High refractive index polymeric compositions suitable for use as expansile hydrogel intraocular lenses
Assignee: Individual
•
Filing: 1990-11-16
•
Granted: 1992-09-15
•
Expires: 2010-11-16
Abstract
Abstract Flexible, crosslinked polymeric compositions providing transparent hydrogels having a refractive index in the dehydrated (dry) state of at least about 1.53 and having equilibrium water content of at least 40% by weight of the polymeric gel for use an expansile intraocular lenses for surgical implantation. The dehydrated polymeric compositions are capable of hydration by natural fluids present in the eye to expand about 180% after implantation and in the fully swollen state have refractive indices of at least 1.40. They are prepared by polymerizing a multicomponent monomeric mixture consisting essentially of from about 50 to 75% by weight vinyl pyrrolidone, from about 3.25 to 12.5% by weight of 2-hydroxypropyl acrylate, from about 3.25 to 12.5% by weight of 2-hydroxyethyl methacrylate, from about 5 to 35% by weight of acrylamide and as a fifth component a crosslinking agent in an amount of from 1.25 to 15 parts per hundred parts of monomers by weight selected from the group consisting of tetraethylene glycol dimethacrylate and dibromoneopentyl glycol dimethacrylate.
Inventors
- 👤 Steven B. Siepser
- 👤 B. David Halpern
- 👤 Wolf Karo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 23:44
CPC Classifications
A; A61; A61L; A61L27/00; A61L27/14; A61L27/16; A61F; A61F2/00; A61F2/02; A61F2/14; A61F2/16; A61L27/50; A61L2430/00; A61L2430/16
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
108 words
A high refractive index polymeric composition which consists essentially of polymerized mixture of four monomeric components and a crosslinking agent, said mixture consisting essentially of from about 50 to 75% by weight of 2-vinyl pyrrolidone, from about 3.25 to 12.5% by weight of 2-hydroxypropyl acrylate, from about 5 to 35% by weight of acrylamide, from about 3.25 to 12.5% by weight 2-hydroxyethyl methacrylate, and from about 1.25 to 15 parts per hundred parts of said polymerized mixture by weight of a crosslinking agent selected from the group consisting of tetraethylene glycol dimethacrylate and dibromoneopentyl glycol dimethacrylate, the monomeric components totaling 100% by weight exclusive of the crosslinking agent.
Claim 2
Dependent Claim
108 words
A high refractive index polymeric composition which consists essentially of polymerized mixture of four monomeric components and a crosslinking agent, said mixture consisting essentially of from about 50 to 75% by weight of 2-vinyl pyrrolidone, from about 3.25 to 12.5% by weight of 2-hydroxypropyl acrylate, from about 5 to 35% by weight of acrylamide, from about 3.25 to 12.5% by weight 2-hydroxyethyl methacrylate, and from about 1.25 to 15 parts per hundred parts of said polymerized mixture by weight of a crosslinking agent selected from the group consisting of tetraethylene glycol dimethacrylate and dibromoneopentyl glycol dimethacrylate, the monomeric components totaling 100% by weight exclusive of the crosslinking agent.
Claim 3
Dependent Claim
93 words
An expansile, polymeric, optically clear hydrogel having a dehydrated state, wherein said hydrogel is capable of being formed in the dehydrated state into an intraocular lens and having (a) an equilibrium water content of at least 40 per cent by weight of the gel, (b) a refractive index measured from air with respect to the lens material of at least 1.53 in the dehydrated state and at least 1.40 in a swollen state, and (c) a swell factor in aqueous humor which renders the intraocular lens particularly suitable for small incision cataract surgery.
Claim 4
Dependent Claim
93 words
An expansile, polymeric, optically clear hydrogel having a dehydrated state, wherein said hydrogel is capable of being formed in the dehydrated state into an intraocular lens and having (a) an equilibrium water content of at least 40 per cent by weight of the gel, (b) a refractive index measured from air with respect to the lens material of at least 1.53 in the dehydrated state and at least 1.40 in a swollen state, and (c) a swell factor in aqueous humor which renders the intraocular lens particularly suitable for small incision cataract surgery.
Claim 5
Dependent Claim
15 words
The hydrogel of claim 2, wherein the swell factor of the hydrogel is about 180%.
Claim 6
Dependent Claim
40 words
The hydrogel of claim 3, wherein the hydrogel is sized to be inserted in its dehydrated state through an incision of less than 3.5 mm and expanded by the aqueous humor to a 5.8 mm optic in about twenty minutes.
Claim 7
Dependent Claim
56 words
A process for preparing a hydrogel of claim 1 which comprises polymerizing in the presence of catalytic initiator selected from the group consisting of benzoyl peroxide and hydrogen peroxide a monomeric mixture comprising 2-vinyl pyrrolidone, acrylamide, 2-hydroxypropyl acrylate, 2-hydroxethyl methacrylate and an additive selected form the group consisting of tetraethylene glycol dimethacrylate and dibromoneopentyl glycol dimethacrylate.
References Cited (Backward Citations)
US4036788A
Cited
US4123408A
Cited
US4430458A
Cited
US4608049A
Cited
US4693939A
Cited
US4556998A
Cited
US4849285A
Cited
US5092884A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-09-15 | 1996-03-16 | 1996-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-09-15 | 2000-03-16 | 2000-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-09-15 | 2004-03-16 | 2004-09-15 | $7700.00 | Window Closed / Lapsed |