Method of preparing UV absorbant and abrasion-resistant transparent plastic articles
Assignee: SABIC Global Technologies BV
•
Filing: 1991-12-30
•
Granted: 1992-10-20
•
Expires: 2011-12-30
Abstract
Abstract A method of preparing transparent plastic articles having an improved protective stratum thereon. The protective stratum provides protection from UV light and abrasion. The article includes a polycarbonate substrate and multi-layered coating applied by plasma enhanced chemical vapor deposition on surface of the substrate.
Inventors
- 👤 Stefan J. Rzad
- 👤 Douglas J. Conley
- 👤 Clive W. Reed
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 07:53
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J7/123; B; B05; B05D; B05D1/00; B05D1/62; B05D7/00; B05D7/24; C09; C09D; C09D4/00; B05D2201/00; B05D2201/02
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
134 words
A method of forming a transparent, abrasion resistant and ultraviolet light absorbant article comprising: plasma enhanced chemical vapor deposition of an interfacial layer of an adherent resinous composition on the surfaces of said article; plasma enhanced chemical vapor deposition of a layer of an ultraviolet light absorbant composition selected from the group consisting of zinc oxide, titanium dioxide, cerium dioxide and vanadium pentoxide on said interfacial layer of said adherent resinous composition; and plasma enhanced chemical vapor deposition of a layer of an abrasion resistant composition on top of said layer of said ultraviolet light absorbant composition, said layer of said abrasion resistant composition exhibiting increase in haze of less than 15% after 1000 cycles under The Taber Abrasion Test, designated by American Society for Testing and Materials, as ASTM D1044 or its equivalent.
Claim 2
Independent Claim
134 words
A method of forming a transparent, abrasion resistant and ultraviolet light absorbant article comprising: plasma enhanced chemical vapor deposition of an interfacial layer of an adherent resinous composition on the surfaces of said article; plasma enhanced chemical vapor deposition of a layer of an ultraviolet light absorbant composition selected from the group consisting of zinc oxide, titanium dioxide, cerium dioxide and vanadium pentoxide on said interfacial layer of said adherent resinous composition; and plasma enhanced chemical vapor deposition of a layer of an abrasion resistant composition on top of said layer of said ultraviolet light absorbant composition, said layer of said abrasion resistant composition exhibiting increase in haze of less than 15% after 1000 cycles under The Taber Abrasion Test, designated by American Society for Testing and Materials, as ASTM D1044 or its equivalent.
Claim 3
Dependent Claim
16 words
The method according to claim 1 wherein said article is made of polycarbonate or polymethyl methacrylate.
Claim 4
Dependent Claim
21 words
The method according to claim 1 wherein said adherent resinous composition is plasma polymerized during said plasma enhanced chemical vapor deposition.
Claim 5
Dependent Claim
27 words
The method according to claim 1 wherein said adherent resinous composition comprises an interfacial material selected from the group consisting of organosilicon, organometallic, acrylic, and polyolefin materials.
Claim 6
Dependent Claim
20 words
The method according to claim 4 wherein said interfacial material is formed by polymerizing an olefinic monomer in the plasma.
Claim 7
Dependent Claim
20 words
The method according to claim 4 wherein said interfacial material is formed by polymerizing an acrylic monomer in the plasma.
Claim 8
Dependent Claim
20 words
The method according to claim 4 wherein said interfacial material is formed by polymerizing an organosilicon monomer in the plasma.
Claim 9
Dependent Claim
23 words
The method according to claim 7 wherein said organosilicon monomer is selected from the group consisting of hexamethyldisilazane, hexamethyldisiloxane, vinyl trimethylsilane, and octamethylcyclotetrasiloxane.
Claim 10
Dependent Claim
37 words
The method according to claim 1 wherein said abrasion resistant composition is selected from the group consisting of silicon carbide, silicon dioxide, silicon nitride, silicon oxynitride, boron oxide, boron nitride, aluminum oxide, aluminum nitride, and mixtures thereof.
Claim 11
Dependent Claim
22 words
The transparent, abrasion resistant and ultraviolet light absorbant article produced according to the method of claim 1 on a transparent plastic substrate.
Claim 12
Independent Claim
160 words
A method of forming a transparent, abrasion resistant and ultraviolet light absorbant polycarbonate article comprising: plasma enhanced chemical vapor deposition of an interfacial layer having thickness of about 100 Å to about 10,000 Å of an adherent resinous composition of hexamethyldisiloxane on the surfaces of said polycarbonate article; plasma enhanced chemical vapor deposition of a layer having thickness of about 1000 Å to about 10,000 Å of an ultraviolet light absorbant composition of titanium dioxide on top of said layer of said adherent resinous composition; and plasma enhanced chemical vapor deposition of a layer having thickness of about 20,000 Å to about 90,000 Å of an abrasion resistant composition of silicon dioxide on top of said layer of said ultraviolet light absorbant composition, said layer of said abrasion resistant composition exhibiting increase in haze of less than 15% after 1000 cycles under The Taber Abrasion Test, designated by American Society for Testing and Materials, as ASTM D1044 or its equivalent.
Claim 13
Independent Claim
160 words
A method of forming a transparent, abrasion resistant and ultraviolet light absorbant polycarbonate article comprising: plasma enhanced chemical vapor deposition of an interfacial layer having thickness of about 100 Å to about 10,000 Å of an adherent resinous composition of hexamethyldisiloxane on the surfaces of said polycarbonate article; plasma enhanced chemical vapor deposition of a layer having thickness of about 1000 Å to about 10,000 Å of an ultraviolet light absorbant composition of titanium dioxide on top of said layer of said adherent resinous composition; and plasma enhanced chemical vapor deposition of a layer having thickness of about 20,000 Å to about 90,000 Å of an abrasion resistant composition of silicon dioxide on top of said layer of said ultraviolet light absorbant composition, said layer of said abrasion resistant composition exhibiting increase in haze of less than 15% after 1000 cycles under The Taber Abrasion Test, designated by American Society for Testing and Materials, as ASTM D1044 or its equivalent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-10-20 | 1996-04-20 | 1996-10-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-10-20 | 2000-04-20 | 2000-10-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-10-20 | 2004-04-20 | 2004-10-20 | $7700.00 | Window Closed / Lapsed |