Selective deposition of tungsten on TiSi2
Assignee: Cornell Research Foundation Inc
•
Filing: 1991-03-11
•
Granted: 1992-08-11
•
Expires: 2011-03-11
Abstract
Abstract An improved process for preparing selective deposition of conductive metals on disilicide encroachment barriers allows the construction of integrated circuit components wherein the metal/disilicide interface is substantially free of O and/or F contamination. The level of interfacial oxygen and/or fluorine contamination in the selective W deposition on the TiSi 2 was substantially reduced or eliminated by first forming a C49 TiSi 2 phase on a substrate, selectively depositiong W on the C49 TiSi 2 phase and thereafter annealing a a (minimum) temperature sufficient to convert the high resistivity phase C49 TiSi 2 to the low resistivity phase C54 TiSi 2 .
Inventors
- 👤 David Stanasolovich
- 👤 Leslie H. Allen
- 👤 James W. Mayer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 15:30
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/056; H10W20/057; H10P; H10P14/00; H10P14/40; H10P14/42; H10P14/43; H10P14/432
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
147 words
An article prepared by a process for the selective deposition of tungsten on a titanium disilicide surface which comprises: 1) first forming a metastable titanium disilicide layer on a substrate wherein said disilicide is characterized as a metastable C49 titanium disilicide (TiSi 2 ); 2) selectively depositing tungsten (W) on said C49 TiSi 2 to give a product having a W/C49 TiSi 2 interface which is substantially free of oxygen and/or fluorine contamination; and 3) annealing the product of step 2 at a temperature and time sufficient to convert the C49 TiSi 2 to C54 TiSi 2 ; wherein the C49 TiSi 2 layer of step 2 is characterized by a resistivity of from about 80 to about 120 μohm-cm and is converted by annealing to a C54 TiSi 2 characterized by a resistivity in the range of from about 5 μohm-cm to about 50 μohm-cm centimeter.
Claim 2
Dependent Claim
147 words
An article prepared by a process for the selective deposition of tungsten on a titanium disilicide surface which comprises: 1) first forming a metastable titanium disilicide layer on a substrate wherein said disilicide is characterized as a metastable C49 titanium disilicide (TiSi 2 ); 2) selectively depositing tungsten (W) on said C49 TiSi 2 to give a product having a W/C49 TiSi 2 interface which is substantially free of oxygen and/or fluorine contamination; and 3) annealing the product of step 2 at a temperature and time sufficient to convert the C49 TiSi 2 to C54 TiSi 2 ; wherein the C49 TiSi 2 layer of step 2 is characterized by a resistivity of from about 80 to about 120 μohm-cm and is converted by annealing to a C54 TiSi 2 characterized by a resistivity in the range of from about 5 μohm-cm to about 50 μohm-cm centimeter.
Claim 3
Dependent Claim
20 words
The article of claim 1 wherein the tungsten deposition on C 49 TiSi 2 was effected by chemical vapor deposition.
Claim 4
Dependent Claim
48 words
The article of claim 1 wherein the conversion of C 49 TiSi 2 to C 54 TiSi 2 was effected by a rapid thermal anneal under protecting atmosphere using an anneal time of from about 10-35 seconds and anneal temperature of from about 575° C. to 700° C.
Claim 5
Dependent Claim
21 words
The article of claim 3 wherein the thermal anneal is conducted for 15-30 seconds at a temperature of about 700° C.
Claim 6
Dependent Claim
42 words
The article of claim 1 wherein the selective tungsten deposition is carried out by contacting the said C49 TiSi 2 layer with a mixture of WF 6 and hydrogen, a mixture of WF 6 with a silicon hydride or a mixture thereof.
