Wire rod for high strength and high toughness fine steel wire, high strength and high toughness fine steel wire, twisted products using the fine steel wires, and manufacture of the fine steel wire
Assignee: Kobe Steel Ltd
•
Filing: 1991-12-27
•
Granted: 1993-05-18
•
Expires: 2011-12-27
Abstract
Abstract The fine steel wire according to the present invention has a high strength and high toughness, which is used as a rubber reinforcing material for a belt cord or tire cord, or as missile wires. Such a fine steel wire can be obtained by drawing a wire rod for a fine steel wire properly adjusted in its composition and structure, while applying working strain such that the total reduction of area in the final wire drawing step becomes 95% or more.
Inventors
- 👤 Shinzo Ashida
- 👤 Nobuhiko Ibaraki
- 👤 Katsuji Mizutani
- 👤 Kenji Ochiai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:17
CPC Classifications
C; C22; C22C; C22C38/00; C22C38/08; C21; C21D; C21D8/00; C21D8/06; C21D9/00; C21D9/52; C22C38/04; C22C38/10; C22C38/105; C22C38/12; C22C38/16; C22C38/18; C22C38/30; D; D07; D07B; D07B1/00; D07B1/06; D07B1/0606; D07B1/066; C21D2211/00; C21D2211/003
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
132 words
A wire rod for a high strength and high toughness fine steel wire, containing 0.85-1.2 wt % of C, less than 0.45 wt % of Si, and 0.3-1.0 wt % of Mn, one or more of elements selected from the group consisting of 0.1-4.0 wt % of Ni and 0.05-4.0 wt % of Co, the balance being essentially Fe and inevitable impurities, wherein Al, N, P and S among the impurities are restricted as 0.005 wt % or less of Al, 0.005 wt % or less of N, 0.02 wt % or less of P and 0.015 wt % or less of S, and the average area ratio of the pro-eutectoid cementite in an as-rolled state or in a rolled and re-heat treated state is specified at 10 wt % or less.
Claim 2
Dependent Claim
132 words
A wire rod for a high strength and high toughness fine steel wire, containing 0.85-1.2 wt % of C, less than 0.45 wt % of Si, and 0.3-1.0 wt % of Mn, one or more of elements selected from the group consisting of 0.1-4.0 wt % of Ni and 0.05-4.0 wt % of Co, the balance being essentially Fe and inevitable impurities, wherein Al, N, P and S among the impurities are restricted as 0.005 wt % or less of Al, 0.005 wt % or less of N, 0.02 wt % or less of P and 0.015 wt % or less of S, and the average area ratio of the pro-eutectoid cementite in an as-rolled state or in a rolled and re-heat treated state is specified at 10 wt % or less.
Claim 3
Dependent Claim
47 words
The wire rod for a high strength and high toughness fine steel wire as defined in claim 1, further containing one or more of elements selected from the group consisting of 0.05-0.5 wt % of Cu, 0.05-0.5 wt % of Cr and 0.02-0.5 wt % of W.
Claim 4
Dependent Claim
52 words
The wire rod for a high strength and high toughness fine steel wire as defined in claim 1, further containing one or more of elements selected from the group consisting of 0.05-0.5 wt % of V, 0.01-0.1 wt % of Nb, 0.05-0.1 wt % of Zr and 0.02-0.5 wt % of Mo.
Claim 5
Dependent Claim
79 words
The wire rod for a high strength and high toughness fine steel wire as defined in claim 1, further containing one or more of elements selected from the group consisting of 0.05-0.5 wt % of Cu, 0.05-0.5 wt % of Cr, 0.02-0.5 wt % of W, and one or more of elements selected from the group consisting of 0.05-0.5 wt % of V, 0.01-0.1 wt % of Nb, 0.05-0.1 wt % of Zr and 0.02-0.5 wt % of Mo.
Claim 6
Dependent Claim
84 words
The wire rod for a high strength and high toughness fine steel wire as defined in any one of claim 1, wherein the composition of non-metallic inclusions to the entire amount thereof is specified as, (a) Al 2 O 3 : 20 wt % or less, MnO: 40% or less, SiO 2 : 20 to 70 wt %, or (b) Al 2 O 3 : 20 wt % or less, CaO: 50 wt % or less, SiO 2 : 20 to 70 wt %.
