Method for manufacturing ultrathin inorganic membranes
Assignee: Air Products and Chemicals Inc
•
Filing: 1992-01-02
•
Granted: 1992-11-03
•
Expires: 2012-01-02
Abstract
Abstract The present invention is a method for manufacturing ultrathin inorganic membranes comprising yttria-stabilized zirconia (YSZ) in a thickness of ≦0.5 μm which has been deposited onto a lanthanum-doped alumina surface layer of a porous alumina substrate having an average pore diameter of less than about 50 nm. The inorganic membranes formed by the method provide oxygen flux rates superior to those known in the art and are suitable for numerous uses including processes for separating oxygen from oxygen-containing gaseous mixtures and in processes for partially oxidizing hydrocarbons to their corresponding oxidized products.
Inventors
- 👤 Antonij J. Burggraaf
- 👤 Yue-Sheng Lin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 10:20
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/02; B01D71/024; B01D67/00; B01D67/0039; B01D67/0072; B01J; B01J35/00; B01J35/50; B01J35/58; B01J35/59; C; C01; C01B; C01B13/00; C01B13/02; C01B13/0229; C01B13/0248; C01B13/0251; C01B13/0255; C04; C04B; C04B41/00; C04B41/009; C04B41/45; C04B41/4505; C04B41/455; C04B41/52; C04B41/80; C04B41/81; C04B41/89; C23; C23C; C23C16/00; C23C16/04; C23C16/045; C23C16/22; C23C16/30; C23C16/40; C23C16/405; H; H01; H01M; H01M8/00; H01M8/10; H01M8/12; H01M8/124; H01M8/1246; H01M8/1253; B01D2323/00; B01D2323/10; C01B2210/00; C01B2210/0043; C01B2210/0046; C04B2111/00; C04B2111/00474; C04B2111/00793; C04B2111/00801; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
196 words
A method for manufacturing an ultrathin inorganic membrane comprising a multicomponent oxide in a thickness less than or equal to about 0.5 μm which is deposited on a porous substrate having a porous surface layer, the method comprising: (a) independently heating at least two metal halides to temperatures sufficient to vaporize each of the metal halides; (b) introducing the vaporized metal halides into a first chamber of a reactor comprising two chambers which are connected by a removable porous substrate having a network of pores capable of transporting gases between the two chambers, said removable porous substrate further comprising a porous surface layer having an average pore diameter of less than or equal to about 50 nm; (c) introducing an oxidizing agent into a second chamber of the reactor; (d) contacting the metal halides and the oxidizing agent in the pores of the porous surface layer at a temperature, a pressure and for a time sufficient to deposit plugs of the multicomponent oxide within the pores of the surface layer of the substrate and to restrict growth of the plugs to a thickness of less than or equal to 0.5 μm to form the inorganic membrane.
Claim 2
Independent Claim
196 words
A method for manufacturing an ultrathin inorganic membrane comprising a multicomponent oxide in a thickness less than or equal to about 0.5 μm which is deposited on a porous substrate having a porous surface layer, the method comprising: (a) independently heating at least two metal halides to temperatures sufficient to vaporize each of the metal halides; (b) introducing the vaporized metal halides into a first chamber of a reactor comprising two chambers which are connected by a removable porous substrate having a network of pores capable of transporting gases between the two chambers, said removable porous substrate further comprising a porous surface layer having an average pore diameter of less than or equal to about 50 nm; (c) introducing an oxidizing agent into a second chamber of the reactor; (d) contacting the metal halides and the oxidizing agent in the pores of the porous surface layer at a temperature, a pressure and for a time sufficient to deposit plugs of the multicomponent oxide within the pores of the surface layer of the substrate and to restrict growth of the plugs to a thickness of less than or equal to 0.5 μm to form the inorganic membrane.
Claim 3
Dependent Claim
37 words
The method according to claim 1 wherein the contacting occurs at a temperature ranging from 600° to 1300° C., a pressure ranging from 1 to 760 torr and a time ranging from 1 minute to 10 hours.
Claim 4
Dependent Claim
38 words
The method according to claim 2 wherein the porous substrate is selected from the group consisting of alumina, silica, magnesia, titania, a high temperature oxygen compatible metal alloy, a metal oxide stabilized zirconia and compounds and mixtures thereof.
Claim 5
Dependent Claim
43 words
The method according to claim 3 wherein the metal halides to be vaporized are represented by fluorides, chlorides, bromides and iodides of metals selected from Groups 2, 3, 4 and 15 and the F block lanthanides of the Periodic Table of the Elements.
Claim 6
Dependent Claim
33 words
The method according to claim 4 wherein the porous substrate connecting the first chamber and the second chamber is oriented such that the porous surface layer is contacted with the vaporized metal halides.
Claim 7
Dependent Claim
19 words
The method according to claim 5 wherein the metal halides to be vaporized further comprise a halide of zirconium.
Claim 8
Dependent Claim
26 words
The method according to claim 6 wherein the oxidizing agent is selected from the group consisting of oxygen, ozone, N 2 O, water and mixtures thereof.
Claim 9
Dependent Claim
30 words
The method according to claim 6 wherein the oxidizing agent is selected from the group consisting of a mixture of oxygen and water and a mixture of hydrogen and water.
