Low temperature multi-layer extrusion coating process and articles produced thereby
Assignee: Eastman Chemical Co
•
Filing: 1992-04-08
•
Granted: 1993-01-12
•
Expires: 2012-04-08
Abstract
Abstract Process for applying multi-layer extrusion coatings to substrate at low temperature is described, employing as one extrusion coating layer a defined polyethylene-containing component, and, as the second extrusion coating layer at least one second extrudable polymeric composition. Also provided are novel extrusion coated articles comprising substrate having coated thereon defined polyethylene-containing component and at least one other extrudable polymeric composition. These articles display good adhesion of extrusion coating material to the substrate without the degradation of the extrudable coatings caused by exposure to excessive levels of heat as is required for successful extrusion coating employing prior art materials.
Inventors
- 👤 John W. Cook
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 09:49
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/50; B05D7/52; B05D7/54; B05D7/548; B05D7/5483; B05D7/5485; B05D1/00; B05D1/26; B05D2507/00; B05D2507/01; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2904; Y10T428/2907; Y10T428/2913; Y10T428/2933; Y10T428/31504; Y10T428/31678; Y10T428/31692; Y10T428/31725; Y10T428/31739; Y10T428/31743; Y10T428/31746; Y10T428/31786; Y10T428/31797; Y10T428/31855; Y10T428/3188; Y10T428/31895; Y10T428/31899; Y10T428/31902; Y10T442/00; Y10T442/20; Y10T442/2025
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
325 words
An article produced by the process for the low-temperature multi-layer extrusion coating of a substrate with a first, polyethylene-containing layer which is subjected to a temperature less than than about 480° F., and at least one additional layer comprising at least one second extrudable composition, said process comprising: applying to at least one surface of said substrate a polyethylene-containing composition to form said first, polyethylene-containing layer, comprising: (a) a polyethylene component having a melt index in the range of about 10 up to 100 dg per minute at 190° C. and having a sufficiently broad molecular weight distribution so that the resulting composition is capable of being extrusion coated at a temperature less than about 480° F. to a thickness as thin as 0.0003 inches (0.0075 mm) at a speed of at least 1000 feet per minute (300 meters per minute), and (b) in the range of about 5 up to 15 wt%, based on the weight of the total composition, of a hydrocarbon tackifying resin having a Ring and Ball Softening Point in the range of about 125° up to 140° C., and at least one second extrudable composition selected from: polyethylenes having a melt index different than the melt index of said first polyethylene component, polyethylenes having a density different than the density of said first polyethylene component, polyethylenes modified with polymer additives, polypropylene homopolymers, comonomers, copolymers, and terpolymers, optionally modified with polymer additives, polyethylene comonomers, copolymers and terpolymers, including extrudable ionomers, optionally modified with polymer additives, extrudable polymers of higher olefins having in the range of 4 up to 8 carbon atoms, optionally modified with polymer additives, extrudable polyvinylidene chloride, optionally modified with polymer additives, extrudable polyamides, optionally modified with polymer additives, or extrudable polyesters, optionally modified with polymer additives; wherein said process is carried out by multi-layer extrusion coating of said substrate; and wherein the temperature of said polyethylene-containing composition is no greater than about 480° F. during the extrusion process.
Claim 2
Dependent Claim
325 words
An article produced by the process for the low-temperature multi-layer extrusion coating of a substrate with a first, polyethylene-containing layer which is subjected to a temperature less than than about 480° F., and at least one additional layer comprising at least one second extrudable composition, said process comprising: applying to at least one surface of said substrate a polyethylene-containing composition to form said first, polyethylene-containing layer, comprising: (a) a polyethylene component having a melt index in the range of about 10 up to 100 dg per minute at 190° C. and having a sufficiently broad molecular weight distribution so that the resulting composition is capable of being extrusion coated at a temperature less than about 480° F. to a thickness as thin as 0.0003 inches (0.0075 mm) at a speed of at least 1000 feet per minute (300 meters per minute), and (b) in the range of about 5 up to 15 wt%, based on the weight of the total composition, of a hydrocarbon tackifying resin having a Ring and Ball Softening Point in the range of about 125° up to 140° C., and at least one second extrudable composition selected from: polyethylenes having a melt index different than the melt index of said first polyethylene component, polyethylenes having a density different than the density of said first polyethylene component, polyethylenes modified with polymer additives, polypropylene homopolymers, comonomers, copolymers, and terpolymers, optionally modified with polymer additives, polyethylene comonomers, copolymers and terpolymers, including extrudable ionomers, optionally modified with polymer additives, extrudable polymers of higher olefins having in the range of 4 up to 8 carbon atoms, optionally modified with polymer additives, extrudable polyvinylidene chloride, optionally modified with polymer additives, extrudable polyamides, optionally modified with polymer additives, or extrudable polyesters, optionally modified with polymer additives; wherein said process is carried out by multi-layer extrusion coating of said substrate; and wherein the temperature of said polyethylene-containing composition is no greater than about 480° F. during the extrusion process.
