High temperature resistant reticulated foam structure and process
Assignee: Ultramet Inc
•
Filing: 1991-07-16
•
Granted: 1992-10-13
•
Expires: 2011-07-16
Abstract
Abstract A high temperature resistant reticulated porous foam structure for use as a diesel emission particulate trap. A reticulated porous foam substrate which is capable of maintaining its structural integrity at temperatures in excess of approximately 2500, and preferably 2700, degrees Fahrenheit is coated with a formed in situ oxidation resistant coating which extends substantially throughout the interstices of the porous foam structure. The coating comprises very thin alternate layers of silicon carbide and a carbide formed from a Group IVA metal which has a melting point in excess of approximately 1850 degrees Centigrade.
Inventors
- 👤 Richard B. Kaplan
- 👤 Hugh O. Pierson
- 👤 Robert H. Tuffias
- 👤 Brian E. Williams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 16:30
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/38; C23C16/32; C23C16/325; C23C28/00; C23C28/04; F; F02; F02B; F02B3/00; F02B3/06; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/249921; Y10T428/249953; Y10T428/249967; Y10T428/249969; Y10T428/30
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
128 words
A highly permeable high temperature resistant shaped structure capable of withstanding repeated cycling in an oxidizing environment to temperatures in excess of approximately 2200 degrees Fahrenheit comprising: a porous substrate comprising material which is capable of maintaining its structural integrity at temperatures in excess of approximately 2000 degrees Fahrenheit in the absence of oxygen, and a formed in situ structurally stable oxidation resistant coating extending substantially throughout the interstices of said permeable structure, said coating comprising very thin alternate layers of silicon carbide and a carbide formed from a Group IVA metal having a melting point in excess of approximately 1850 degrees Centrigrade, said alternate layers including at least two such layers of silicon carbide and two such layers of a carbide formed from said Group IVA metal.
Claim 2
Dependent Claim
128 words
A highly permeable high temperature resistant shaped structure capable of withstanding repeated cycling in an oxidizing environment to temperatures in excess of approximately 2200 degrees Fahrenheit comprising: a porous substrate comprising material which is capable of maintaining its structural integrity at temperatures in excess of approximately 2000 degrees Fahrenheit in the absence of oxygen, and a formed in situ structurally stable oxidation resistant coating extending substantially throughout the interstices of said permeable structure, said coating comprising very thin alternate layers of silicon carbide and a carbide formed from a Group IVA metal having a melting point in excess of approximately 1850 degrees Centrigrade, said alternate layers including at least two such layers of silicon carbide and two such layers of a carbide formed from said Group IVA metal.
Claim 3
Dependent Claim
15 words
A high temperature resistant porous structure of claim 1 wherein said substrate comprises porous carbon.
Claim 4
Dependent Claim
15 words
A high temperature resistant porous structure of claim 1 wherein said substrate comprises porous graphite.
Claim 5
Dependent Claim
15 words
A high temperature resistant porous structure of claim 1 wherein said substrate comprises porous metal.
Claim 6
Dependent Claim
16 words
A high temperature resistant porous structure of claim 1 wherein said substrate comprises porous carbon-carbon composite.
Claim 7
Dependent Claim
15 words
A high temperature resistant porous structure of claim 1 wherein said substrate comprises porous ceramic.
Claim 8
Dependent Claim
15 words
A high temperature resistant porous structure of claim 1 wherein said substrate comprises porous cermet.
Claim 9
Dependent Claim
22 words
A high temperature resistant porous structure of claim 1 wherein each of said layers is from approximately 0.1 to 5 microns thick.
Claim 10
Dependent Claim
20 words
A high temperature resistant porous structure of claim 1 wherein said coating is from approximately 0.5 to 5 mils thick.
Claim 11
Dependent Claim
43 words
A high temperature resistant porous structure of claim 1 wherein said substrate comprises a shaped porous foamed carbon structure having from approximately 20 to 200 pores per inch and a wall thickness in at least one dimension of less than approximately 2 inches.
Claim 12
Dependent Claim
21 words
A high temperature resistant porous structure of claim 1 wherein said structure has from approximately 20 to 200 pores per inch.
Claim 13
Dependent Claim
24 words
A high temperature resistant porous structure of claim 1 wherein said structure has a density of less than about 3 grams per cubic centimeter.
Claim 14
Dependent Claim
23 words
A high temperature resistant porous structure of claim 1 wherein said coating comprises alternate layers of silicon carbide, hafnium carbide and hafnium boride.
Claim 15
Dependent Claim
21 words
A high temperature resistant porous structure of claim 1 wherein said coating comprises alternate layers of silicon carbide and hafnium carbide.
Claim 16
Dependent Claim
21 words
A high temperature resistant porous structure of claim 1 wherein said coating comprises alternate layers of silicon carbide and zirconium carbide.
Claim 17
Dependent Claim
145 words
Process for forming a high temperature resistant porous structure capable of withstanding repeated cycles of cooling and heating to temperatures in excess of approximately 2200 degrees Fahrenheit in an oxidizing environment comprising: selecting a highly permeable substrate, and applying a high temperature oxidation resistant coating to said substrate at an application temperature in excess of approximately 2000 degrees Fahrenheit in a non-oxidizing environment, said coating comprising alternate thin layers of silicon carbide and a carbide formed from a Group IVA metal having a melting point in excess of about 1850 degrees centrigrade, said porous substrate being composed of material which is capable of maintaining its structural integrity in the absence of oxygen at temperatures in excess of said application temperature, applying at least two of said silicon carbide layers and at least two of said layers of a carbide formed from said Group IVA metal.
Claim 18
Dependent Claim
145 words
Process for forming a high temperature resistant porous structure capable of withstanding repeated cycles of cooling and heating to temperatures in excess of approximately 2200 degrees Fahrenheit in an oxidizing environment comprising: selecting a highly permeable substrate, and applying a high temperature oxidation resistant coating to said substrate at an application temperature in excess of approximately 2000 degrees Fahrenheit in a non-oxidizing environment, said coating comprising alternate thin layers of silicon carbide and a carbide formed from a Group IVA metal having a melting point in excess of about 1850 degrees centrigrade, said porous substrate being composed of material which is capable of maintaining its structural integrity in the absence of oxygen at temperatures in excess of said application temperature, applying at least two of said silicon carbide layers and at least two of said layers of a carbide formed from said Group IVA metal.
Claim 19
Dependent Claim
14 words
A process of claim 16 wherein said applying comprises a chemical vapor deposition process.
References Cited (Backward Citations)
US4863798A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-10-13 | 1996-04-13 | 1996-10-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-10-13 | 2000-04-13 | 2000-10-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-10-13 | 2004-04-13 | 2004-10-13 | $7700.00 | Window Closed / Lapsed |