Optimized container stacked capacitor DRAM cell utilizing sacrificial oxide deposition and chemical mechanical polishing
Assignee: Round Rock Research LLC
•
Filing: 1992-03-13
•
Granted: 1992-11-10
•
Expires: 2012-03-13
Abstract
Abstract An existing stacked capacitor fabrication process is modified to construct a three-dimensional stacked container capacitor. The present invention develops the container capacitor by etching an opening (or contact opening) into a low etch rate oxide. The contact opening is used as a form for deposited polysilicon that conforms to the sides of the opening walls. Within the thin poly lining of the oxide container a high etch-rate oxide, such as ozone TEOS, is deposited over the entire structure thereby bridging across the top of the oxide container. The high etch-rate oxide is planarized back to the thin poly and the resulting exposed poly is then removed to separate neighboring containers. The two oxides, having different etch rates, are then etched thereby leaving a free-standing poly container cell with 100% (or all) of the higher etch rate oxide removed and a pre-determined oxide surrounding the container still intact.
Inventors
- 👤 Charles H. Dennison
- 👤 Michael A. Walker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:44
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/01; H10D1/041; H10D1/042; H10D1/60; H10D1/68; H10D1/692; H10D1/711; H10D1/716
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
251 words
A process for fabricating a uniform and repeatable conductive container structure on a starting substrate's existing topography, said process comprising the steps of: a) forming a blanketing first insulating layer, having a first etch rate, over said existing topography; b) patterning and etching an opening into said first insulating layer, said opening thereby forming a container form; c) forming a conformal first conductive layer superjacent said first insulating layer and said container form thereby lining said container form; d) forming a blanketing second insulating layer, having a second etch rate, superjacent said first conductive layer; e) removing said second insulating layer until upper portion of said first conductive layer is exposed; f) removing said exposed first conductive upper layer until underlying said first insulating layer is exposed thereby separating said first conductive layer into individual said conductive containers having inner and outer walls; g) simultaneously removing said first and said second insulating layers such that said second insulating layer is completely removed thereby exposing the entire inner walls of said conductive container and said first insulating layer is partially removed thereby exposing an upper portion of said outer walls of said conductive container, wherein the partially remaining first insulating layer provides insulation between said underlying substrate topography and subsequently formed layers; h) forming a third insulating layer superjacent and coextensive said exposed walls and inner bottom portion of said container and said partially remaining first insulating layer; and i) forming a second conductive layer superjacent and coextensive said third insulating layer.
Claim 2
Dependent Claim
251 words
A process for fabricating a uniform and repeatable conductive container structure on a starting substrate's existing topography, said process comprising the steps of: a) forming a blanketing first insulating layer, having a first etch rate, over said existing topography; b) patterning and etching an opening into said first insulating layer, said opening thereby forming a container form; c) forming a conformal first conductive layer superjacent said first insulating layer and said container form thereby lining said container form; d) forming a blanketing second insulating layer, having a second etch rate, superjacent said first conductive layer; e) removing said second insulating layer until upper portion of said first conductive layer is exposed; f) removing said exposed first conductive upper layer until underlying said first insulating layer is exposed thereby separating said first conductive layer into individual said conductive containers having inner and outer walls; g) simultaneously removing said first and said second insulating layers such that said second insulating layer is completely removed thereby exposing the entire inner walls of said conductive container and said first insulating layer is partially removed thereby exposing an upper portion of said outer walls of said conductive container, wherein the partially remaining first insulating layer provides insulation between said underlying substrate topography and subsequently formed layers; h) forming a third insulating layer superjacent and coextensive said exposed walls and inner bottom portion of said container and said partially remaining first insulating layer; and i) forming a second conductive layer superjacent and coextensive said third insulating layer.
Claim 3
Dependent Claim
17 words
A process as recited in claim 1, wherein said first and said second insulating layers are oxides.
Claim 4
Dependent Claim
26 words
A process as recited in claim 1, wherein said first insulating layer etch rate is a lower etch rate than said second insulating layer etch rate.
Claim 5
Dependent Claim
33 words
A process as recited in claim 3, wherein the etch rate ratio between said second insulating layer etch rate and said first insulating layer etch rate is a ratio of 2:1 or greater.
Claim 6
Dependent Claim
31 words
A process as recited in claim 3, wherein the etch rate ratio between said second insulating layer etch rate and said first insulating layer etch rate is a ratio of 4:1.
