Catalyst for purification of exhaust gases of diesel engines and method of use
Assignee: DMC2 Degussa Metals Catalysts Cerdec AG
•
Filing: 1991-03-11
•
Granted: 1992-10-20
•
Expires: 2011-03-11
Abstract
Abstract An open-cell, monolithic catalyst for the purification of diesel-engine exhaust gas with a coating of finely divided inorganic oxides containing vanadium and platinum group metal as active components. The active components of the oxidic coating are added as water-soluble precursors which are then converted by means of tempering, preferably in an atmosphere of hydrogen, into the active component.
Inventors
- 👤 Rainer Domesle
- 👤 Bernd Engler
- 👤 Edgar Koberstein
- 👤 Herbert Voelker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:41
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01J; B01J37/00; B01J37/02; B01D53/92; B01D53/94; B01D53/944; B01J23/00; B01J23/38; B01J23/54; B01J23/56; B01J23/64; B01J23/648; B01J23/6482; F; F02; F02B; F02B3/00; F02B3/06; Y; Y02; Y02A; Y02A50/00; Y02A50/20
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
223 words
A catalyst capable of operating in a continuous manner without soot particulate separation and without cyclical regeneration for the oxidative purification of the exhaust gases of diesel engines and having a high conversion performance for hydrocarbons and carbon monoxide at low temperatures and inhibited oxidation action in respect of NO and SO 2 comprising: an open-cell monolithic or honeycombed inert carrier of ceramic or metal, said inert carrier having a plurality of channels essentially parallel to the direction of flow of said exhaust gases, such that exhaust gas flows freely through the channels of the carrier, said channels having interior surfaces coated with an activity-enhancing support material selected from the group consisting of finely divided aluminum oxide, titanium oxide, silicon oxide, zeolite and mixtures thereof, said activity-enhancing support material having deposited thereon a catalytically active component of at least one platinum group metal selected from the group consisting of platinum, palladium, rhodium and iridium, the platinum group metal or metals being doped with vanadium or being in contact with an oxidic vanadium compound, said catalyst being prepared by impregnating said activity-enhancing support material with a solution of compounds of said platinum group metals and a solution of a vanadium compound, said impregnating taking place simultaneously or successively in any desired sequence, thereafter drying, optionally calcining at a temperature of at least 200° C.
Claim 2
Dependent Claim
223 words
A catalyst capable of operating in a continuous manner without soot particulate separation and without cyclical regeneration for the oxidative purification of the exhaust gases of diesel engines and having a high conversion performance for hydrocarbons and carbon monoxide at low temperatures and inhibited oxidation action in respect of NO and SO 2 comprising: an open-cell monolithic or honeycombed inert carrier of ceramic or metal, said inert carrier having a plurality of channels essentially parallel to the direction of flow of said exhaust gases, such that exhaust gas flows freely through the channels of the carrier, said channels having interior surfaces coated with an activity-enhancing support material selected from the group consisting of finely divided aluminum oxide, titanium oxide, silicon oxide, zeolite and mixtures thereof, said activity-enhancing support material having deposited thereon a catalytically active component of at least one platinum group metal selected from the group consisting of platinum, palladium, rhodium and iridium, the platinum group metal or metals being doped with vanadium or being in contact with an oxidic vanadium compound, said catalyst being prepared by impregnating said activity-enhancing support material with a solution of compounds of said platinum group metals and a solution of a vanadium compound, said impregnating taking place simultaneously or successively in any desired sequence, thereafter drying, optionally calcining at a temperature of at least 200° C.
Claim 3
Dependent Claim
47 words
The catalyst according to claim 1, characterized in that the activity-enhancing support material includes a mixture of aluminum oxide with titanium oxide, silica and/or zeolite in a weight ratio between aluminum oxide and the other oxides of 90:10 to 10:90, thereby providing a finely divided support material.
Claim 4
Dependent Claim
69 words
The catalyst according to claim 1, characterized in that the activity-enhancing support material is present in a concentration in the range of 30-250 g/dm 3 catalyst volume, the vanadium, calculated as V 2 O 5 , is present in a concentration in the range of 0.15-15 g/dm 3 catalyst volume and the platinum group metals are present in a concentration in the range of 0.1-7 g/dm 3 catalyst volume.
