Alginate gels

Claim 2

A covalently cross-linked alkali metal and ammonium alginate gel having a swellability of 10-300 times its volume in water or 2-70 time its volume in physiological saline solution while retaining its original shape.

Claim 3

An alginate gel according to claim 1 characterized in having an ability to swell 50-200 time s it original volume in water.

Claim 4

An alginate gel according to claim 2 characterized in having an ability to swell 200 times its original volume in water.

Claim 5

A process for the preparation of a cross-linked alkali metal or ammonium alginate gel which comprises (a) adding an aqueous solution of an alginate to an aqueous saline solution comprising polyvalent gelforming cations; (b) replacing the aqueous solvent with an organic solvent or mixture of organic solvents wherein a cross-linking agent is present; (c) reacting the alginate gel suspended in said organic solvent or solvent mixture with a cross-linking agent; (d) removing the remaining cross-linking agent by washing with an organic solvent, water or with both an organic solvent and water in several steps; (e) replacing gelforming cations with non-gelforming monovalent cations in aqueous phase; and (f) drying the thus obtained product.

Claim 6

A process for the preparation of a cross-linked alkali metal or ammonium alginate gel which comprises (a) adding an aqueous solution of an alginate to an aqueous saline solution comprising polyvalent gelforming cations; (b) replacing the aqueous solvent with an organic solvent or mixture of organic solvents wherein a cross-linking agent is present; (c) reacting the alginate gel suspended in said organic solvent or solvent mixture with a cross-linking agent; (d) removing the remaining cross-linking agent by washing with an organic solvent, water or with both an organic solvent and water in several steps; (e) replacing gelforming cations with non-gelforming monovalent cations in aqueous phase; and (f) drying the thus obtained product.

Claim 7

A process according to claim 4 wherein the alginate gel is dried by replacing the aqueous phase with an organic solvent or mixture of organic solvents, followed by drying in air or with an inert gas.

Claim 8

A process according to claim 5 wherein said organic solvent or organic solvent mixture is miscible with water.

Claim 9

A process according to claim 4 which comprises (a) adding a 0.8-5% w/v aqueous solution of an alginate to an aqueous salt solution comprising polyvalent gelforming cations in a concentration of 10 mM-1M, in the presence of a non gelling salt; (b) replacing the aqueous solvent with an organic solvent or mixture of organic solvents in which a cross-linking agent is soluble; (c) reacting the alginate gel in said organic solvent or organic solvent mixture with 0.1-4M concentration of a cross-linking agent for 1-8 hours; (d) removing the remaining cross-linking agent by washing with an organic solvent, water or with both an organic solvent and water in several steps; (e) replacing the gelforming cations with an excess of non-gelforming monovalent cations in aqueous solution; and (f) drying the resultant product by replacing the aqueous solvent with an organic solvent which is miscible with water followed by drying of the alginate gel with air or an inert gas in a fluidized bed.

Claim 10

A process according to claim 7 wherein in step (c) the reaction is in the presence of 0.5-15 mM CaCl 2 and 10-500 mM NaOH.

Claim 11

A process according to claim 7 wherein the organic solvent in step (f) is selected from the group consisting of acetone, methanol, ethanol and isopropylalcohol.

Claim 12

A process according to claim 4 which comprises (a) adding an aqueous solution f a sodium alginate, 1-3% w/v, to an aqueous solution of CaCl 2 , 0.1-0.5M, with addition of NaCl, 0.1-2M; (b) replacing the aqueous solvent with ethanol; (c) reacting the alginate gel suspended in the organic solvent, representing three volume parts, with 0.5-2 volume parts epichlorohydrin, int he presence of 1 volume part of 0.1M CaCl 2 and 1 volume part 10-500 mM NaOH at room temperature for 1-8 hours; (d) removing the remaining cross-linking agent by washing with ethanol; (e) replacing the Ca ions with Na ions by adding to 20-500 mM Na 2 EDTA in aqueous phase; and (f) drying the resultant gel by adding ethanol in a total amount of 6 times the gel volume in several portions with equilibration between the addition of each portion and drying the gel at room temperature.