Claim 3
Dependent Claim
81 words
The article of claim 1 wherein said at least one second extrudable composition is selected from: polyethylene having a melt index different than the melt index of said first polyethylene component, polyethylenes having a density different than the density of said first polyethylene component, polyethylenes modified with polymer additives, polypropylene homopolymers, comonomers, copolymers, and terpolymers, optionally modified with polymer additives, polyethylene comonomers, copolymers and terpolymers, including extrudable ionomers, optionally modified with polymer additives, or extrudable polyamides, optionally modified with polymer additives.
Claim 4
Dependent Claim
49 words
The article of claim 1 wherein said at least one second extrudable composition is a heat sealable composition selected from: polyethylene having a melt index lower than the melt index of said first polyethylene component, or polyethylene comonomers, copolymers and terpolymers, including extrudable ionomers, optionally modified with polymer additives.
Claim 5
Dependent Claim
47 words
The article of claim 1 wherein said at least one second extrudable composition provides a barrier layer, and is selected from: polyethylene comonomers, copolymers na terpolymers, optionally modified with polymer additives, extrudable polyvinylidene chloride, optionally modified with polymer additives, or extrudable polyamides, optionally modified with polymer additives.
Claim 6
Dependent Claim
64 words
The article of claim 1 wherein said at least one second extrudable composition is selected from: polyethylene comonomers, copolymers and terpolymers with at least one co-monomer selected from: vinyl acetate, vinyl alcohol, carbon monoxide, maleic anhydride, ethyl methyl acrylate, ethyl ethyl acrylate, ethyl methyl pentene, or ethyl acrylic acid, wherein each of said polyethylene copolymers and terpolymers can optionally be modified with polymer additives.
Claim 7
Dependent Claim
32 words
The article of claim 1 wherein said hydrocarbon tackifying resin is selected from polymerized β-pinenes, hydrogenated polymers of C 5 hydrocarbons, α-methyl styrene-vinyl toluene copolymers, or pentaerythritol esters of tall oil rosin.
Claim 8
Dependent Claim
17 words
The article of claim 1 wherein said first polyethylene-containing layer is the layer that contacts the substrate.
Claim 9
Dependent Claim
15 words
The article of claim 1 wherein said first polyethylene-containing layer is an exterior barrier layer.
Claim 10
Dependent Claim
33 words
The article of claim 1 comprising said first polyethylene containing layer and at least two additional extruded layers wherein said first polyethylene-containing layer is an adhesive tie-layer between the two additional extruded layers.
Claim 11
Dependent Claim
245 words
An article of manufacture comprising a substrate having adhered thereto a multilayer polymeric laminate comprising: (i) A polyethylene composition layer comprising: (a) a polyethylene component having a melt index in the range of about 10 up to 100 dg per minute at 190° C. and having a sufficiently broad molecular weight distribution so that the resulting composition is capable of being extrusion coated at a temperature less than about 480° F. to a thickness as thin as 0.0075 mm at a speed of at least 300 meters per minute, and (b) in the range of about 5 up to 15 weight percent, based on the weight of the total composition, of a hydrocarbon tackifying resin having a Ring and Ball Softening Point in the range of about 90° up to 150° C.; and (ii) at least on second extrudable composition layer selected from: polyethylenes having a melt index different than the melt index of said first polyethylene component, polyethylenes having a density different than the density of said first polyethylene component, polyethylenes modified with polymer additives, polypropylene homopolymers, comonomers, copolymers, and terpolymers, optionally modified with polymer additives, polyethylene comonomers, copolymers and terpolymers, including extrudable ionomers, optionally modified with polymer additives, extrudable polymers of higher olefins having in the range of 4 up to 8 carbon atoms, optionally modified with polymer additives, extrudable polyvinylidene chloride, optionally modified with polymer additives, or extrudable polyamides, optionally modified with polymer additives, or extrudable polyesters, optionally modified with polymer additives.