Claim 7
Dependent Claim
105 words
A semiconductor or microelectronic device comprising a titanium disilicide encroachment barrier having deposited thereon a tungsten layer wherein the interface between the tungsten and the titanium disilicide is substantially free of oxygen and fluorine contamination; said tungsten having been deposited on a C 49 TiSi 2 characterized by a resistivity of from about 80 to about 120 μohm-cm followed by an annealing step at an anneal temperature of from about 575° C. to about 700° C. sufficient to convert the C 49 TiSi 2 to C 54 TiSi 2 characterized by a resistivity in the range of from about 5 μohm-cm to about 50 μohm-cm.
Claim 8
Dependent Claim
105 words
A semiconductor or microelectronic device comprising a titanium disilicide encroachment barrier having deposited thereon a tungsten layer wherein the interface between the tungsten and the titanium disilicide is substantially free of oxygen and fluorine contamination; said tungsten having been deposited on a C 49 TiSi 2 characterized by a resistivity of from about 80 to about 120 μohm-cm followed by an annealing step at an anneal temperature of from about 575° C. to about 700° C. sufficient to convert the C 49 TiSi 2 to C 54 TiSi 2 characterized by a resistivity in the range of from about 5 μohm-cm to about 50 μohm-cm.
Claim 9
Dependent Claim
63 words
An article comprising a substrate, a disilicide encroachment barrier on said substrate and a tungsten layer selectively deposited on the disilicide barrier wherein the interface between the tungsten and disilicide layer is substantially free of oxygen and/or fluorine contamination; said disilicide prior to the deposition of the tungsten layer having a silicon content in excess of stoichiometric amount required by the disilicide formula.
Claim 10
Dependent Claim
63 words
An article comprising a substrate, a disilicide encroachment barrier on said substrate and a tungsten layer selectively deposited on the disilicide barrier wherein the interface between the tungsten and disilicide layer is substantially free of oxygen and/or fluorine contamination; said disilicide prior to the deposition of the tungsten layer having a silicon content in excess of stoichiometric amount required by the disilicide formula.
Claim 11
Dependent Claim
34 words
The article of claim 7 wherein the disilicide is TiSi 2 having a silicon content from about 2.5 to 3.5 mole percent in excess of the stoichiometric amount required by the TiSi 2 formula.
Claim 12
Dependent Claim
173 words
An article comprising a metal or metal compound (M) selectively deposited on a titanium disilicide encroachment barrier according to the following process steps: 1) first forming a metastable titanium disilicide layer on a substrate wherein said disilicide is characterized as a metastable C49 titanium disilicide (TiSi 2 ); 2) selectively depositing a metal or metal compound on said C49 TiSi 2 to give a product having a M/C49 TiSi 2 interface which is substantially free of oxygen and/or fluorine contamination; and 3) annealing the product of step 2 at a temperature and time sufficient to convert the C49 TiSi 2 to C54 TiSi 2 ; wherein the C49 TiSi 2 layer of step 2 is characterized by a resistivity of from about 80 to about 120 μohm-cm and is converted by annealing to a C54 TiSi 2 characterized by a resistivity in the range of from about 5 μohm-cm to about 50 μohm-cm; wherein M is selected from the group consisting of: platinum, molybdenum, titanium, titanium nitride, tungsten, tantalum, copper, silver and aluminum.
Claim 13
Dependent Claim
173 words
An article comprising a metal or metal compound (M) selectively deposited on a titanium disilicide encroachment barrier according to the following process steps: 1) first forming a metastable titanium disilicide layer on a substrate wherein said disilicide is characterized as a metastable C49 titanium disilicide (TiSi 2 ); 2) selectively depositing a metal or metal compound on said C49 TiSi 2 to give a product having a M/C49 TiSi 2 interface which is substantially free of oxygen and/or fluorine contamination; and 3) annealing the product of step 2 at a temperature and time sufficient to convert the C49 TiSi 2 to C54 TiSi 2 ; wherein the C49 TiSi 2 layer of step 2 is characterized by a resistivity of from about 80 to about 120 μohm-cm and is converted by annealing to a C54 TiSi 2 characterized by a resistivity in the range of from about 5 μohm-cm to about 50 μohm-cm; wherein M is selected from the group consisting of: platinum, molybdenum, titanium, titanium nitride, tungsten, tantalum, copper, silver and aluminum.
