Biodecomposable or biodisintegrable moldable material
Assignee: CHUOKAGAKU Ltd
•
Filing: 1991-02-26
•
Granted: 1993-04-27
•
Expires: 2011-02-26
Abstract
Abstract A biodecomposable or biodisintegrable moldable material which comprises a mixture of 10-70 vol. % of a natural high molecular substance, 30-70 vol. % of a thermoplastic resin and 0-45 vol. % of a filler.
Inventors
- 👤 Yutaka Tokiwa
- 👤 Masahiro Suzuki
- 👤 Masatoshi Koyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:15
CPC Classifications
C; C08; C08L; C08L101/00; C08L2201/00; C08L2201/06; Y; Y10; Y10S; Y10S428/00; Y10S428/903; Y10T; Y10T428/00; Y10T428/13; Y10T428/1348; Y10T428/1352; Y10T428/1372; Y10T428/25; Y10T428/252; Y10T428/254; Y10T428/259; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2998
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
184 words
A biodecomposable or biodisintegrable moldable material in the form of porous granules each having a diameter of 0.1-20 mm and including (a) a plurality of thermoplastic resin particles which are fuse-bonded to each other, (b) a naturally-occurring high molecular weight substance which is in the form of particles having an average volume within the range of 4.2×1/10 3 μm 3 -520× 10 3 μm 3 or in the form of fibers having a diameter of less than 100 μm and a length of less than 10 mm, and (c) a filler which is in the form of particles having an average volume within the range of 4.2×1/10 3 μm 3 -910×10 3 μm 3 or in the form of fibers having a diameter of less than 100 μm and a length of less than 10 mm, said naturally-occurring high molecular weight substance and said filler being attached to the outer surfaces of said thermoplastic resin particles, said thermoplastic resin, said naturally-occurring high molecular weight substance and said filler being present in amounts of 30-70% by volume, 10-70% by volume and 0-45% by volume, respectively.
Claim 2
Dependent Claim
184 words
A biodecomposable or biodisintegrable moldable material in the form of porous granules each having a diameter of 0.1-20 mm and including (a) a plurality of thermoplastic resin particles which are fuse-bonded to each other, (b) a naturally-occurring high molecular weight substance which is in the form of particles having an average volume within the range of 4.2×1/10 3 μm 3 -520× 10 3 μm 3 or in the form of fibers having a diameter of less than 100 μm and a length of less than 10 mm, and (c) a filler which is in the form of particles having an average volume within the range of 4.2×1/10 3 μm 3 -910×10 3 μm 3 or in the form of fibers having a diameter of less than 100 μm and a length of less than 10 mm, said naturally-occurring high molecular weight substance and said filler being attached to the outer surfaces of said thermoplastic resin particles, said thermoplastic resin, said naturally-occurring high molecular weight substance and said filler being present in amounts of 30-70% by volume, 10-70% by volume and 0-45% by volume, respectively.
Claim 3
Dependent Claim
16 words
A biodecomposable moldable material according to claim 1, wherein the thermoplastic resin is a biodecomposable resin.
Claim 4
Dependent Claim
34 words
A moldable material according to claim 2 wherein said biodecomposable resin is selected from the group consisting of polyhydroxybutyrate, polyhydroxybutyrate derivatives, polycaprolactones, polyethyleneadipate, aliphatic polyesters, and copolymers of cycloaliphatic polyesters with other thermoplastic resins.
Claim 5
Dependent Claim
24 words
A biodisintegrable moldable material according to claim 1, wherein the thermoplastic resin is a mixed resin of a biodecomposable resin and a non-biodecomposable resin.
Claim 6
Dependent Claim
62 words
A moldable material according to claim 4 wherein said biodecomposable resin is a member selected from the group consisting of polyhydroxybutyrate, polyhydroxybutyrate derivatives, polycaprolactones, polyethyleneadipate, aliphatic polyesters, and copolymers of cycloaliphatic polyesters with other thermoplastic resins and wherein said non-biodecomposable resin is selected from the group consisting of polyethylene, polypropylene, polymethylpentene, ethylene-vinyl acetate copolymer, polyesters, vinyl resins, styrene resins, polyamides and polycarbonates.
Claim 7
Dependent Claim
32 words
A biodisintegrable moldable material according to claim 4, wherein the proportion of the biodecomposable resin in the mixed resin is 1-80 tw. % based on the total weight of the mixed resin.
Claim 8
Dependent Claim
37 words
A moldable material according to claim 1 wherein said naturally-occurring high molecular weight substance is selected from the group consisting of starches, starch copolymers with vinyl monomers, plant powders, cellulosic fibers, gums, animal proteins and plant proteins.
Claim 9
Dependent Claim
20 words
A biodecomposable or biodisintegrable molded article obtained from the biodecomposable or biodisintegrable moldable material as set forth in claim 1.
Claim 10
Dependent Claim
18 words
A molded article according to claim 8, wherein the article has a moisture-proof film on the surface thereof.
Claim 11
Dependent Claim
105 words
A biodecomposable or biodisintegrable moldable material in the form of porous granules, each of said granules having a diameter of 0.1-20 mm and including 30-80% by volume of a plurality of biodegradable, thermoplastic resin particles which are fuse bonded to each other and 20-70% by volume of a filler which is in the form of particles having an average volume within the range of 4.2×1/10 3 μm-910×10 3 μm 3 or in the form of fibers having a diameter of less than 100 μm and a length of less than 10 mm and which is attached to the outer surfaces of said thermoplastic resin particles.
Claim 12
Dependent Claim
105 words
A biodecomposable or biodisintegrable moldable material in the form of porous granules, each of said granules having a diameter of 0.1-20 mm and including 30-80% by volume of a plurality of biodegradable, thermoplastic resin particles which are fuse bonded to each other and 20-70% by volume of a filler which is in the form of particles having an average volume within the range of 4.2×1/10 3 μm-910×10 3 μm 3 or in the form of fibers having a diameter of less than 100 μm and a length of less than 10 mm and which is attached to the outer surfaces of said thermoplastic resin particles.
Claim 13
Dependent Claim
16 words
A biodecomposable molded article obtained from the biodisintegrable moldable material as set forth in claim 10.
Claim 14
Dependent Claim
40 words
A moldable material according to claim 10 wherein said filler is selected from the group consisting of talc, calcium carbonate, clay, silica, alumina, glass powder, metal powder, thermocurable resin powder, mica, metal flake, glass fibers, carbonaceous fibers and mineral fibers.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-04-26 | 1996-10-26 | 1997-04-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-04-26 | 2000-10-26 | 2001-04-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-04-26 | 2004-10-26 | 2005-04-27 | $7700.00 | Window Closed / Lapsed |