Laminated metal sheet
Assignee: Crown Packaging UK Ltd
•
Filing: 1990-04-18
•
Granted: 1992-09-22
•
Expires: 2010-04-18
Abstract
Abstract A laminated metal sheet, the metal sheet having adhered on at least one major surface thereof a film of a non-crystalline polyester, and a process for the preparation thereof. The laminated metal sheet is particularly useful for forming into drawn and wall ironed (DWI) cans. The laminate is also useful for forming other non-retorted packaging components.
Inventors
- 👤 Peter J. Heyes
- 👤 Nicholas J. Middleton
- 👤 Alison M. Brown
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 14:56
CPC Classifications
B; B32; B32B; B32B37/00; B32B37/14; B32B37/16; B32B37/20; B32B37/203; B32B37/206; B32B15/00; B32B15/04; B32B15/08; B32B38/00; B32B38/0036; B65; B65D; B65D1/00; B65D1/22; B65D1/26; B65D1/28; B32B2439/00; B32B2439/40; B32B2439/66
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
244 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a film of a non-crystalline polyester adhered directly thereto, said polyester being formed by polymerisation of a difunctional acid component comprising at least 60 mole percent terephthalic acid and a dihydric alcohol component comprising at least 60 mole percent ethylene glycol, which process comprises adhereing to one or both major surfaces of the metal sheet a monofilm of a polyester which is formed from a difunctional acid component comprising at least 60 mole percent terephthalic acid and a dihydric alcohol component comprising at least 60 mole percent ethylene glycol, said monofilm or monofilms being adhered to the metal sheet by heating the metal sheet to a temperature (T1) above the melting point of the polyester film, the temperature (T1) being such that during lamination of the polyester film or films to the metal sheet, the outer surfaces of the polyester film or films remain below their melting points, laminating the film or films to the metal sheet, reheating by indirect means the laminate to a temperature (T2) above the melting points of the polyester films; and after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester coating resins, the laminating reheating and quenching conditions being such that the polyester monofilm or monofilms in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 2
Dependent Claim
244 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a film of a non-crystalline polyester adhered directly thereto, said polyester being formed by polymerisation of a difunctional acid component comprising at least 60 mole percent terephthalic acid and a dihydric alcohol component comprising at least 60 mole percent ethylene glycol, which process comprises adhereing to one or both major surfaces of the metal sheet a monofilm of a polyester which is formed from a difunctional acid component comprising at least 60 mole percent terephthalic acid and a dihydric alcohol component comprising at least 60 mole percent ethylene glycol, said monofilm or monofilms being adhered to the metal sheet by heating the metal sheet to a temperature (T1) above the melting point of the polyester film, the temperature (T1) being such that during lamination of the polyester film or films to the metal sheet, the outer surfaces of the polyester film or films remain below their melting points, laminating the film or films to the metal sheet, reheating by indirect means the laminate to a temperature (T2) above the melting points of the polyester films; and after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester coating resins, the laminating reheating and quenching conditions being such that the polyester monofilm or monofilms in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 3
Dependent Claim
21 words
A process according to claim 1, wherein the temperature to which the laminate is re-heated after lamination is from 220°-330° C.
Claim 4
Dependent Claim
19 words
A process according to claim 1, wherein the indirect means for re-heating the laminate is an induction heating means.
Claim 5
Dependent Claim
24 words
A process according to claim 1, wherein the or each polyester film which is applied to the metal sheet is a cast thermoplastic polyester.
Claim 6
Dependent Claim
14 words
A process according to claim 4, wherein the cast thermoplastic polyester is polyethylene terephthalate.
Claim 7
Dependent Claim
29 words
A process according to claim 1, wherein the or each polyester film which is converted into non-crystalline or amorphous form is a biaxially oriented polyester having a semi-crystalline structure.
Claim 8
Dependent Claim
17 words
A process according to claim 6, wherein the biaxially oriented polyester is a biaxially oriented polyethylene terephthalate.
