US5185177A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Producing a ceramic implant by coating a powder mixture of zirconia and either tricalcium phosphate or hydroxyapatite on a molded unsintered body of partially stabilized zirconia and then sintering the article
Assignee: Mitsubishi Chemical Corp
•
Filing: 1990-10-15
•
Granted: 1993-02-09
•
Expires: 2010-10-15
Abstract
Abstract A process for producing a ceramic implant which comprises creating a powder mixture comprising zirconia and alpha -tricalcium phosphate or zirconia and hydroxyapatite, in a weight ratio of 0.05 to 20 on the surface of a molded unsintered product of partially stabilized zirconia, followed by sintering at 1200 DEG to 1550 DEG C. The partially stabilized zirconia may have a BET specific surface area of from 5 to 10 m2/g and have been subjected to wet pulverization to increase the BET specific surface area from 1.05 to 2.0 times relative to the starting material.
Inventors
- 👤 Naoto Kijima
- 👤 Yasuo Oguri
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:44
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/80; C04B41/81; C04B41/85; A; A61; A61C; A61C8/00; A61C8/0012; A61L; A61L27/00; A61L27/02; A61L27/10; A61L27/28; A61L27/30; A61L27/32; B; B32; B32B; B32B18/00; C04B35/00; C04B35/01; C04B35/48; C04B35/486; C04B41/45; C04B41/50; C04B41/5076; C04B41/5092; A61C8/0013; A61F; A61F2310/00; A61F2310/00389; A61F2310/00592; A61F2310/00796; C04B2237/00; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/345; C04B2237/348
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
53 words
A process for producing a ceramic implant, which comprises coating a powder mixture comprising zironia and a member of the group consisting of hydroxyapatite and α-tricalcium phosphate in a weight ratio of 0.05-20 on the surface of a molded unsintered product of partially stabilized zironia, followed by sintering at 1200° to 1550° C.
Claim 2
Dependent Claim
53 words
A process for producing a ceramic implant, which comprises coating a powder mixture comprising zironia and a member of the group consisting of hydroxyapatite and α-tricalcium phosphate in a weight ratio of 0.05-20 on the surface of a molded unsintered product of partially stabilized zironia, followed by sintering at 1200° to 1550° C.
Claim 3
Dependent Claim
58 words
A process for producing a ceramic implant, which comprises coating a powder mixture of zirconia and a member of the group consisting of α-tricalcium phosphate and hydroxyapatite in a weight ratio of 0.05-20 on the surface of a molded unsintered product of partially stabilized zirconia, followed by sintering at 1200° to 1550° C. and then by hydrothermal treatment.
Claim 4
Dependent Claim
58 words
A process for producing a ceramic implant, which comprises coating a powder mixture of zirconia and a member of the group consisting of α-tricalcium phosphate and hydroxyapatite in a weight ratio of 0.05-20 on the surface of a molded unsintered product of partially stabilized zirconia, followed by sintering at 1200° to 1550° C. and then by hydrothermal treatment.
Claim 5
Dependent Claim
116 words
A process for producing a ceramic implant, which comprises coating a powder mixture comprising zirconia and a member of the group consisting of hydroxyapatite and α-tricalcium phosphate in a weight ratio of 0.05 to 20 on the surface of a molded unsintered produce of wet pulverized partially stabilized zirconia wherein partially stabilized zirconia powder having a BET specific surface area of from 5 to 10 m 2 /g has been subjected to wet pulverization treatment in the presence of water and a dispersant so that the BET specific surface area of the partially stabilized zirconia powder has increased from 1.05 to 2.0 times relative to the starting material, followed by sintering at 1200° to 1550° C.
Claim 6
Dependent Claim
116 words
A process for producing a ceramic implant, which comprises coating a powder mixture comprising zirconia and a member of the group consisting of hydroxyapatite and α-tricalcium phosphate in a weight ratio of 0.05 to 20 on the surface of a molded unsintered produce of wet pulverized partially stabilized zirconia wherein partially stabilized zirconia powder having a BET specific surface area of from 5 to 10 m 2 /g has been subjected to wet pulverization treatment in the presence of water and a dispersant so that the BET specific surface area of the partially stabilized zirconia powder has increased from 1.05 to 2.0 times relative to the starting material, followed by sintering at 1200° to 1550° C.
Claim 7
Dependent Claim
25 words
The process according to claim 3, wherein the wet pulverization treatment is conducted under a zirconia slurry concentration of from 75 to 90% by weight.
Claim 8
Dependent Claim
28 words
The process according to claim 3, wherein the dispersant is used in an amount of from 0.1 to 1.0% by weight relative to the partially stabilized zirconia powder.
Claim 9
Dependent Claim
21 words
The process according to claim 3, wherein the wet pulverization treatment is conducted at a pH of from 9 to 10.
Claim 10
Dependent Claim
22 words
The process according to claim 3, wherein the dispersant is an ammonium salt of an acrylate polymer composed essentially of acrylic acid.
Claim 11
Dependent Claim
35 words
The process according to claim 3, wherein the wet pulverization treatment is conducted in two steps of slurrying by means of a vibration ball mill and subsequent treatment by means of a rotary ball mill.
References Cited (Backward Citations)
US4308064A
Cited
US4636218A
Cited
US4722915A
Cited
US4957509A
Cited
US4882196A
Cited
US4740288A
Cited
US4771950A
Cited
US4969913A
Cited
US4983182A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-02-09 | 1996-08-10 | 1997-02-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-02-09 | 2000-08-10 | 2001-02-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-02-09 | 2004-08-10 | 2005-02-09 | $7700.00 | Window Closed / Lapsed |