Alkalline-solution-developable liquid photographic composition
Assignee: Transpacific IP Ltd
•
Filing: 1990-08-10
•
Granted: 1992-10-06
•
Expires: 2010-08-10
Abstract
Abstract An alkaline-solution-developable liquid image-producing composition useful as a permanent protective layer for printed circuit boards is disclosed comprising at least: (1) an acrylic copolymer with hyroxy group, carboxyl group and branched unsaturated carbon double bond. Its number average molecular weight is 3,000 to 10,000 and its acid value is at least 30 mg KOH/g; (2) a photo reactive monomer with hydroxy group, the number of the unsaturated carbon double bond functional groups should be not less than 2; (3) a melamine compound; and (4) a free radical photo initiator.
Inventors
- 👤 Rong-Jer Lee
- 👤 Chein-Dhau Lee
- 👤 Wen-Shin Shen
- 👤 Dhei-Jhai Lin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 02:09
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/027; G03F7/032; G03F7/033; Y; Y10; Y10S; Y10S430/00; Y10S430/1053; Y10S430/1055; Y10S430/106; Y10S430/107; Y10S430/11; Y10S430/111
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
163 words
A photopolymerizable composition which, after being exposed imagewise, can be developed with an aqueous alkaline solution, said composition comprising: a) from 20 to 80 percent by weight of a linear acrylic copolymer consisting essentially of hydroxyl-containing units, carboxyl-containing units and pendant unsaturated double bond-containing units, where the number average molecular weight of said copolymer is from 3,000 to 100,000, the acid value of said copolymer is at least 30 mg KOH/g, said hydroxyl-containing units constitute from 3 to 15 percent by mole of said copolymer, said carboxyl-containing units constitute from 5 to 45 percent by mole of said copolymer and said pendant unsaturated double bond-containing units constitute from 5 to 40 percent by mole of said copolymer; b) from 5 to 40 percent by weight of a hydroxyl-containing photoreactive monomer which contains at least 2 double bonds; c) from 5 to 30 percent by weight of a melamine compound; and d) from 0.5 to 12 percent by weight of a free radical photoinitiator.
Claim 2
Dependent Claim
163 words
A photopolymerizable composition which, after being exposed imagewise, can be developed with an aqueous alkaline solution, said composition comprising: a) from 20 to 80 percent by weight of a linear acrylic copolymer consisting essentially of hydroxyl-containing units, carboxyl-containing units and pendant unsaturated double bond-containing units, where the number average molecular weight of said copolymer is from 3,000 to 100,000, the acid value of said copolymer is at least 30 mg KOH/g, said hydroxyl-containing units constitute from 3 to 15 percent by mole of said copolymer, said carboxyl-containing units constitute from 5 to 45 percent by mole of said copolymer and said pendant unsaturated double bond-containing units constitute from 5 to 40 percent by mole of said copolymer; b) from 5 to 40 percent by weight of a hydroxyl-containing photoreactive monomer which contains at least 2 double bonds; c) from 5 to 30 percent by weight of a melamine compound; and d) from 0.5 to 12 percent by weight of a free radical photoinitiator.
Claim 3
Dependent Claim
40 words
A photopolymerizable composition according to claim 1, wherein said hydroxyl-containing photoreactive monomer is selected from the group consisting of pentaerythrite triacrylate, dipentaerythrite hydroxyl penta-acrylate, pentaerythrite diacrylate, quaternary pentaerythrite dimethacrylate, pentaerythrite trimethyl acrylate, bis(acryloxyethyl) hydroxy ethyl isocyanurate and any mixture thereof.
Claim 4
Dependent Claim
36 words
A photopolymerizable composition according to claim 1, wherein said melamine compound is hexamethoxymethyl melamine in which the methoxy contains from 2 to 4 carbon atoms and can partly or wholly be substituted by hydroxyl or alkoxyl.
Claim 5
Dependent Claim
34 words
A photopolymerizable composition according to claim 1, wherein said photoinitiator is selected from the group consisting of benzoin, benzoin alkyl ether, benzil ketals, acetophenone, dimethoxy-2-phenyl acetophenone, diphenyl ketone, 4,4'-dimethylamine diphenylketone, 2-chlorothioxanthone, and 1-hydroxycyclohexyl phenylketone.
Claim 6
Dependent Claim
85 words
A photopolymerizable composition according to claim 1 wherein said linear acrylic copolymer is produced by reacting (a) a hydroxyl acrylic monomer; (b) a carboxyl acrylic monomer; and (c) an acrylate monomer for forming a linear polymer with the following structure: ##STR6## wherein R 1 =H, CH 3 ; R 2 =C r H 2r+1 ; r=1 to 18; n, m, and p are integers; and also grafting said linear polymer with unsaturated double bond-containing compounds to form double bond-containing units pendant on said linear polymer.
Claim 7
Dependent Claim
106 words
A photopolymerizable composition according to claim 5, wherein the grafting reaction between unsaturated double bond-containing compounds and the linear acrylic polymer is selected from the reactions consisting of (i) substitution reaction between a compound having ##STR7## on the linear copolymer; (ii) condensation reaction between compounds having the formula of ##STR8## and the --COOH on the linear copolymer; (iii) condensation reaction between compounds having ##STR9## and the --OH or COOH on the linear copolymer, wherein R 1 is H or --CH 3 , and R 2 is a group involving no grafting reaction, and is selected from the group consisting of alkyl, alkoxy, alicyclic, and aryl groups.
Claim 8
Dependent Claim
59 words
A photopolymerizable composition according to claim 6 where the mole number of --OH groups contained in the grafted linear polymer occupy 3-15% of the mole number of the repeated units in the main chain of the grafted polymer and the mole number of --COOH groups occupy 5-40% of the mole number of the repeated units in the main chain.
Claim 9
Dependent Claim
21 words
The photopolymerizable composition of claim 7 wherein the amount of the grafted polymer is about 20-80% by weight of said composition.
Claim 10
Dependent Claim
21 words
The photopolymerizable composition of claim 8 wherein the amount of the grafted polymer is about 40-60% by weight of said composition.
References Cited (Backward Citations)
US3899611A
Cited
US4140605A
Cited
US4438189A
Cited
US4587199A
Cited
US4572887A
Cited
US4806450A
Cited
US4920037A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-10-06 | 1996-04-06 | 1996-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-10-06 | 2000-04-06 | 2000-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-10-06 | 2004-04-06 | 2004-10-06 | $7700.00 | Window Closed / Lapsed |