US5166012A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Manganese oxide compounds
Assignee: Technology Finance Corp Pty Ltd
•
Filing: 1991-05-02
•
Granted: 1992-11-24
•
Expires: 2011-05-02
Abstract
Abstract The invention provides a hydrogen manganese oxide compound. It has manganese cations and oxygen anions arranged in a framework having a hollandite-type structure and defining channels. Cations in the channels are confined to manganse, hydrogen and/or lithium cations. The ionic ratios of lithium:manganese cations and of hydrogen:manganese cations are respectively at most 0.05:1 and at least 0.01:1.00. The invention also provides a method of making said compound; a lithium manganese oxide compound derived from said hydrogen manganese oxide compound and a method of synthesising it therefrom; and electrochemical cells employing said hydrogen manganese oxide and lithium manganese oxide compounds as active cathode materials.
Inventors
- 👤 Margaretha H. Rossouw
- 👤 Michael M. Thackeray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 17:49
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/05; C; C01; C01G; C01G45/00; C01G45/03; C01G45/12; C01G45/1221; C01G45/1228; C01G45/125; C01G45/1257; H01M4/00; H01M4/02; H01M4/36; H01M4/48; H01M4/50; H01M6/00; H01M6/04; H01M6/06; C01P; C01P2002/00; C01P2002/50; C01P2002/52; C01P2002/54; C01P2002/70; C01P2002/72; C01P2002/74; C01P2002/77; C01P2006/00; C01P2006/40; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
61 words
A hydrogen manganese oxide compound in which there are manganese cations and oxygen anions arranged in a framework having a hollandite structure defining channels, the only metal cations in the channels other than manganese cations being lithium cations, the ionic ratio of lithium cations:manganese cations being at most 0.05:1.00, and the ionic ratio of hydrogen cations:manganese cations being at least 0.01:1.00.
Claim 2
Dependent Claim
61 words
A hydrogen manganese oxide compound in which there are manganese cations and oxygen anions arranged in a framework having a hollandite structure defining channels, the only metal cations in the channels other than manganese cations being lithium cations, the ionic ratio of lithium cations:manganese cations being at most 0.05:1.00, and the ionic ratio of hydrogen cations:manganese cations being at least 0.01:1.00.
Claim 3
Dependent Claim
20 words
A compound as claimed in claim 1, in which said ionic ratio of lithium cations:manganese cations is at most 0.03:1.00.
Claim 4
Dependent Claim
20 words
A compound as claimed in claim 1, in which the ionic ratio of oxygen anions to manganese cations is 1.74:1.00-2.00:1.00.
Claim 5
Dependent Claim
20 words
A compound as claimed in claim 2, in which the ionic ratio of oxygen anions to manganese cations is 1.75:1.00-2.00:1.00.
Claim 6
Dependent Claim
71 words
An electrochemical cell which comprises an anode whose active anode material is selected from the group consisting of zinc, zinc alloys, mixtures of said zinc-containing anode materials, lithium, lithium alloys, lithium-containing compounds and mixtures of said lithium-containing anode materials, a cathode and an electrolyte whereby the anode is electrochemically coupled to the cathode, the cathode having as its active cathode material, a hydrogen manganese oxide compound as claimed in claim 1.
Claim 7
Dependent Claim
53 words
A cell as claimed in claim 5, which has a zinc-containing active anode material, the electrolyte being an aqueous room temperature electrolyte selected from solutions of NH 4 Cl, ZnCl 2 , KOH and mixtures thereof, the cathode being one in which the ionic ratio of hydrogen cations:manganese cations is at least 0.10:1.00.
Claim 8
Dependent Claim
56 words
A cell as claimed in claim 5, which has a lithium-containing active anode material, the electrolyte being a room temperature electrolyte selected from LiClO 4 , LiAsF 6 , LiBF 4 and mixtures thereof, dissolved in an organic solvent, the cathode being one in which the ionic ratio of hydrogen cations:manganese cations is at most 0.10:1.00.
Claim 9
Dependent Claim
49 words
A method of making a hydrogen manganese oxide compound as claimed in claim 1, the method comprising treating a suitable lithium manganese oxide compound with an acid at a temperature of 40°-100° C., to leach Li 2 O therefrom, to leave a residue comprising said hydrogen manganese oxide compound.
Claim 10
Dependent Claim
19 words
A method as claimed in claim 8, in which the lithium manganese oxide is Li 2 MnO 3 .
Claim 11
Dependent Claim
22 words
A method as claimed in claim 8, in which the acid is a mineral acid, the leaching taking place at 70°-100° C.
Claim 12
Dependent Claim
22 words
A method as claimed in claim 10, in which the acid is H 2 SO 4 at a concentration of 0.5-10 Molar.
Claim 13
Dependent Claim
43 words
A lithium manganese compound of formula H 2x-z Li z MnO 2+x in which 0.005<x≦0.3 and 0<z≦2x, having manganese cations and oxygen anions arranged in a stable hollandite structure having channels containing no cations other than lithium cations, hydrogen cations and manganese cations.
Claim 14
Dependent Claim
43 words
A lithium manganese compound of formula H 2x-z Li z MnO 2+x in which 0.005<x≦0.3 and 0<z≦2x, having manganese cations and oxygen anions arranged in a stable hollandite structure having channels containing no cations other than lithium cations, hydrogen cations and manganese cations.
Claim 15
Dependent Claim
96 words
A method of synthesizing a lithium manganese oxide compound of formula H 2x-z Li z MnO 2+x in which 0.005<x≦0.3 and 0<z≦2x, having manganese cations and oxygen anions arranged in a stable hollandite structure having channels containing no cations other than lithium cations, hydrogen cations and manganese cations, which method comprises reacting a hydrogen manganese oxide compound as claimed in claim 1 with a lithium compound, in an oxygen-containing atmosphere at a temperature of 250°-400° C., until the lithium compound has been consumed by the heating and by reaction thereof with said hydrogen manganese oxide compound.
Claim 16
Dependent Claim
58 words
An electrochemical cell which comprises an anode whose active anode material is selected from the group consisting of lithium, lithium alloys, lithium-containing compounds and mixtures of said lithium-containing anode-materials, a cathode and an electrolyte whereby the anode is electrochemically coupled to the cathode, the cathode having as its active cathode material, a compound as claimed in claim 12.
Claim 17
Dependent Claim
73 words
A hydrogen manganese oxide compound in which there are manganese cations and oxygen anions arranged in a framework having a hollandite structure defining channels, the only metal cations in the channels other than manganese cations being lithium cations, the ionic ratio of lithium cations: manganese cations being at most 0.05:1.00, and the ionic ratio of hydrogen cations:manganese cations being at least 0.01:1.00, made in accordance with the method as claimed in claim 8.
Claim 18
Dependent Claim
55 words
A lithium manganese oxide compound of formula H 2x-z Li z MnO 2+x in which 0.005<x≦0.03 and 0<z≦2x, having manganese cations and oxygen anions arranged in a stable hollandite structure having channels containing no cations other than lithium cations, hydrogen cations and manganese cations, made in accordance with the method as claimed in claim 13.
References Cited (Backward Citations)
US2885262A
Cited
US3320157A
Cited
US4758484A
Cited
EP0279235A1
Cited
US4959282A
Cited
GB2221213A
Cited
US4975346A
Cited
GB2234233A
Cited
FR2656957A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-24 | 1996-05-25 | 1996-11-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-24 | 2000-05-25 | 2000-11-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-24 | 2004-05-25 | 2004-11-24 | $7700.00 | Window Closed / Lapsed |