Claim 9
Dependent Claim
233 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a composite film of a non-crystalline polyester adhered directly thereto, said polyester comprising a copolyester formed by polymerisation of a difunctional acid component comprising at least 60 mole percent terephthalic acid and a dihydric alcohol component comprising at least 60 mole percent ethylene glycol, which process comprises adhering to one or both major surfaces of the metal sheet a composite film or films of said copolyester having a polyester inner layer (A1) and a polyester outer layer (A2), said composite film or films of said copolyester being adhered to the metal sheet by a process which comprises (i) heating the metal sheet to a temperature (T1) above the softening point of the polyester inner layer (A1) but below the melting point of the polyester outer layer (A2), (ii) laminating the film or films to the metal sheet, and (iii) reheating by indirect means the laminate so that the metal sheet reaches a temperature above the melting point of the or each polyester film, (iv) after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester coating resins, (v) the laminating, reheating, and quenching conditions being such that the polyester film or films in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 10
Dependent Claim
233 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a composite film of a non-crystalline polyester adhered directly thereto, said polyester comprising a copolyester formed by polymerisation of a difunctional acid component comprising at least 60 mole percent terephthalic acid and a dihydric alcohol component comprising at least 60 mole percent ethylene glycol, which process comprises adhering to one or both major surfaces of the metal sheet a composite film or films of said copolyester having a polyester inner layer (A1) and a polyester outer layer (A2), said composite film or films of said copolyester being adhered to the metal sheet by a process which comprises (i) heating the metal sheet to a temperature (T1) above the softening point of the polyester inner layer (A1) but below the melting point of the polyester outer layer (A2), (ii) laminating the film or films to the metal sheet, and (iii) reheating by indirect means the laminate so that the metal sheet reaches a temperature above the melting point of the or each polyester film, (iv) after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester coating resins, (v) the laminating, reheating, and quenching conditions being such that the polyester film or films in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 11
Dependent Claim
21 words
A process according to claim 8, wherein the temperature to which the laminate is re-heated after lamination is from 220°-330° C.
Claim 12
Dependent Claim
19 words
A process according to claim 8, wherein the indirect means for re-heating the laminate is an induction heating means.
Claim 13
Dependent Claim
29 words
A process according to claim 8, wherein the or each composite film of said polyester which is applied to the metal sheet is a co-extruded cast composite polyester film.
Claim 14
Dependent Claim
83 words
A process according to claim 8, wherein the or each composite film of said polyester which is applied to the metal sheet is a composite co-extruded polyester film comprising prior to the conversion into non-crystalline or amorphous form: (A1) an inner layer of a substantially non-crystalline linear polyester having a softening point below 200° C. and a melting point below 250° C. but above 150° C., and (A2) an outer layer of a biaxially oriented linear polyester having a crystallinity greater than 30%.
Claim 15
Dependent Claim
35 words
A process according to claim 12, wherein the linear polyester of inner layer (A1) is an amorphous copolymer of ethylene terephthalate and ethylene isophthalate or a copolymer formed from terephthalic acid and two dihydric alcohols.
Claim 16
Dependent Claim
16 words
A process according to claim 12, wherein the outer layer (A2) is biaxially oriented polyethylene terephthalate.
Claim 17
Dependent Claim
18 words
A process according to claim 8 wherein said film has an outer layer of coextruded polyethylene terephthalate homopolymer.
Claim 18
Dependent Claim
32 words
A process according to claim 8, wherein said film has an outer layer of coextruded polyethylene terephthalate homopolymer with an intrinsic viscosity between 0.6 and 0.7 as measured by gel permeation chromotography.
Claim 19
Dependent Claim
37 words
A process according to claim 8, wherein a different coextruded composite film is adhered to each side of said metal sheet and the outer layer of at least one of those films is a polyethylene terephthalate homopolymer.
