US5141576A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Titanium composite materials coated with calcium phosphate compound and process for production thereof
Assignee: De Nora Permelec Ltd
•
Filing: 1990-04-04
•
Granted: 1992-08-25
•
Expires: 2010-04-04
Abstract
Abstract A titanium composite material is disclosed which comprises a titanium or titanium alloy substrate, a base layer formed thereon of a calcium phosphate compound resulting from calcination of a hydrochloric or nitric acid aqueous solution of the calcium phosphate compound, and a covering layer thereon of a calcium phosphate compound formed by sintering a suspension of the calcium phosphate compound applied to the base layer. The composite material is useful as a biological implant. It is produced by activating the surface of the substrate, forming the base layer by calcining the solution coated on the substrate and then forming the covering layer by sintering the suspension coated on the base layer. The covering layer may be hydrothermally treated to increase its crystallinity.
Inventors
- 👤 Takayuki Shimamune
- 👤 Masashi Hosonuma
- 👤 Yukiei Matsumoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 14:09
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/02; C23C18/12; C23C18/1225; A; A61; A61F; A61F2/00; A61F2/02; A61F2/30; A61F2/30767; A61L; A61L27/00; A61L27/28; A61L27/30; A61L27/32; C23C18/04; C23C18/1204; C23C18/1229; C23C18/1241; C23C22/00; C23C22/05; C23C22/06; C23C22/07; C23C22/08; C23C22/22; C23C22/73; C23C22/74; C23C22/78; A61F2/3094; A61F2002/30968; A61F2310/00; A61F2310/00005; A61F2310/00011; A61F2310/00023; A61F2310/00389; A61F2310/00592; A61F2310/00796
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
83 words
A process for producing a titanium composite material, which comprises activating the surface of a titanium or titanium alloy substrate, coating a hydrochloric or nitric acid aqueous solution of a calcium phosphate compound on the activated surface of the substrate, calcining the coating to form a base layer of the calcium phosphate compound on the substrate, thereafter coating a suspension of a calcium phosphate compound on the base layer, and sintering the coating to form a covering layer of the calcium phosphate compound.
Claim 2
Dependent Claim
83 words
A process for producing a titanium composite material, which comprises activating the surface of a titanium or titanium alloy substrate, coating a hydrochloric or nitric acid aqueous solution of a calcium phosphate compound on the activated surface of the substrate, calcining the coating to form a base layer of the calcium phosphate compound on the substrate, thereafter coating a suspension of a calcium phosphate compound on the base layer, and sintering the coating to form a covering layer of the calcium phosphate compound.
Claim 3
Dependent Claim
36 words
A process for producing a titanium composite material as in claim 1, wherein the calcium phosphate compound formed as the base layer and the covering layer is mainly at least one of hydroxyapatite and tricalcium phosphate.
Claim 4
Dependent Claim
32 words
A process for producing a titanium composite material as in claim 1, wherein the activation of the surface of said substrate is carried out by at least one of blasting and etching.
Claim 5
Dependent Claim
27 words
A process for producing a titanium composite material as in claim 1, wherein the calcination is carried out at a temperature of from 200° to 800° C.
Claim 6
Dependent Claim
27 words
A process for producing a titanium composite material as in claim 1, wherein the sintering is carried out at a temperature of from 300° to 900° C.
Claim 7
Dependent Claim
20 words
A process for producing a titanium composite material as in claim 1, wherein the covering layer is then hydrothermally treated.
Claim 8
Dependent Claim
30 words
A process for producing a titanium composite material as in claim 6, wherein the hydrothermal treatment is carried out in steam at a temperature of from 100° to 200° C.
References Cited (Backward Citations)
US4702930A
Cited
US4882196A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-08-25 | 1996-02-24 | 1996-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-08-25 | 2000-02-24 | 2000-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-08-25 | 2004-02-24 | 2004-08-25 | $7700.00 | Window Closed / Lapsed |