Claim 14
Dependent Claim
150 words
An article comprising tungsten selectively deposited on a metal disilicide (MSi 2 ) encroachment barrier according to the following process steps: 1) first forming a metal disilicide MSi 2 layer on a substrate wherein said disilicide layer is characterized as having, at least on the surface thereof, an amount of silicon from about 2.5 to about 3.5 mole percent in excess of the calculated formula MSi 2 ; and 2) selectively depositing tungsten (W) on said MSi 2 layer to give a produce having a W-MSi 2 interface which is substantially free of oxygen and/or fluorine contamination; wherein said metal disilicide is selected from the group consisting of titanium disilicide, tungsten disilicide (WSi 2 ), molybdenum disilicide (MoSi 2 ), tantalum disilicide (TaSi 2 ), vanadium disilicide (VSi 2 ), platinum silicide (PlSi), nickel silicide (NiSi; Ni 2 Si), chromium disilicide (CrSi 2 ) and niobium disilicide (NiSi 2 ).
Claim 15
Dependent Claim
150 words
An article comprising tungsten selectively deposited on a metal disilicide (MSi 2 ) encroachment barrier according to the following process steps: 1) first forming a metal disilicide MSi 2 layer on a substrate wherein said disilicide layer is characterized as having, at least on the surface thereof, an amount of silicon from about 2.5 to about 3.5 mole percent in excess of the calculated formula MSi 2 ; and 2) selectively depositing tungsten (W) on said MSi 2 layer to give a produce having a W-MSi 2 interface which is substantially free of oxygen and/or fluorine contamination; wherein said metal disilicide is selected from the group consisting of titanium disilicide, tungsten disilicide (WSi 2 ), molybdenum disilicide (MoSi 2 ), tantalum disilicide (TaSi 2 ), vanadium disilicide (VSi 2 ), platinum silicide (PlSi), nickel silicide (NiSi; Ni 2 Si), chromium disilicide (CrSi 2 ) and niobium disilicide (NiSi 2 ).
Claim 16
Dependent Claim
14 words
The article of claim 10 wherein the metal disilicide is C54 TiSi 2 .
Claim 17
Dependent Claim
104 words
An article comprising a substrate, a disilicide encroachment barrier on said substrate and a tungsten layer selectively deposited on the disilicide barrier to form an interface therewith which is substantially free of oxygen and fluorine contamination; said disilicide on which the tungsten is selectively deposited being selected from the group consisting of titanium disilicide (TiSi 2 ), tungsten disilicide (WSi 2 ); molybdenum disilicide (MoSi 2 ); tantalum disilicide (TaSi 2 ); vanadium disilicide (VSi 2 ); chromium disilicide (CrSi 2 ) and niobium disilicide (NbSi 2 ) and having a silicon content in excess of the stoichiometric amount required by the disilicide formula.
Claim 18
Dependent Claim
104 words
An article comprising a substrate, a disilicide encroachment barrier on said substrate and a tungsten layer selectively deposited on the disilicide barrier to form an interface therewith which is substantially free of oxygen and fluorine contamination; said disilicide on which the tungsten is selectively deposited being selected from the group consisting of titanium disilicide (TiSi 2 ), tungsten disilicide (WSi 2 ); molybdenum disilicide (MoSi 2 ); tantalum disilicide (TaSi 2 ); vanadium disilicide (VSi 2 ); chromium disilicide (CrSi 2 ) and niobium disilicide (NbSi 2 ) and having a silicon content in excess of the stoichiometric amount required by the disilicide formula.
References Cited (Backward Citations)
US4940509A
Cited
US4957777A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-08-11 | 1996-02-10 | 1996-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-08-11 | 2000-02-10 | 2000-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-08-11 | 2004-02-10 | 2004-08-11 | $7700.00 | Window Closed / Lapsed |