Preceramic compositions and ceramic products with an unsaturated organic or organosilicon compound
Assignee: Albemarle Corp
•
Filing: 1991-01-15
•
Granted: 1993-03-30
•
Expires: 2011-01-15
Abstract
Abstract A crosslinkable preceramic composition suitable for use as an infiltrant for porous ceramics, such as fiber-reinforced ceramic composites, comprises about 75-99% by weight of a low molecular weight polysilazane and about 1-25% by weight of an unsaturated organic or organosilicon compound containing at least two alkenyl groups, preferably methylvinylcyclosilazane. Infiltration of composites with the infiltrant can be accomplished by melt or solution infiltration, and the subsequent pyrolysis of the infiltrant results in the formation of a densified ceramic article having improved strength.
Inventors
- 👤 Eric W. Liimatta
- 👤 Yuan-Fu Yu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 12:41
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/16; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/589; C04B35/71; C04B35/78; C04B35/80
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
33 words
A crosslinkable preceramic composition comprising about 75-99% by weight of a low molecular weight polysilazane and about 1-25% by weight of an unsaturated organic or organosilicon compound containing at least two alkenyl groups.
Claim 2
Dependent Claim
33 words
A crosslinkable preceramic composition comprising about 75-99% by weight of a low molecular weight polysilazane and about 1-25% by weight of an unsaturated organic or organosilicon compound containing at least two alkenyl groups.
Claim 3
Dependent Claim
52 words
The composition of claim 1 wherein the polysilazane is a polymer which has been prepared by reacting an organodihalosilane with ammonia and polymerizing the ammonolysis product with a basic deprotonation catalyst and which has a relative viscosity of 1.12-1.16, measured as a solution of 5% by weight of the polymer is tetrahydrofuran.
Claim 4
Dependent Claim
17 words
The composition of claim 2 wherein the organodihalosilane is methyldichlorosilane and the basic catalyst is potassium hydride.
Claim 5
Dependent Claim
13 words
The composition of claim 1 wherein the unsaturated compound is an organosilicon compound.
Claim 6
Dependent Claim
114 words
The composition of claim 4 wherein the organosilicon compound is a compound corresponding to one of the formulas: SiE.sub.4, [R.sub.m (E).sub.3-m Si].sub.2 Z.sub.n, and cyclo[R.sub.p (E).sub.2-p SiT].sub.q wherein E is a substituted or unsubstituted vinyl or allyl group; Z is O, S, NH, NR', methylene, ethylene, phenylene, or other organic bridge; T is O, S, NH, NR', methylene, CH═CH, or C═C; R and R' are independently selected from substituted and unsubstituted alkyl groups containing 1-6 carbons and substituted and unsubstituted aryl groups containing 6-10 carbons; m is 0, 1, or 2; n and p represent 0 or 1; and q is at least 3 when T is O and is otherwise at least 2.
Claim 7
Dependent Claim
23 words
The composition of claim 5 wherein the organosilicon compound is one or more compounds corresponding to the formula cyclo[R(CH 2 ═CH)SiNH] q .
Claim 8
Dependent Claim
15 words
The composition of claim 6 wherein R is methyl and q is at least 3.
Claim 9
Dependent Claim
16 words
The composition of claim 1 containing a free radical initiator as a catalyst to promote crosslinking.
Claim 10
Dependent Claim
80 words
The composition of claim 8 comprising about 85% by weight of a polysilazane which has been prepared by reacting methyldichlorosilane with ammonia and polymerizing the ammonolysis product with potassium hydride and which has a relative viscosity of 1.12-1.16, measured as a solution of 5% by weight of the polymer in tetrahydrofuran, and about 15% by weight of at least one unsaturated organosilicon compound corresponding to the formula cyclo[CH 3 (CH 2 ═CH)SiNH] q in which q is at least 3.
Claim 11
Dependent Claim
13 words
A ceramic derived by pyrolyzing the composition of claim 1 at 850°-1400° C.
Claim 12
Dependent Claim
22 words
A fiber-reinforced ceramic composite densified with interspersed areas of a ceramic derived by pyrolyzing the composition of claim 1 at 850°-1400° C.
Claim 13
Dependent Claim
91 words
A process which comprises preparing a densified fiber-reinforced ceramic composite by immersing a porous fiber-reinforced ceramic composite in a liquid comprising the composition of claim 1 to infiltrate the pores of the composite with the composition, recovering the infiltrated composite, heating the infiltrated composite at 850°-1400° C. to pyrolyze the infiltrant, and optionally repeating the infiltration and pyrolysis one or more times to increase the densification of the composite; the pore of the porous composite optionally being subjected to removal of air therefrom before the composite is immersed in the liquid.
Claim 14
Dependent Claim
35 words
The process of claim 12 wherein the liquid in which the porous composite is immersed is a melt of the infiltrant and the infiltration is effected at a temperature of at least about 100° C.
Claim 15
Dependent Claim
12 words
The process of claim 13 wherein the infiltration is effected under pressure.
Claim 16
Dependent Claim
26 words
The process of claim 14 wherein the infiltration is effected at a temperature of about 100°-300° C. and a pressure of at least about 1.4 MPa.
Claim 17
Dependent Claim
23 words
The process of claim 15 wherein the porous composite is subjected to removal of air therefrom before it is immersed in the liquid.
Claim 18
Dependent Claim
98 words
The process of claim 16 wherein the infiltrant is a crosslinkable composition comprising (A) about 85% by weight of a polysilazane which has been prepared by reacting methyldichlorosilane with ammonia and polymerizing the ammonolysis product with potassium hydride and which has a relative viscosity of 1.12-1.16, measured as a solution of 5% by weight of the polymer in tetrahydrofuran, (B) about 15% by weight of at least one unsaturated organosilicon compound corresponding to the formula cyclo[CH 3 (CH 2 ═CH)SiNH] q in which q is at least 3, and (C) a catalytic amount of a free radical initiator.
Claim 19
Dependent Claim
25 words
The process of claim 12 wherein the liquid in which the porous composite is immersed is a solution of the infiltrant in an organic solvent.
Claim 20
Dependent Claim
98 words
The process of claim 18 wherein the infiltrant is a crosslinkable composition comprising (A) about 85% by weight of a polysilazane which has been prepared by reacting methyldichlorosilane with ammonia and polymerizing the ammonolysis product with potassium hydride and which has a relative viscosity of 1.12-1.16, measured as a solution of 5% by weight of the polymer in tetrahydrofuran, (B) about 15% by weight of at least one unsaturated organosilicon compound corresponding to the formula cyclo[CH 3 (CH 2 ═CH)SiNH] q in which q is at least 3, and (C) a catalytic amount of a free radical initiator.
Claim 21
Dependent Claim
59 words
A composition suitable for use in forming the matrix of a fiber/matrix composite and comprising about 30-60% by weight of the composition of claim 1 and about 70-40% by weight of a ceramic powder selected from silicon carbide, silicon nitride, and mixtures thereof or a mixture thereof with up to about 30% by weight of one or more polysilazanes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-03-29 | 1996-09-28 | 1997-03-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-03-29 | 2000-09-28 | 2001-03-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-03-29 | 2004-09-28 | 2005-03-30 | $7700.00 | Window Closed / Lapsed |