Fire-resistant thermoplastic composite structure
Assignee: Dow Chemical Co
•
Filing: 1991-06-28
•
Granted: 1992-11-03
•
Expires: 2011-06-28
Abstract
Abstract Disclosed is a coextruded, fire-resistant, composite structure of adjacent, alternating first and second layers wherein the first layer comprises a thermoplastic foam and second layer a thermoplastic material with such second layers containing a quantity of a brominated fire retardant sufficient to enhance the flame retardancy of the composite structure. Incorporation of the fire retardant into the thermoplastic material layers allows a fire-resistant foam structure to be made using water as a blowing agent for the first layers while avoiding serious corrosion problems encountered when incorporating both brominated fire retardants and water in the same foam structure. Further disclosed are processes for making the above described composite structure. Further disclosed is a composite flow melt expandable into the above-described composite structure.
Inventors
- 👤 Creston D. Shmidt
- 👤 William G. Stobby
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:34
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/18; B29; B29C; B29C44/00; B29C44/20; B29C44/22; B29C44/34; B29C44/36; B29C44/46; B29C44/50; B29C44/505; B32B27/00; B32B27/06; B32B27/065; B32B27/08; B32B27/30; B32B27/302; B32B7/00; B32B7/04; B32B7/12; B29K; B29K2995/00; B29K2995/0012; B29K2995/0016; B32B2250/00; B32B2250/42; B32B2307/00; B32B2307/30; B32B2307/306; B32B2307/3065; B32B2325/00; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10S428/92; Y10S428/921; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249981; Y10T428/249987; Y10T428/249991; Y10T428/249992; Y10T428/249993
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
74 words
A coextruded, fire-resistant, thermoplastic composite structure, comprising: a first layer of a foam of a thermoplastic material, the first layer having a blowing agent comprising water, the first layer being substantially free of brominated aliphatic fire retardants; a second layer of a thermoplastic material, the second layer having a quantity of a brominated aliphatic fire retardant sufficient to reduce the flammability of the composite structure, the first and second layers being adjacent each other.
Claim 2
Dependent Claim
74 words
A coextruded, fire-resistant, thermoplastic composite structure, comprising: a first layer of a foam of a thermoplastic material, the first layer having a blowing agent comprising water, the first layer being substantially free of brominated aliphatic fire retardants; a second layer of a thermoplastic material, the second layer having a quantity of a brominated aliphatic fire retardant sufficient to reduce the flammability of the composite structure, the first and second layers being adjacent each other.
Claim 3
Dependent Claim
18 words
The structure of claim 1, wherein the structure has a plurality of substantially alternating first and second layers.
Claim 4
Dependent Claim
29 words
The structure of claim 2, wherein the brominated fire retardant comprises about 0.4 to about 10 weight percent based upon the weight of the thermoplastic material in the structure.
Claim 5
Dependent Claim
12 words
The structure of claim 2, wherein the brominated fire retardant is hexabromocyclododecane.
Claim 6
Dependent Claim
16 words
The structure of claim 2, wherein the second layer is in the form of a film.
Claim 7
Dependent Claim
14 words
The structure of claim 2, wherein the second layer is substantially free of water.
Claim 8
Dependent Claim
11 words
The structure of claim 2, wherein the thermoplastic material is polystyrene.
Claim 9
Dependent Claim
12 words
The structure of claim 2, wherein the outer layers are second layers.
Claim 10
Dependent Claim
108 words
A composite thermoplastic flow melt suitable for expansion into a composite foam structure, comprising: a first stream layer of a flow melt of a thermoplastic material, the first stream layer having a blowing agent comprising water, the first stream layer being substantially free of brominated aliphatic fire retardants; a second stream layer of a flow melt of a thermoplastic material, the second stream layer having a quantity of a brominated fire retardant sufficient to reduce the flammability of the composite structure formed by expansion of the composite flow melt, the second stream layer being substantially free of water, the first and second stream layers being adjacent each other.
Claim 11
Dependent Claim
108 words
A composite thermoplastic flow melt suitable for expansion into a composite foam structure, comprising: a first stream layer of a flow melt of a thermoplastic material, the first stream layer having a blowing agent comprising water, the first stream layer being substantially free of brominated aliphatic fire retardants; a second stream layer of a flow melt of a thermoplastic material, the second stream layer having a quantity of a brominated fire retardant sufficient to reduce the flammability of the composite structure formed by expansion of the composite flow melt, the second stream layer being substantially free of water, the first and second stream layers being adjacent each other.
Claim 12
Dependent Claim
23 words
The composite flow melt of claim 9, wherein the composite flow melt comprises a plurality of substantially alternating first and second stream layers.
References Cited (Backward Citations)
US3645837A
Cited
JPS5366986A
Cited
US4331725A
Cited
US4784906A
Cited
US4889669A
Cited
US4818603A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-03 | 1996-05-04 | 1996-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-03 | 2000-05-04 | 2000-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-03 | 2004-05-04 | 2004-11-03 | $7700.00 | Window Closed / Lapsed |