Claim 12
Dependent Claim
245 words
An article of manufacture comprising a substrate having adhered thereto a multilayer polymeric laminate comprising: (i) A polyethylene composition layer comprising: (a) a polyethylene component having a melt index in the range of about 10 up to 100 dg per minute at 190° C. and having a sufficiently broad molecular weight distribution so that the resulting composition is capable of being extrusion coated at a temperature less than about 480° F. to a thickness as thin as 0.0075 mm at a speed of at least 300 meters per minute, and (b) in the range of about 5 up to 15 weight percent, based on the weight of the total composition, of a hydrocarbon tackifying resin having a Ring and Ball Softening Point in the range of about 90° up to 150° C.; and (ii) at least on second extrudable composition layer selected from: polyethylenes having a melt index different than the melt index of said first polyethylene component, polyethylenes having a density different than the density of said first polyethylene component, polyethylenes modified with polymer additives, polypropylene homopolymers, comonomers, copolymers, and terpolymers, optionally modified with polymer additives, polyethylene comonomers, copolymers and terpolymers, including extrudable ionomers, optionally modified with polymer additives, extrudable polymers of higher olefins having in the range of 4 up to 8 carbon atoms, optionally modified with polymer additives, extrudable polyvinylidene chloride, optionally modified with polymer additives, or extrudable polyamides, optionally modified with polymer additives, or extrudable polyesters, optionally modified with polymer additives.
Claim 13
Dependent Claim
21 words
An article in accordance with claim 10 wherein said substrate is selected from: papers, paperboards, fibers, polymeric materials, or metal foils.
Claim 14
Dependent Claim
33 words
An article in accordance with claim 11 wherein said polymeric materials are selected from: polyolefins or functionally modified polyolefins; polyesters or functionally modified polyesters; ethylene-vinyl alcohol copolymers, or polyamides or functionally modified polyamides.
Claim 15
Dependent Claim
83 words
An article in accordance with claim 10 wherein said at least one second extrudable composition is selected from: polyethylenes having a melt index different than the melt index of said first polyethylene component, polyethylenes having a density different than the density of said first polyethylene component, polyethylenes modified with polymer additives, polypropylene homopolymers, comonomers, copolymers, and terpolymers, optionally modified with polymer additives, polyethylene comonomers, copolymers and terpolymers, including extrudable ionomers, optionally modified with polymer additives, or extrudable polyamides, optionally modified with polymer additives.
Claim 16
Dependent Claim
51 words
An article in accordance with claim 10 wherein said at least one second extrudable composition is a heat sealable composition selected from: polyethylenes having a melt index lower than the melt index of said first polyethylene component, or polyethylene comonomers, copolymers and terpolymers, including extrudable ionomers, optionally modified with polymer additives.
Claim 17
Dependent Claim
49 words
An article in accordance with claim 10 wherein said at least one second extrudable composition provides a barrier layer, and is selected from: polyethylene comonomers, copolymers and terpolymers, optionally modified with polymer additives, extrudable polyvinylidene chloride, optionally modified with polymer additives, or extrudable polyamides, optionally modified with polymer additives.
Claim 18
Dependent Claim
66 words
An article in accordance with claim 10 wherein said at least one second extrudable composition is selected from: polyethylene comonomers, copolymers and terpolymers with at least one co-monomer selected from: vinyl acetate, vinyl alcohol, carbon monoxide, maleic anhydride, ethyl methyl acrylate, ethyl ethyl acrylate, ethyl methyl pentene, or ethyl acrylic acid, wherein each of said polyethylene copolymers and terpolymers can optionally be modified with polymer additives.
Claim 19
Dependent Claim
34 words
An article in accordance with claim 10 wherein said hydrocarbon tackifying resin is selected from polymerized β-pinenes, hydrogenated polymers of C 5 hydrocarbons, α-methyl styrene-vinyl toluene copolymers, or pentaerythritol esters of tall oil rosin.
Claim 20
Dependent Claim
24 words
An article in accordance with claim 17 containing in the range of about 7 up to 10 wt % of said hydrocarbon tackifying resin.
Claim 21
Dependent Claim
15 words
An article in accordance with claim 18 wherein said tackifying resin is a polymerized β-pinene.
Claim 22
Dependent Claim
17 words
An article in accordance with claim 10 wherein said polyethylene composition layer is the substrate contact layer.
Claim 23
Dependent Claim
17 words
An article in accordance with claim 10 wherein said polyethylene composition layer is the exterior barrier layer.
Claim 24
Dependent Claim
19 words
An article in accordance with claim 10 comprising said polyethylene composition layer and at least two additional extrudable compositions.
Claim 25
Dependent Claim
22 words
An article in accordance with claim 22 wherein said polyethylene composition layer is an adhesive tie-layer between the two additional extrudable compositions.
References Cited (Backward Citations)
US5112424A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-01-12 | 1996-07-13 | 1997-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-01-12 | 2000-07-13 | 2001-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-01-12 | 2004-07-13 | 2005-01-12 | $7700.00 | Window Closed / Lapsed |