In-situ molding of fiber reinforced composites to net shape
Assignee: ZF Transmission Technologies LLC
•
Filing: 1990-12-06
•
Granted: 1992-12-22
•
Expires: 2010-12-06
Abstract
Abstract A method for fabricating composite structures wherein a single mold is used to preform a foam core between fiber reinforcement plies that are subsequently subjected to resin transfer molding to form an integrated foam core composite structure having the formed foam core mechanically interlocked to the composite skins. Fiber reinforcement plies are layed up on contoured molding surfaces of dies to define a core cavity with the mold closed. Foam is injected into the core cavity, concomitantly penetrating the fiber reinforcement plies, and allowed to cure to form the foam core. Heat and pressure generated during foam cure compresses the fiber reinforcement plies to provide debulking therefor. A resin binder is injected into the mold plenum to impregnate the layed-up fiber reinforcement plies, and the formed foam core/resin-impregnated layed-up fiber reinforcement plies are subsequently cured to form the integrated foam core composite structure. Film barriers may be formed in the fiber reinforcement plies to limit penetration of the injected foam to a predetermined number of fiber reinforcement plies. The film barriers may be melted and fused with the injected resin to provide an adhesive bond between the formed foam core and the composite skins, in addition to the mechanical interlock therebetween, to provide an integrated foam core composite structure with superior integrity.
Inventors
- 👤 James H. Ewen
- 👤 Nestor J. Diaz
- 👤 Robert L. Faiz
- 👤 David J. Parker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:57
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/42; B29C70/44; B29C70/443; B29C44/00; B29C44/02; B29C44/12; B29C44/1209; B29C44/14; B29C44/16; B29C70/54; B29C70/546; B29C43/00; B29C43/02; B29C43/10; B29C43/12; B29K; B29K2075/00; B29K2105/00; B29K2105/06; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24149; Y10T428/24157
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
255 words
A method for fabricating an integrated foam core composite structure, using a molding apparatus that includes a set of dies having contoured molding surfaces defining a mold cavity having the shape of said integrated foam core composite structure to be fabricated, means for injecting foam, and means for injecting a resin binder, comprising: laying up a plurality of unpreformed fiber reinforcement plies in the contoured molding surfaces of the set of dies; closing the set of dies wherein exposed layers of said layed-up plurality of unpreformed fiber reinforcement plies define a core cavity; injecting a foam material into said core cavity, said injected foam material penetrating said exposed layers of said layed-up plurality of unpreformed fiber reinforcement plies; allowing said injected foam material to cure to form a foam core mechanically interlocked to said layed-up plurality of unpreformed fiber reinforcement plies, curing of said injected foam generating heat and pressure that simultaneously compresses said layed-up plurality of unpreformed fiber reinforcement plies into conformance with the contoured molding surfaces such that said layed-up plurality of unpreformed fiber reinforcement plies are debulked; injecting the resin binder into a plenum of the mold cavity to impregnate said layed-up plurality of debulked fiber reinforcement plies; and curing said resin binder-impregnated layed-up plurality of debulked fiber reinforcement plies to form composite skins, and wherein said formed foam core is simultaneously post cured; said formed foam core and said composite skins in combination defining said integrated foam core composite structure having said formed foam core mechanically interlocked with said composite skins.
Claim 2
Independent Claim
255 words
A method for fabricating an integrated foam core composite structure, using a molding apparatus that includes a set of dies having contoured molding surfaces defining a mold cavity having the shape of said integrated foam core composite structure to be fabricated, means for injecting foam, and means for injecting a resin binder, comprising: laying up a plurality of unpreformed fiber reinforcement plies in the contoured molding surfaces of the set of dies; closing the set of dies wherein exposed layers of said layed-up plurality of unpreformed fiber reinforcement plies define a core cavity; injecting a foam material into said core cavity, said injected foam material penetrating said exposed layers of said layed-up plurality of unpreformed fiber reinforcement plies; allowing said injected foam material to cure to form a foam core mechanically interlocked to said layed-up plurality of unpreformed fiber reinforcement plies, curing of said injected foam generating heat and pressure that simultaneously compresses said layed-up plurality of unpreformed fiber reinforcement plies into conformance with the contoured molding surfaces such that said layed-up plurality of unpreformed fiber reinforcement plies are debulked; injecting the resin binder into a plenum of the mold cavity to impregnate said layed-up plurality of debulked fiber reinforcement plies; and curing said resin binder-impregnated layed-up plurality of debulked fiber reinforcement plies to form composite skins, and wherein said formed foam core is simultaneously post cured; said formed foam core and said composite skins in combination defining said integrated foam core composite structure having said formed foam core mechanically interlocked with said composite skins.
Claim 3
Dependent Claim
61 words
The method of claim 1 further comprising: forming film barriers in said layed-up plurality of unpreformed fiber reinforcement plies to limit penetration of said injected foam to a predetermined number of unpreformed fiber reinforcement plies forming said exposed layers, said film barriers being operative to melt as a result of the heat and pressure generated by curing of said injected foam.
Claim 4
Dependent Claim
57 words
The method of claim 2 wherein said film barriers are formed by chemically treating unpreformed fiber reinforcement plies with a material that renders said treated unpreformed fiber reinforcement plies substantially insoluble to said injected foam and substantially soluble to the injected resin binder thereby permitting penetration of the treated unpreformed fiber reinforcement plies by the resin binder.