Claim 5
Dependent Claim
23 words
The catalyst according to claim 3 wherein the activity-enhancing support material is present in a concentration the range 75-180 g/dm 3 catalyst volume.
Claim 6
Dependent Claim
24 words
The catalyst according to claim 3 wherein the activity-enhancing support material is present in a concentration the range of 90-150 g/dm 3 catalyst volume.
Claim 7
Dependent Claim
26 words
The catalyst according to claim 1, characterized in that the cell density of the monolithic or honeycombed inert carrier is 5 to 100 cells/cm 2 .
Claim 8
Dependent Claim
19 words
The catalyst according to claim 1, characterized in that platinum and/or palladium is present as said platinum group metal.
Claim 9
Dependent Claim
20 words
The catalyst according to claim 1, wherein during calcining the catalyst is subjected to a current of gas containing hydrogen.
Claim 10
Dependent Claim
57 words
The catalyst according to claim 1, wherein said activity-enhancing support material includes an additional material selected from the group consisting of MgO, CeO 2 , GeO 2 , ZrO 2 , HfO 2 , ThO 2 , Nb 2 O 5 , WO 3 , MoO 3 , magnesium silicate, aluminum silicate, magnesium titanate, and mixtures thereof.
Claim 11
Dependent Claim
57 words
The catalyst according to claim 2, wherein said activity-enhancing support material includes an additional material selected from the group consisting of MgO, CeO 2 , GeO 2 , ZrO 2 , HfO 2 , ThO 2 , Nb 2 O 5 , WO 3 , MoO 3 , magnesium silicate, aluminum silicate, magnesium titanate, and mixtures thereof.
Claim 12
Dependent Claim
57 words
The catalyst according to claim 6, wherein said activity-enhancing support material includes an additional material selected from the group consisting of MgO, CeO 2 , GeO 2 , ZrO 2 , HfO 2 , ThO 2 , Nb 2 O 5 , WO 3 , MoO 3 , magnesium silicate, aluminum silicate, magnesium titanate, and mixtures thereof.
Claim 13
Dependent Claim
19 words
The catalyst according to claim 1, wherein said activity-enhancing support material includes a finely dispersed support of titanium oxide.
Claim 14
Dependent Claim
35 words
The catalyst according to claim 1, wherein said activity-enhancing support material includes a finely dispersed support of a mixture of titanium oxide with silicon dioxide in weight ratio ranging from 95 to 5:5 to 95.
Claim 15
Dependent Claim
26 words
The catalyst according to claim 13, wherein the weight ratio of titanium dioxide with silicon dioxide is in the range of 75 to 25:25 to 75.
Claim 16
Dependent Claim
35 words
The catalyst according to claim 1, wherein said activity-enhancing support material includes a finely dispersed support of a mixture of titanium oxide with zirconium dioxide in weight ratio ranging from 95 to 5:5 to 95.
Claim 17
Dependent Claim
26 words
The catalyst according to claim 15, wherein the weight ratio of titanium dioxide to zirconium dioxide is in the range of 75 to 25:25 to 75.
Claim 18
Independent Claim
175 words
A method of making a catalyst capable of operating in a continuous manner without soot particulate separation and without cyclical regeneration and suitable for the oxidative purification of the exhaust gases of diesel engines, comprising the steps of: impregnating an activity-enhancing support material with a vanadium compound and at least one platinum group metal, said support material being selected from the group consisting of finely divided aluminum oxide, titanium oxide, silica, zeolite and mixtures thereof, and said impregnation being made with a solution of at least one compound including the platinum group or metals and a solution of a vanadium compound, said impregnating taking place simultaneously or successively in any desired sequence; drying the impregnated support material; and optionally calcining at a temperature of at least 200° C., and wherein said impregnating with at least one of said vanadium compound and said platinum group metal takes place after depositing said activity-enhancing support material onto an open-celled monolithic or honeycombed inert carrier, said open celled carrier allowing exhaust gas to flow freely through the cells thereof.