Claim 7
Independent Claim
175 words
A method of manufacturing a high strength and high toughness fine steel wire, which comprise drawing a wire rod into a fine wire steel of 0.4 mm or less in diameter, and applying a working strain thereto such that reduction of total area upon the wire drawing after final patenting becomes 95% or more, and wherein said wire rod contains 0.85-1.2 wt % of C, less than 0.45 wt. % of Si, and 0.3-1.0 wt % of Mn, one or more elements selected from the group consisting of 0.1-4.0 wt. % of Ni and 0.05-4.0 wt. % of Co, the balance being essentially Fe and inevitable impurities, wherein Al, N, P and S among the impurities are restricted as 0.005 wt. % or less of Al, 0.005 wt. % or less of N, 0.02 wt. % or less of P and 0.015 wt. % or less of S, and having an average area ratio of proeutectoid cementite in an as-rolled state or in a rolled and re-heat treated state of 10 wt. % or less.
Claim 8
Independent Claim
175 words
A method of manufacturing a high strength and high toughness fine steel wire, which comprise drawing a wire rod into a fine wire steel of 0.4 mm or less in diameter, and applying a working strain thereto such that reduction of total area upon the wire drawing after final patenting becomes 95% or more, and wherein said wire rod contains 0.85-1.2 wt % of C, less than 0.45 wt. % of Si, and 0.3-1.0 wt % of Mn, one or more elements selected from the group consisting of 0.1-4.0 wt. % of Ni and 0.05-4.0 wt. % of Co, the balance being essentially Fe and inevitable impurities, wherein Al, N, P and S among the impurities are restricted as 0.005 wt. % or less of Al, 0.005 wt. % or less of N, 0.02 wt. % or less of P and 0.015 wt. % or less of S, and having an average area ratio of proeutectoid cementite in an as-rolled state or in a rolled and re-heat treated state of 10 wt. % or less.
Claim 9
Dependent Claim
37 words
The method of claim 6, wherein said wire rod further contains one or more elements selected from the group consisting of 0.05-0.5 wt % of Cu, 0.05-0.5 wt T of Cr and 0.02-0.5 wt % of W.
Claim 10
Dependent Claim
42 words
The method of claim 6, wherein said wire rod further contains one or more elements selected from the group consisting of 0.05-0.5 wt % of V, 0.01-0.1 wt % of Nb, 0.05-0.1 wt % of Zr and 0.02-0.5 wt T of Mo.
Claim 11
Dependent Claim
62 words
The method of claim 6, wherein the wire rod further contains non-metallic inclusions in the amount of: (a) Al 2 O 3 : 20 wt. % or less, MnO: 40% or less, SiO 2 : 20-70 wt. %, or (b) Al 2 O 3 : 20 wt. % or less, CaO: 50 wt. % or less, SiO 2 : 20-70 wt. %.
Claim 12
Dependent Claim
60 words
A high strength and high toughness fine steel wire having a diameter of 0.4 mm or less manufactured by said method as defined in claim 6, wherein said fine steel wire has a tensile strength (kgf/mm 2 ) not less than a value of 270-(130×log 10 D) (D: wire diameter (mm)) and a reduction of area not less than 35%.
Claim 13
Dependent Claim
60 words
A high strength and high toughness fine steel wire having a diameter of 0.4 mm or less manufactured by said method as defined in claim 7, wherein said fine steel wire has a tensile strength (kgf/mm 2 ) not less than a value of 270-(130×log 10 D) (D: wire diameter (mm)) and a reduction of area not less than 35%.
Claim 14
Dependent Claim
15 words
A twisted product made by twisting said fine steel wires as defined in claim 10.
Claim 15
Dependent Claim
15 words
A twisted product made by twisting said fine steel wires as defined in claim 11.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-05-17 | 1996-11-16 | 1997-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-05-17 | 2000-11-16 | 2001-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-05-17 | 2004-11-16 | 2005-05-18 | $7700.00 | Window Closed / Lapsed |