Claim 10
Independent Claim
203 words
A method for manufacturing an ultrathin inorganic membrane comprising a yttria-stabilized zirconia layer having a thickness less than or equal to about 0.5 μm which is deposited onto a porous metal-doped alumina surface layer of a porous alumina substrate, the method comprising: (a) independently heating halides of yttrium and zirconium to temperatures sufficient to vaporize each of the metal halides; (b) introducing the vaporized metal halides into a first chamber of a reactor comprising two chambers which are connected by a removable porous alumina substrate having a network of pores capable of transporting gases between the chambers, said removable porous alumina substrate further comprising a porous metal-doped alumina surface layer having an average pore diameter of less than or equal to about 50 nm; (c) introducing an oxidizing agent into a second chamber of the reactor; (d) contacting the metal halides and the oxidizing agent in the pores of the metal-doped alumina layer at a temperature, a pressure and for a time sufficient to deposit plugs of the yttria stabilized zirconia within the pores of the metal-doped alumina surface layer and to restrict growth of the plugs to a thickness of less than or equal to 0.5 μm to form the inorganic membrane.
Claim 11
Independent Claim
203 words
A method for manufacturing an ultrathin inorganic membrane comprising a yttria-stabilized zirconia layer having a thickness less than or equal to about 0.5 μm which is deposited onto a porous metal-doped alumina surface layer of a porous alumina substrate, the method comprising: (a) independently heating halides of yttrium and zirconium to temperatures sufficient to vaporize each of the metal halides; (b) introducing the vaporized metal halides into a first chamber of a reactor comprising two chambers which are connected by a removable porous alumina substrate having a network of pores capable of transporting gases between the chambers, said removable porous alumina substrate further comprising a porous metal-doped alumina surface layer having an average pore diameter of less than or equal to about 50 nm; (c) introducing an oxidizing agent into a second chamber of the reactor; (d) contacting the metal halides and the oxidizing agent in the pores of the metal-doped alumina layer at a temperature, a pressure and for a time sufficient to deposit plugs of the yttria stabilized zirconia within the pores of the metal-doped alumina surface layer and to restrict growth of the plugs to a thickness of less than or equal to 0.5 μm to form the inorganic membrane.
Claim 12
Dependent Claim
41 words
The method according to claim 9 wherein the contacting according to step (d) occurs at a temperature ranging from 700° to 1100° C., a pressure ranging from 1 to 760 torr and a time ranging from 1 minute to 2 hours.
Claim 13
Dependent Claim
33 words
The method according to claim 10 wherein the porous substrate connecting the first chamber and the second chamber is oriented such that the porous surface layer is contacted with the vaporized metal halides.
Claim 14
Dependent Claim
28 words
The method according to claim 11 wherein the metal halides to be vaporized are selected from the group consisting of chlorides, bromides and iodides of zirconium and yttrium.
Claim 15
Dependent Claim
26 words
The method according to claim 12 wherein the metal halides are introduced into the first chamber of the reactor by means of an inert carrier gas.
Claim 16
Dependent Claim
22 words
The method according to claim 13 wherein the inert carrier gas is selected from the group consisting of argon, nitrogen and helium.
Claim 17
Dependent Claim
26 words
The method according to claim 14 wherein the oxidizing agent is selected from the group consisting of oxygen, ozone, N 2 O, water and mixtures thereof.
Claim 18
Dependent Claim
26 words
The method according to claim 15 wherein the oxidizing agent is a mixture selected from the group consisting of oxygen and water, and hydrogen and water.
Claim 19
Dependent Claim
32 words
The method according to claim 16 wherein the alumina surface of the porous alumina substrate is doped with a metal selected from F block lanthanides of the Periodic Table of the Elements.
Claim 20
Dependent Claim
53 words
An ultrathin inorganic membrane formed by the method according to claim 1 wherein the membrane comprises a multicomponent oxide layer having a thickness less than or equal to about 0.5 μm which is deposited onto a surface layer of a porous substrate having an average pore diameter of less than about 50 nm.
Claim 21
Dependent Claim
40 words
The inorganic membrane according to claim 18 wherein the porous substrate is selected from the group consisting of alumina, silica, magnesia, titania, a high temperature oxygen compatible metal alloy, and a metal oxide stabilized zirconia, and compounds and mixtures thereof.
Claim 22
Dependent Claim
36 words
The inorganic membrane according to claim 19 wherein the multicomponent oxide comprises two or more metals selected from Groups 2, 3, 4 and 15 and the F block lanthanides of the Periodic Table of the Elements.
Claim 23
Dependent Claim
14 words
The inorganic membrane according to claim 20 wherein the multicomponent oxide further comprises zirconia.
Claim 24
Dependent Claim
27 words
The inorganic membrane according to claim 19 wherein the porous surface layer of the porous substrate comprises a composition differing from the composition of the porous substrate.
Claim 25
Dependent Claim
53 words
An inorganic membrane formed by the process according to claim 9 which comprises a yttria-stabilized zirconia layer having a thickness less than or equal to about 0.5 μm which has been deposited onto a metal-doped porous alumina surface layer of an alumina substrate having an average pore diameter of less about 50 nm.
Claim 26
Dependent Claim
17 words
The inorganic membrane according to claim 23 wherein the metal-doped porous alumina surface layer comprises lanthanum-doped alumina.
References Cited (Backward Citations)
US5106654A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-03 | 1996-05-04 | 1996-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-03 | 2000-05-04 | 2000-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-03 | 2004-05-04 | 2004-11-03 | $7700.00 | Window Closed / Lapsed |