Claim 19
Independent Claim
175 words
A method of making a catalyst capable of operating in a continuous manner without soot particulate separation and without cyclical regeneration and suitable for the oxidative purification of the exhaust gases of diesel engines, comprising the steps of: impregnating an activity-enhancing support material with a vanadium compound and at least one platinum group metal, said support material being selected from the group consisting of finely divided aluminum oxide, titanium oxide, silica, zeolite and mixtures thereof, and said impregnation being made with a solution of at least one compound including the platinum group or metals and a solution of a vanadium compound, said impregnating taking place simultaneously or successively in any desired sequence; drying the impregnated support material; and optionally calcining at a temperature of at least 200° C., and wherein said impregnating with at least one of said vanadium compound and said platinum group metal takes place after depositing said activity-enhancing support material onto an open-celled monolithic or honeycombed inert carrier, said open celled carrier allowing exhaust gas to flow freely through the cells thereof.
Claim 20
Dependent Claim
17 words
The method according to claim 17 which further comprises calcining in a current of gas containing hydrogen.
Claim 21
Dependent Claim
40 words
The catalyst according to claim 1, wherein the impregnating of the activity-enhancing support material with at least one of said vanadium compound or said platinum group metal compound takes place after depositing said activity-enhancing support material on said inert carrier.
Claim 22
Dependent Claim
40 words
The catalyst according to claim 1, wherein the impregnating of the activity-enhancing support material with at least one of said vanadium compound or said platinum group metal compound takes place before depositing said activity-enhancing support material on said inert carrier.
Claim 23
Independent Claim
175 words
A method of making a catalyst capable of operating in a continuous manner without soot particulate separation and without cyclical regeneration and suitable for the oxidative purification of the exhaust gases of diesel engines, comprising the steps of: impregnating an activity-enhancing support material with a vanadium compound and at least one platinum group metal, said support material being selected from the group consisting of finely divided aluminum oxide, titanium oxide, silica, zeolite and mixtures thereof, and said impregnation being made with a solution of at least one compound including the platinum group metal or metals and a solution of a vanadium compound, said impregnating taking place simultaneously or successively in any desired sequence; drying the impregnated support material; and optionally calcining at a temperature of at least 200° C., and wherein said impregnating with at least one of said vanadium compound and said platinum group metal takes place before depositing said activity-enhancing support material onto an open-celled monolithic or honeycombed inert carrier, said open-celled carrier allowing exhaust gas to flow freely through the cells thereof.
Claim 24
Independent Claim
175 words
A method of making a catalyst capable of operating in a continuous manner without soot particulate separation and without cyclical regeneration and suitable for the oxidative purification of the exhaust gases of diesel engines, comprising the steps of: impregnating an activity-enhancing support material with a vanadium compound and at least one platinum group metal, said support material being selected from the group consisting of finely divided aluminum oxide, titanium oxide, silica, zeolite and mixtures thereof, and said impregnation being made with a solution of at least one compound including the platinum group metal or metals and a solution of a vanadium compound, said impregnating taking place simultaneously or successively in any desired sequence; drying the impregnated support material; and optionally calcining at a temperature of at least 200° C., and wherein said impregnating with at least one of said vanadium compound and said platinum group metal takes place before depositing said activity-enhancing support material onto an open-celled monolithic or honeycombed inert carrier, said open-celled carrier allowing exhaust gas to flow freely through the cells thereof.
Claim 25
Dependent Claim
17 words
The method according to claim 21, which further comprises calcining in a current of gas containing hydrogen.
References Cited (Backward Citations)
US3864451A
Cited
JPS5413816A
Cited
US4455393A
Cited
US4477417A
Cited
US4515758A
Cited
US4588707A
Cited
US4828807A
Cited
US4900517A
Cited
JPS6134972A
Cited
EP0174495A1
Cited
EP0211233A1
Cited
US4759918A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-10-20 | 1996-04-20 | 1996-10-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-10-20 | 2000-04-20 | 2000-10-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-10-20 | 2004-04-20 | 2004-10-20 | $7700.00 | Window Closed / Lapsed |