Abrasive grain, method of making same and abrasive products
Assignee: 3M Co
•
Filing: 1992-07-28
•
Granted: 1993-05-25
•
Expires: 2012-07-28
Abstract
Abstract An improved abrasive grain comprising the sintered product of a porous non-sintered particle having a coating of inorganic material thereon is provided. A preferred method of making such abrasive grains comprises coating the porous base particles with inorganic particles. The preferred step of coating comprises a step of mixing the base particles with a suspension containing the inorganic particles in a carrier fluid. The porous base particles having the coating of inorganic particles thereon are sintered, to generate the ceramic abrasive grain product. The abrasive grains may be incorporated, to advantage, in a variety of abrasive products including for example bonded abrasives, nonwoven abrasive products and coated abrasive products.
Inventors
- 👤 Ahmet Celikkaya
- 👤 Jerald A. Scherger
- 👤 Vernon M. Wald
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:29
CPC Classifications
B; B24; B24D; B24D11/00; B24D13/00; B24D13/02; B24D13/12; B24D3/00; B24D3/02; B24D3/04; B24D3/14; B24D3/16; B24D3/34; C; C09; C09K; C09K3/00; C09K3/14; C09K3/1436; C09K3/1445
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
164 words
A method of making ceramic abrasive grain characterized by each abrasive particle thereof being comprised of an alpha-alumina-based core with an exterior surface having a coating of particulate inorganic material autogenously bonded to the exterior surface, said method comprising the steps of: (a) providing a mass of porous first particles comprising alpha-alumina precursor material each particle of which is sinterable to an alpha-alumina-based abrasive grain; (b) mixing with said mass, in the presence of a liquid, mass of second particles having the same or different composition and are much finer than said first particles until the second particles are distributed over the exterior surface of each first particle, said second particles being capable of autogenous bonding to the exterior surface of said first particles upon sintering of said first particles; and (c) heating said particles to remove said liquid and then to sinter said first particles and cause autogenous bonding of said second particles to the exterior surface of each of said first particles.
Claim 2
Independent Claim
164 words
A method of making ceramic abrasive grain characterized by each abrasive particle thereof being comprised of an alpha-alumina-based core with an exterior surface having a coating of particulate inorganic material autogenously bonded to the exterior surface, said method comprising the steps of: (a) providing a mass of porous first particles comprising alpha-alumina precursor material each particle of which is sinterable to an alpha-alumina-based abrasive grain; (b) mixing with said mass, in the presence of a liquid, mass of second particles having the same or different composition and are much finer than said first particles until the second particles are distributed over the exterior surface of each first particle, said second particles being capable of autogenous bonding to the exterior surface of said first particles upon sintering of said first particles; and (c) heating said particles to remove said liquid and then to sinter said first particles and cause autogenous bonding of said second particles to the exterior surface of each of said first particles.
Claim 3
Dependent Claim
68 words
A method according to claim 1 wherein said step (b) is selected from the group of steps consisting of: A. (i) adding said second particles to said liquid to provide a dispersion; and (ii) adding said dispersion to said porous first particles; and B. (i) adding said liquid to said porous first particles to provide liquid-impregnated particles; and (ii) mixing said second particles with said liquid impregnated particles.
Claim 4
Dependent Claim
12 words
A method according to claim 1 wherein said liquid includes modifier precursor.
Claim 5
Dependent Claim
53 words
A method according to claim 3 wherein said step of impregnating comprises impregnating with modifier precursor material selected from the group consisting of salts of: magnesium; zinc; cobalt; iron; nickel; zirconium; manganese; silicon; hafnium; chromium; yttrium; praseodymium; samarium; ytterbium; neodymium; lanthanum; gadolinium; cerium; dysprosium; erbium; titanium; and mixtures of two or more thereof.
Claim 6
Dependent Claim
77 words
A method according to claim 1 wherein said second particles are comprised of a material selected from the group consisting of: transitional alumina, alpha alumina, hydrated aluminas, yttria, magnesia, rare earth metal oxide material, zinc oxide, iron oxide, silica, silicate material, chrome oxide, titanium oxide, nickel oxide, yttrium alumina garnet, hexagonal rare earth aluminate, alumina zirconia, zirconia, silicon nitride, alumina oxynitride, titanium carbide, titanium nitride, silicon alumina oxynitride, silicon aluminum oxycarbide and combinations two or more thereof.
Claim 7
Dependent Claim
17 words
A method according to claim 1 wherein said porous first particles include metal oxide precursor material therein.
Claim 8
Dependent Claim
17 words
A method according to claim 1 wherein said porous first particles are calcined prior to step (b).
Claim 9
Dependent Claim
52 words
A method according to claim 2 wherein said step of adding the porous first particles to the second particles comprises mixing at least 50 ml of said liquid as a carrier fluid having second particles suspended therein for each 100 grams of porous first particles to be coated to provide a mixture.
Claim 10
Dependent Claim
32 words
A method according to claim 8 wherein said mixture comprises between about 0.01% and 30%, by weight, of said second particles, based on total weight of said second particles and carrier fluid.