Claim 20
Dependent Claim
223 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a film of a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of ethylene terephthalate and the remainder being less than about 40 mole percent of copolymerized ester units other than ethylene terephthalate, which process comprises adhering to one or both major surfaces of the metal sheet a monofilm or monofilms of said copolyester, said monofilm or monofilms being adhered to the metal sheet by heating the metal sheet to a temperature (T1) above the melting point of the polyester film, the temperature (T1) being such that during lamination of the polyester film or films to the metal sheet, the outer surfaces of the polyester film or films remain below their melting points; laminating the film or films to the metal sheet; reheating by indirect means the laminate to a temperature (T 2 ) above the melting points of the polyester films; and after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester film or films, the laminating, reheating and quenching conditions being such that the polyester monofilm or monofilms in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 21
Dependent Claim
223 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a film of a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of ethylene terephthalate and the remainder being less than about 40 mole percent of copolymerized ester units other than ethylene terephthalate, which process comprises adhering to one or both major surfaces of the metal sheet a monofilm or monofilms of said copolyester, said monofilm or monofilms being adhered to the metal sheet by heating the metal sheet to a temperature (T1) above the melting point of the polyester film, the temperature (T1) being such that during lamination of the polyester film or films to the metal sheet, the outer surfaces of the polyester film or films remain below their melting points; laminating the film or films to the metal sheet; reheating by indirect means the laminate to a temperature (T 2 ) above the melting points of the polyester films; and after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester film or films, the laminating, reheating and quenching conditions being such that the polyester monofilm or monofilms in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 22
Dependent Claim
39 words
The process according to claim 18, wherein said copolyester consists essentially of at least about 75 mole percent of ethylene terephthalate and the remainder being less than about 25 mole percent of copolymerized ester units other than ethylene terephthalate.
Claim 23
Dependent Claim
34 words
The process according to claim 19, wherein said copolyester consists essentially of at least about 80 mole percent of ethylene terephthalate and the remainder being less than about 20 mole percent of copolymerized isophthalate.
Claim 24
Dependent Claim
72 words
The process according to claim 18, wherein said copolyester is defined by: ##STR2## in which R 1 is a divalent hydrocarbon group at least 60 mole percent of which consists of p-phenylene groups; R 2 is a divalent hydrocarbon group at least 60 mole percent of which consists of --C 2 H 4 -- groups with A=1 and wherein, for the remaining mole percent of R 2 , A is an integer.
Claim 25
Dependent Claim
34 words
The process according to claim 21, wherein R 1 is at least 75 mole percent p-phenylene groups; and R 2 is at least 75 mole percent --C 2 H 4 -- groups with A=1.
Claim 26
Dependent Claim
34 words
The process according to claim 22, wherein R 2 is at least 80 mole percent p-phenylene groups; and R 2 is at least 80 mole percent --C 2 H 4 -- groups with A=1.
Claim 27
Dependent Claim
26 words
The process according to claim 21 wherein said remaining mole percent of R 2 is selected from the group consisting of diethylene glycol and cyclohexane dimethanol.
Claim 28
Dependent Claim
202 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a film of a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of polyethylene terephthalate which process comprises adhering to one or both major surfaces of the metal sheet a monofilm or monofilms of said copolyester, said monofilm or monofilms being adhered to the metal sheet by heating the metal sheet to a temperature (T1) above the melting point of the polyester film, the temperature (T1) being such that during lamination of the polyester film or films to the metal sheet, the outer surfaces of the polyester film or films remain below their melting points; laminating the film or films to the metal sheet; reheating by indirect means the laminate to a temperature (T2) above the melting points of the polyester films; and after holding at these elevated temperatures, quenching repidly the polyester coated metal to a temperature below the glass transition points of the polyester film or films, the laminating, reheating, quenching conditions being such that the polyester monofilm or monofilms in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 29
Dependent Claim
202 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a film of a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of polyethylene terephthalate which process comprises adhering to one or both major surfaces of the metal sheet a monofilm or monofilms of said copolyester, said monofilm or monofilms being adhered to the metal sheet by heating the metal sheet to a temperature (T1) above the melting point of the polyester film, the temperature (T1) being such that during lamination of the polyester film or films to the metal sheet, the outer surfaces of the polyester film or films remain below their melting points; laminating the film or films to the metal sheet; reheating by indirect means the laminate to a temperature (T2) above the melting points of the polyester films; and after holding at these elevated temperatures, quenching repidly the polyester coated metal to a temperature below the glass transition points of the polyester film or films, the laminating, reheating, quenching conditions being such that the polyester monofilm or monofilms in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 30