Claim 7
Dependent Claim
18 words
A process as recited in claim 1, wherein said first and said second conductive layers are doped polysilicon.
Claim 8
Dependent Claim
19 words
A process as recited in claim 4, wherein said doped polysilicon is formed by insitu doped chemical vapor deposition.
Claim 9
Dependent Claim
23 words
A process as recited in claim 1, wherein said first, said second and said third insulating layers are formed by chemical vapor deposition.
Claim 10
Dependent Claim
260 words
A process for fabricating a DRAM container storage capacitor on a silicon substrate having active areas, word lines and digit lines, said process comprising the following sequence of steps: a) forming a blanketing first insulating layer, having a first etch rate, over said existing topography; b) patterning and etching an opening into said first insulating layer, said opening thereby forming a container form; c) forming a conformal first conductive layer superjacent said first insulating layer and said container form thereby lining said container form; d) forming a blanketing second insulating layer, having a second etch rate, superjacent said first conductive layer; e) removing said second insulating layer until upper portion of said first conductive layer is exposed; f) removing said exposed first conductive upper layer until underlying said first insulating layer is exposed thereby separating said first conductive layer into individual said container storage capacitors having inner and outer walls; g) simultaneously removing said first and said second insulating layers such that said second insulating layer is completely removed thereby exposing the entire inner walls of said container storage capacitor and said first insulating layer is partially removed thereby exposing an upper portion of said outer walls of said container storage capacitor, wherein the partially remaining first insulating layer provides insulation between said underlying substrate topography and subsequently formed layers; h) forming a third insulating layer superjacent and coextensive said exposed walls and inner bottom portion of said capacitor and said partially remaining first insulating layer; and i) forming a second conductive layer superjacent and coextensive said third insulating layer.
Claim 11
Dependent Claim
260 words
A process for fabricating a DRAM container storage capacitor on a silicon substrate having active areas, word lines and digit lines, said process comprising the following sequence of steps: a) forming a blanketing first insulating layer, having a first etch rate, over said existing topography; b) patterning and etching an opening into said first insulating layer, said opening thereby forming a container form; c) forming a conformal first conductive layer superjacent said first insulating layer and said container form thereby lining said container form; d) forming a blanketing second insulating layer, having a second etch rate, superjacent said first conductive layer; e) removing said second insulating layer until upper portion of said first conductive layer is exposed; f) removing said exposed first conductive upper layer until underlying said first insulating layer is exposed thereby separating said first conductive layer into individual said container storage capacitors having inner and outer walls; g) simultaneously removing said first and said second insulating layers such that said second insulating layer is completely removed thereby exposing the entire inner walls of said container storage capacitor and said first insulating layer is partially removed thereby exposing an upper portion of said outer walls of said container storage capacitor, wherein the partially remaining first insulating layer provides insulation between said underlying substrate topography and subsequently formed layers; h) forming a third insulating layer superjacent and coextensive said exposed walls and inner bottom portion of said capacitor and said partially remaining first insulating layer; and i) forming a second conductive layer superjacent and coextensive said third insulating layer.
Claim 12
Dependent Claim
17 words
A process as recited in claim 9, wherein said first and said second insulating layers are oxides.
Claim 13
Dependent Claim
26 words
A process as recited in claim 9, wherein said first insulating layer etch rate is a lower etch rate than said second insulating layer etch rate.
Claim 14
Dependent Claim
33 words
A process as recited in claim 11, wherein the etch rate ratio between said second insulating layer etch rate and said first insulating layer etch rate is a ratio of 2:1 or greater.
Claim 15
Dependent Claim
31 words
A process as recited in claim 11, wherein the etch rate ratio between said second insulating layer etch rate and said first insulating layer etch rate is a ratio of 4:1.
Claim 16
Dependent Claim
18 words
A process as recited in claim 9, wherein said first and said second conductive layers are doped polysilicon.
Claim 17
Dependent Claim
19 words
A process as recited in claim 9, wherein said doped polysilicon is formed by insitu doped chemical vapor deposition.
Claim 18
Dependent Claim
23 words
A process as recited in claim 9, wherein said first, said second and said third insulating layers are formed by chemical vapor deposition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-10 | 1996-05-11 | 1996-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-10 | 2000-05-11 | 2000-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-10 | 2004-05-11 | 2004-11-10 | $7700.00 | Window Closed / Lapsed |