Claim 5
Independent Claim
382 words
A method for fabricating an integrated foam core composite structure, using a molding apparatus that includes a set of dies having contoured molding surfaces defining a mold cavity having the shape of said integrated foam core composite structure to be fabricated, means for injecting foam, and means for injecting a resin binder, comprising: laying up a plurality of fiber reinforcement plies in the contoured molding surfaces of the set of dies; forming film barriers in said layed-up plurality of fiber reinforcement plies by chemically treating fiber reinforcement plies; said laying up step including the steps of laying up a first plurality of untreated fiber reinforcement plies in the contoured molding surfaces of the set of dies, laying up said treated fiber reinforcement plies forming said film barriers onto said first plurality of untreated fiber reinforcement plies, and laying up a predetermined number of untreated fiber reinforcement plies onto said treated fiber reinforcement plies, said first plurality of untreated fiber reinforcement plies, said treated fiber reinforcement plies and said predetermined number of untreated fiber reinforcement plies defining said layed up plurality of fiber reinforcement plies; closing the set of dies wherein exposed layers of said layed-up predetermined number of untreated fiber reinforcement plies define a core cavity; injecting a foam material into said core cavity, penetration of said injected foam being limited to said predetermined number of untreated fiber reinforcement plies; allowing said injected foam material to cure to form a foam core mechanically interlocked to said layed-up plurality of fiber reinforcement plies, curing of said injected foam generating heat and pressure that simultaneously compresses said layed-up plurality of fiber reinforcement plies into conformance with the contoured molding surfaces such that said layed-up plurality of fiber reinforcement plies are debulked; injecting the resin binder into a plenum of the mold cavity to impregnate said layed-up plurality of fiber reinforcement plies; and curing said resin binder-impregnated layed-up plurality of fiber reinforcement plies to form composite skins, and wherein said formed foam core is simultaneously post cured; said treated fiber reinforcement plies being substantially insoluble to said injected foam and substantially soluble to the injected resin binder; said formed foam core and said composite skins in combination defining said integrated foam core composite structure having said formed foam core mechanically interlocked with said composite skins.
Claim 6
Independent Claim
382 words
A method for fabricating an integrated foam core composite structure, using a molding apparatus that includes a set of dies having contoured molding surfaces defining a mold cavity having the shape of said integrated foam core composite structure to be fabricated, means for injecting foam, and means for injecting a resin binder, comprising: laying up a plurality of fiber reinforcement plies in the contoured molding surfaces of the set of dies; forming film barriers in said layed-up plurality of fiber reinforcement plies by chemically treating fiber reinforcement plies; said laying up step including the steps of laying up a first plurality of untreated fiber reinforcement plies in the contoured molding surfaces of the set of dies, laying up said treated fiber reinforcement plies forming said film barriers onto said first plurality of untreated fiber reinforcement plies, and laying up a predetermined number of untreated fiber reinforcement plies onto said treated fiber reinforcement plies, said first plurality of untreated fiber reinforcement plies, said treated fiber reinforcement plies and said predetermined number of untreated fiber reinforcement plies defining said layed up plurality of fiber reinforcement plies; closing the set of dies wherein exposed layers of said layed-up predetermined number of untreated fiber reinforcement plies define a core cavity; injecting a foam material into said core cavity, penetration of said injected foam being limited to said predetermined number of untreated fiber reinforcement plies; allowing said injected foam material to cure to form a foam core mechanically interlocked to said layed-up plurality of fiber reinforcement plies, curing of said injected foam generating heat and pressure that simultaneously compresses said layed-up plurality of fiber reinforcement plies into conformance with the contoured molding surfaces such that said layed-up plurality of fiber reinforcement plies are debulked; injecting the resin binder into a plenum of the mold cavity to impregnate said layed-up plurality of fiber reinforcement plies; and curing said resin binder-impregnated layed-up plurality of fiber reinforcement plies to form composite skins, and wherein said formed foam core is simultaneously post cured; said treated fiber reinforcement plies being substantially insoluble to said injected foam and substantially soluble to the injected resin binder; said formed foam core and said composite skins in combination defining said integrated foam core composite structure having said formed foam core mechanically interlocked with said composite skins.
Claim 7
Dependent Claim
20 words
The method of claim 4 wherein said predetermined number of untreated fiber reinforcement plies comprises one untreated fiber reinforcement ply.
Claim 8
Dependent Claim
46 words
The method of claim 4 further comprising the step of melting said treated fiber reinforcement plies by the heat generated by curing of said injected foam to form an adhesive bond between the formed foam core and said layed-up fiber reinforcement plies forming said composite skins.
References Cited (Backward Citations)
USRE27593E
Cited
US4130614A
Cited
US4379103A
Cited
US4471020A
Cited
US4618532A
Cited
US4509358A
Cited
US4560523A
Cited
US4714575A
Cited
US4891176A
Cited
US4988469A
Cited
US5007976A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-12-22 | 1996-06-22 | 1996-12-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-12-22 | 2000-06-22 | 2000-12-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-12-22 | 2004-06-22 | 2004-12-22 | $7700.00 | Window Closed / Lapsed |