Dependent Claim
216 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a film or a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of polyethylene terephthalate and the remainder being less than about 40 mole percent of modifying agents which process comprises adhereing to one or both major surfaces of the metal sheet a monofilm or monofilms of said copolyester, said monofilm or monofilms being adhered to the metal sheet by heating the metal sheet to a temperature (T1) above the melting point of the polyester film, the temperature (T1) being such that during lamination of the polyester film or films to the metal sheet, the outer surfaces of the polyester film or films remain below their melting points; laminating the film or films to the metal sheet; reheating by indirect means the laminate to a temperature (T2) above the melting points of the polyester films; and after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester film or films, the laminating, reheating, and quenching conditions being such that the polyester monofilm and monofilms in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 31
Dependent Claim
216 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a film or a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of polyethylene terephthalate and the remainder being less than about 40 mole percent of modifying agents which process comprises adhereing to one or both major surfaces of the metal sheet a monofilm or monofilms of said copolyester, said monofilm or monofilms being adhered to the metal sheet by heating the metal sheet to a temperature (T1) above the melting point of the polyester film, the temperature (T1) being such that during lamination of the polyester film or films to the metal sheet, the outer surfaces of the polyester film or films remain below their melting points; laminating the film or films to the metal sheet; reheating by indirect means the laminate to a temperature (T2) above the melting points of the polyester films; and after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester film or films, the laminating, reheating, and quenching conditions being such that the polyester monofilm and monofilms in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 32
Dependent Claim
235 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a composite film of a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of ethylene terephthalate and the remainder being less than about 40 mole percent of copolymerized ester units other than ethylene terephthalate, which process comprises adhering to one or both major surfaces of the metal sheet a composite film or films of said copolyester having a polyester inner layer (A1) and a polyester outer layer (A2), said composite film or films of said copolyester being adhered to the metal sheet by a process which comprises: (i) heating the metal sheet to a temperature (T1) above the softening point of the polyester inner layer (A1) but below the melting point of the polyester outer layer (A2); (ii) laminating the film or films to the metal sheet; (iii) reheating by indirect means the laminate so that the metal sheet reaches a temperature above the melting point of the or each polyester film; and (iv) after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester coating resins; wherein (v) the laminating, reheating and quenching conditions are such that the polyester film or films in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 33
Dependent Claim
235 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a composite film of a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of ethylene terephthalate and the remainder being less than about 40 mole percent of copolymerized ester units other than ethylene terephthalate, which process comprises adhering to one or both major surfaces of the metal sheet a composite film or films of said copolyester having a polyester inner layer (A1) and a polyester outer layer (A2), said composite film or films of said copolyester being adhered to the metal sheet by a process which comprises: (i) heating the metal sheet to a temperature (T1) above the softening point of the polyester inner layer (A1) but below the melting point of the polyester outer layer (A2); (ii) laminating the film or films to the metal sheet; (iii) reheating by indirect means the laminate so that the metal sheet reaches a temperature above the melting point of the or each polyester film; and (iv) after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester coating resins; wherein (v) the laminating, reheating and quenching conditions are such that the polyester film or films in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 34
Dependent Claim
38 words
The process of claim 27, wherein said polyester consists essentially of at least about 75 mole percent of ethylene terephthalate and the remainder being less than about 25 mole percent of copolymerized ester units other than ethylene terephthalate.
Claim 35
Dependent Claim
29 words
The process of claim 28, wherein said polyester consists essentially of at least about 80 mole percent of polyethylene terephthalate and less than about 20 mole percent of isophthalate.
Claim 36
Dependent Claim
72 words
The process of claim 27, wherein said polyester is defined by: ##STR3## in which R 1 is a divalent hydrocarbon group of at least 60 mole percent of which consists of p-phenylene groups; R 2 is a divalent hydrocarbon group at least 60 mole percent of which consists of --C 2 H 4 -- groups with A=1, and wherein, for the remaining mole percent of R 2 , A is an integer.
Claim 37
Dependent Claim
33 words
The process of claim 30, wherein R 1 is at least 80 mole percent p-phenylene groups; and R 2 is at least 80 mole percent --C 2 H 4 -- groups with A=1.
Claim 38
Dependent Claim
33 words
The process of claim 30, wherein R 1 is at least 20 mole percent p-phenylene groups; and R 2 is at least 20 mole percent --C 2 H 4 -- groups with A=1.
