Assignee: Basell Technology Co BV
•
Filing: 1991-06-26
•
Granted: 1993-03-23
•
Expires: 2011-06-26
Abstract
Abstract Essentially syndiotactic crystalline copolymers of propylene with minor proportions of 1-butene, endowed with good mechanical properties, lowered melting point and limited solubility in xylene at 25° C. and the process for their preparation by polymerizing mixtures of propylene with 1-butene, by using catalysts obtained form stereorigid and chiral zirconium and hafnium compounds and from polymethylalumoxane compounds.
Inventors
- 👤 Maurizio Galimberti
- 👤 Enrico Albizzati
- 👤 Romano Mazzocchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:22
CPC Classifications
C; C08; C08F; C08F210/00; C08F210/04; C08F210/06; C08F4/00; C08F4/42; C08F4/44; C08F4/60; C08F4/62; C08F4/64; C08F4/659; C08F4/65912; C08F4/6592; C08F4/65922; C08F4/65927; Y; Y10; Y10S; Y10S526/00; Y10S526/901
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
96 words
Crystalline copolymers of propylene and 1-butene with an essentially syndiotactic structure, containing from 1.3 to 10 mole % of 1-butene units, having a melting point from 110° to 140° C., a fraction soluble in xylene at 25° C. less than 10% by weight, and a composition similar to the mixture of the monomers present in the gas phase during preparation of said polymer, wherein the difference between the amount of comonomer present in the gas phase and the amount of comonomer in said composition is between 13% to 23% less in the composition of said copolymer.
Claim 2
Dependent Claim
96 words
Crystalline copolymers of propylene and 1-butene with an essentially syndiotactic structure, containing from 1.3 to 10 mole % of 1-butene units, having a melting point from 110° to 140° C., a fraction soluble in xylene at 25° C. less than 10% by weight, and a composition similar to the mixture of the monomers present in the gas phase during preparation of said polymer, wherein the difference between the amount of comonomer present in the gas phase and the amount of comonomer in said composition is between 13% to 23% less in the composition of said copolymer.
Claim 3
Dependent Claim
100 words
A process for the preparation of the copolymers of claim 1 comprising the polymerization of gaseous mixtures of propylene and 1-butene with catalysts obtained from isopropyl (cyclopentadienyl-1-fluorenyl) hafninum or zirconium dichloride and polymethylaluminoxane cyclic or linear compounds of the formula ##STR3## where n is a number from 2 to 25 and ##STR4## where n is a number from 1 to 25, operating under conditions where the 1-butene molar content present in the gas mixture being continuously fed is from 1.5 to 10%, and the polymerization is conducted in the liquid phase, at a temperature of from -30° to 70° C.
References Cited (Backward Citations)
US4892851A
Cited
EP0395055A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-03-22 | 1996-09-21 | 1997-03-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-03-22 | 2000-09-21 | 2001-03-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-03-22 | 2004-09-21 | 2005-03-23 | $7700.00 | Window Closed / Lapsed |