Claim 11
Dependent Claim
44 words
A method according to claim 1 wherein said step (b) comprises mixing a sufficient amount of said second particles with said first particles to form a coating of said second particles covering at least 70% of the exterior surface area of said first particles.
Claim 12
Dependent Claim
41 words
A method according to claim 1 wherein said step (b) comprises mixing of a sufficient amount of said second particles with said porous first particles to form a coating thereon which has a thickness of about 0.5 to about 2.0 micrometers.
Claim 13
Dependent Claim
64 words
A method according to claim 1 wherein said second particles have an average size within the range of about 0.01 micrometer to about 20 micrometers and said mixing provides said particles which are filled with liquid to provide wet porous first pores therein at least 70% saturated with said liquid; wherein said adding involves adding dry said second particles to said wet first particles.
Claim 14
Dependent Claim
64 words
A method according to claim 1 wherein said first particles have an average size within the range of about 0.01 micrometer to about 20 micrometers and said mixing involves first mixing said first and said second particles to provide a mixture and then adding a sufficient amount of liquid to the mixture, with further mixing, to at least 70% saturate said porous first particles.
Claim 15
Dependent Claim
11 words
Ceramic abrasive grain prepared according to the process of claim 1.
Claim 16
Dependent Claim
57 words
Ceramic abrasive grain comprising: (a) sintered particles having an average particle size within the range of about 20 micrometers to about 4000 micrometers, each particle comprising: (i) an alpha-alumina-based core; and (ii) a coating of inorganic particulates autogenously bonded to said alpha-alumina-based core; said coating covering at least 70% of the surface area of the alpha-alumina-based core.
Claim 17
Dependent Claim
57 words
Ceramic abrasive grain comprising: (a) sintered particles having an average particle size within the range of about 20 micrometers to about 4000 micrometers, each particle comprising: (i) an alpha-alumina-based core; and (ii) a coating of inorganic particulates autogenously bonded to said alpha-alumina-based core; said coating covering at least 70% of the surface area of the alpha-alumina-based core.
Claim 18
Dependent Claim
19 words
Ceramic abrasive grain according to claim 15 wherein said coating has a density up to about 80% of theoretical.
Claim 19
Dependent Claim
21 words
Ceramic abrasive according to claim 15 wherein said coating of inorganic particulates is between about 0.5 and about 10.0 micrometers thick.
Claim 20
Dependent Claim
23 words
Ceramic abrasive grain according to claim 15 wherein said coating of inorganic particulates comprises a region of at least 3 layers of particulates.
Claim 21
Dependent Claim
17 words
Ceramic abrasive grain according to claim 15 wherein said alpha-alumina-based core comprises alpha-alumina and metal oxide modifier.
Claim 22
Dependent Claim
19 words
Ceramic abrasive grain according to claim 15 wherein said sintered particles have a core which has a seeded microstructure.
Claim 23
Dependent Claim
23 words
Ceramic abrasive grain according to claim 15 wherein said coating comprises material selected from the group consisting of zirconia, alpha-alumina and mixtures thereof.
Claim 24
Dependent Claim
24 words
Ceramic abrasive grain according to claim 15 wherein said alpha-alumina-based core comprises a sintered reaction product of a rare earth metal oxide with alumina.
Claim 25
Dependent Claim
51 words
Ceramic abrasive grain according to claim 15 wherein said alpha-alumina-based core includes a central portion and an outer portion wherein: (i) said central portion includes therein a platelet product comprised of the reaction of a metal oxide modifier and alpha-alumina precursor; and, (ii) said outer portion comprises a seeded alpha-alumina-based microstructure.
Claim 26
Dependent Claim
33 words
An abrasive product comprising: (a) a binder; and (b) a plurality of abrasive grains secured within said abrasive product by said binder; said abrasive grains comprising the ceramic abrasive grain of claim 15.
Claim 27
Dependent Claim
20 words
An abrasive product according to claim 24 including a substrate to which said abrasive grains are bound by said binder.
Claim 28
Dependent Claim
15 words
An abrasive product according to claim 24 wherein said substrate is a non-woven fibrous mat.
Claim 29
Dependent Claim
13 words
An abrasive product according to claim 24 in the form of a wheel.
References Cited (Backward Citations)
US1528543A
Cited
US1910444A
Cited
US2314340A
Cited
US3029160A
Cited
US3269815A
Cited
US4252544A
Cited
US4311489A
Cited
US4278449A
Cited
US4249913A
Cited
US4314827A
Cited
US4518397A
Cited
US4472173A
Cited
US4623364A
Cited
US4737163A
Cited
US4734104A
Cited
US4744802A
Cited
US4652275A
Cited
US4770671A
Cited
EP0293163A2
Cited
US4881951A
Cited
US5009675A
Cited
JPH0297457A
Cited
US5102429A
Cited
US5011508A
Cited
US4913708A
Cited
US4964883A
Cited
US5042991A
Cited
EP0394213A1
Cited
US4997461A
Cited
US5131923A
Cited
US5085671A
Cited
US5131926A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-05-24 | 1996-11-23 | 1997-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-05-24 | 2000-11-23 | 2001-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-05-24 | 2004-11-23 | 2005-05-25 | $7700.00 | Window Closed / Lapsed |