Claim 39
Dependent Claim
26 words
The process according to claim 30 wherein said remaining mole percent of R 2 is selected from the group consisting of diethylene glycol and cyclohexane dimethanol.
Claim 40
Dependent Claim
215 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a composite film of a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of polyethylene terephthalate, which process comprises adhering to one or both major surfaces of the metal sheet a composite film of said copolyester having a polyester inner layer (A1) and a polyester outer layer (A2), said composite film or films of said copolyester being adhered to the metal sheet by a process which comprises: (i) heating the metal sheet to a temperature (T1) above the softening point of the polyester inner layer (A1) but below the melting point of the polyester outer layer (A2); (ii) laminating the film or films to the metal sheet; (iii) reheating by indirect means the laminate so that the metal sheet reaches a temperature above the melting point of the or each polyester film; and (iv) after holding at these elevated temperatures; quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester coating resins; wherein (v) the laminating, reheating and quenching conditions are such that the polyester film or films in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 41
Dependent Claim
215 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a composite film of a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of polyethylene terephthalate, which process comprises adhering to one or both major surfaces of the metal sheet a composite film of said copolyester having a polyester inner layer (A1) and a polyester outer layer (A2), said composite film or films of said copolyester being adhered to the metal sheet by a process which comprises: (i) heating the metal sheet to a temperature (T1) above the softening point of the polyester inner layer (A1) but below the melting point of the polyester outer layer (A2); (ii) laminating the film or films to the metal sheet; (iii) reheating by indirect means the laminate so that the metal sheet reaches a temperature above the melting point of the or each polyester film; and (iv) after holding at these elevated temperatures; quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester coating resins; wherein (v) the laminating, reheating and quenching conditions are such that the polyester film or films in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 42
Dependent Claim
228 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a composite film of a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of polyethylene terephthalate and the remainder being less than about 40 mole percent of modifying agents, which process comprises adhering to one or both major surfaces of the metal sheet a composite film of said polyester having a polyester inner layer (A1) and a polyester outer layer (A2), said composite film or films of said polyester being adhered to the metal sheet by a process which comprises: (i) heating the metal sheet to a temperature (T1) above the softening point of the polyester inner layer (A1) but below the melting point of the polyester outer layer (A2); (ii) laminating the film or films to the metal sheet; (iii) reheating by indirect means the laminate so that the metal sheet reaches a temperature above the melting point of the or each polyester film; and (iv) after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester coating resins; wherein (v) the laminating, reheating and quenching conditions are such that the polyester film or films in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
Claim 43
Dependent Claim
228 words
A process for preparing a laminated metal sheet having on one or both major surfaces thereof a composite film of a non-crystalline copolyester adhered directly thereto, said copolyester consisting essentially of a copolymer having at least about 60 mole percent of polyethylene terephthalate and the remainder being less than about 40 mole percent of modifying agents, which process comprises adhering to one or both major surfaces of the metal sheet a composite film of said polyester having a polyester inner layer (A1) and a polyester outer layer (A2), said composite film or films of said polyester being adhered to the metal sheet by a process which comprises: (i) heating the metal sheet to a temperature (T1) above the softening point of the polyester inner layer (A1) but below the melting point of the polyester outer layer (A2); (ii) laminating the film or films to the metal sheet; (iii) reheating by indirect means the laminate so that the metal sheet reaches a temperature above the melting point of the or each polyester film; and (iv) after holding at these elevated temperatures, quenching rapidly the polyester coated metal to a temperature below the glass transition points of the polyester coating resins; wherein (v) the laminating, reheating and quenching conditions are such that the polyester film or films in the metal/polymer laminate is or are converted into non-crystalline or amorphous form.
References Cited (Backward Citations)
US3647592A
Cited
US4143790A
Cited
US4362775A
Cited
US4319610A
Cited
US4322003A
Cited
US4935079A
Cited
US4330587A
Cited
JPS5882717A
Cited
US4614691A
Cited
JPS61149340A
Cited
US4735835A
Cited
US4849293A
Cited
US5059460A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-09-22 | 1996-03-23 | 1996-09-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-09-22 | 2000-03-23 | 2000-09-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-09-22 | 2004-03-23 | 2004-09-22 | $7700.00 | Window Closed / Lapsed |