Process for manufacturing a superconducting composite
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1992-01-24
•
Granted: 1992-12-08
•
Expires: 2012-01-24
Abstract
Abstract A superconducting composite comprising a compound oxide type superconductor and an outer metal pipe on which said superconductor is supported, characterized in that (i) said outer metal pipe is made of at least one of metals selected from a group comprising gold, silver and platinum metals and their alloys or (ii) an intermediate layer made of these precious metals is interposed between the compound oxide and the metal pipe. The composite may be in a form of a solid pipe or a hollow pipe having a superconducting thin layer deposited on an inner surface of the metal pipe.
Inventors
- 👤 Susumu Yamamoto
- 👤 Teruyuki Murai
- 👤 Nozumu Kawabe
- 👤 Tomoyuki Awazu
- 👤 Shuji Yazu
- 👤 Tetsuji Jodai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:14
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/20; H10N60/203; H10N60/01; H10N60/0268; H10N60/0801; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9265; Y10S428/93; Y10S505/00; Y10S505/70; Y10S505/701; Y10S505/702; Y10S505/703; Y10S505/704; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014; Y10T428/00; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
237 words
An elongated composite comprising a high-temperature oxide superconductor selected from the group consisting of (i) a compound oxide including an element α selected from group IIa of the periodic table, an element β selected from group IIIa of the periodic table, and an element γ selected from groups Ib, IIb, IIIb, and VIII of the periodic table, (ii) a compound oxide including at least two elements α1 and α2 selected from IIa group of the Periodic Table, an element ε selected from IIIa group of the Periodic Table and an element δ selected from groups Ib, IIb, IIIb and VIII of the Periodic Table, and (iii) a compound oxide including at least two elements α1 and α2 selected from IIa group of the Periodic Table, an element ε selected from IIIa group of the Periodic Table and an element γ selected from groups Ia, IIb, IIIb and VIII of the Periodic Table; and an outer metal pipe on which said superconductor is support, wherein an intermediate layer made of at least one of metals selected from a group consisting of Ag, Au, Pt, Pd, Rh, lr, Ru, Os, and their alloys is interposed between said superconductor and said outer metal pipe and further characterized in that more than one metal wires are embedded in said superconductor, wherein the metal wire is formed of a material selected from the group consisting of gold, platinum, silver, and their alloys.
Claim 2
Dependent Claim
237 words
An elongated composite comprising a high-temperature oxide superconductor selected from the group consisting of (i) a compound oxide including an element α selected from group IIa of the periodic table, an element β selected from group IIIa of the periodic table, and an element γ selected from groups Ib, IIb, IIIb, and VIII of the periodic table, (ii) a compound oxide including at least two elements α1 and α2 selected from IIa group of the Periodic Table, an element ε selected from IIIa group of the Periodic Table and an element δ selected from groups Ib, IIb, IIIb and VIII of the Periodic Table, and (iii) a compound oxide including at least two elements α1 and α2 selected from IIa group of the Periodic Table, an element ε selected from IIIa group of the Periodic Table and an element γ selected from groups Ia, IIb, IIIb and VIII of the Periodic Table; and an outer metal pipe on which said superconductor is support, wherein an intermediate layer made of at least one of metals selected from a group consisting of Ag, Au, Pt, Pd, Rh, lr, Ru, Os, and their alloys is interposed between said superconductor and said outer metal pipe and further characterized in that more than one metal wires are embedded in said superconductor, wherein the metal wire is formed of a material selected from the group consisting of gold, platinum, silver, and their alloys.
Claim 3
Dependent Claim
22 words
A composite set forth in claim 1, characterized in that said intermediate layer is made of Ag, Au, Pt, or their alloys.
Claim 4
Dependent Claim
40 words
A composite set forth in claim 1, characterized in that said high temperature oxide superconductor is in a form of a layer deposited on the inner surface of an intermediate layer deposited on an inner surface of said metal pipe.
Claim 5
Dependent Claim
18 words
A composite set forth in claim 1, characterized in that said intermediate layer is deposited by sputtering technique.
Claim 6
Dependent Claim
51 words
A composite set forth in claim 1, characterized in that an inner surface of said intermediate layer is further coated with a material which is selected from a group consisting of silicon, zirconium, SiO 2 , glass and a material formed by oxidation of the inner surface of the intermediate layer.
Claim 7
Dependent Claim
29 words
A composite set forth in claim 1, characterized in that said high temperature oxide superconductor is in a form of a sintered solid mass compacted inside said intermediate layer.
Claim 8
Dependent Claim
59 words
A composite set forth in claim 1, characterized in that said compound oxide is a compound oxide including an element α selected from IIa group of the Periodic Table, an element β selected from IIIa group of the Periodic Table and an element γ selected from a group comprising Ia, IIb, IIIb and VIII group of the Periodic Table.
Claim 9
Dependent Claim
18 words
A composite set forth in claim 7, characterized in that said compound oxide is of quasi-perovskite type oxide.
Claim 10
Dependent Claim
26 words
A composite set forth in claim 7, characterized in that said element α is Ba, said element β is Y and said element γ is Cu.
Claim 11
Dependent Claim
26 words
A composite set forth in claim 7, characterized in that said element α is Ba, said element β is La and said element γ is Cu.
Claim 12
Dependent Claim
26 words
A composite set forth in claim 7, characterized in that said element α is Sr, said element β is La and said element γ is Cu.
Claim 13
Dependent Claim
63 words
A composite set forth in claim 1, characterized in that said compound oxide is a compound oxide including at least two elements α1 and α2 selected from IIa group of the Periodic Table, an element δ selected from Va group of the Periodic Table and an element γ selected from a group comprising Ia, IIb, IIIb and VIII group of the Periodic Table.
Claim 14
Dependent Claim
30 words
A composite set forth in claim 12, characterized in that said element α1 and α2 is Sr and Ca, said element δ is Bi and said element γ is Cu.
Claim 15
Dependent Claim
63 words
A composite set forth in claim 1, characterized in that said compound oxide is a compound oxide including at least two elements α1 and α2 selected from IIa group of the Periodic Table, an element ε selected from IIIa group of the Periodic Table and an element γ selected from a group comprising Ia, IIb, IIIb and VIII group of the Periodic Table.
Claim 16
Dependent Claim
30 words
A composite set forth in claim 14, characterized in that said element α1 and α2 is Ba and Ca, said element δ is Tl and said element γ is Cu.
Claim 17
Dependent Claim
124 words
A composite set forth in claim 1, wherein said compound oxide is represented by the general formula: (α1·xβx)γyOz in which α stands for an element selected from IIa group of the Periodic Table, β stands for an element selected from IIIa group of the Periodic Table and γ stands for an element selected from a group comprising Ia, IIb, IIIb and VIII group of the Periodic Table, and a small letter of "x" represents an atomic ratio of β and is a number which satisfies a range of 0.1≦x≦0.9 with respect to the total of (α+β) which is equal to 1 small letters of "y" and "z" represent atomic ratios of γ and oxygen (O) respectively and satisfy ranges of 1.0≦y≦4.0 and 1≦z≦5 respectively.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-12-08 | 1996-06-08 | 1996-12-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-12-08 | 2000-06-08 | 2000-12-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-12-08 | 2004-06-08 | 2004-12-08 | $7700.00 | Window Closed / Lapsed |