Claim
25 words
A 2 oz. copper foil for printed circuit board applications having IPC-CF-150E Class 3 properties and an R tm of less than about 11 μm.
Claim 37
Dependent Claim
25 words
A 2 oz. copper foil for printed circuit board applications having IPC-CF-150E Class 3 properties and an R tm of less than about 11 μm.
Claim 38
Dependent Claim
25 words
A 1 oz. copper foil for printed circuit board applications having IPC-CF-150E Class 3 properties and an R tm of less than about 7 μm.
Claim 39
Dependent Claim
25 words
A 1 oz. copper foil for printed circuit board applications having IPC-CF-150E Class 3 properties and an R tm of less than about 7 μm.
Claim 40
Dependent Claim
25 words
A 1/2 oz. copper foil for printed circuit board applications having IPC-CF-150E Class 3 properties and an R tm of less than about 5 μm.
Claim 41
Dependent Claim
25 words
A 1/2 oz. copper foil for printed circuit board applications having IPC-CF-150E Class 3 properties and an R tm of less than about 5 μm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-05-31 | 1996-11-30 | 1997-06-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-05-31 | 2000-11-30 | 2001-06-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-05-31 | 2004-11-30 | 2005-06-01 | $7700.00 | Window Closed / Lapsed |