US5131978A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Low temperature, single side, multiple step etching process for fabrication of small and large structures
Assignee: Xerox Corp
•
Filing: 1990-06-07
•
Granted: 1992-07-21
•
Expires: 2010-06-07
Abstract
Abstract A fabrication process for wafer derived elements such as channel plates for thermal ink jet printers includes formation of a final etchant pattern in first and second masking layers. The second masking layer is a protective layer to prevent removal of the first layer upon removal of a subsequent third masking layer. Preferably, the second masking layer is an oxide applied under low temperature condition to lessen the possibility of inducing formation of oxygen precipitates in the wafer. A third masking layer is formed over the final etchant pattern formed by the first and second masking layers. The third masking layer is patterned to form a precursor structure of a large structure contained in the final etchant pattern. After formation of the precursor structure, the third masking layer is removed and the wafer is subjected to a final etching exposure to form the final etched structures. The process is useful for forming channel plates for thermal ink jet printheads.
Inventors
- 👤 James F. O'Neill
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:05
CPC Classifications
B; B41; B41J; B41J2/00; B41J2/005; B41J2/01; B41J2/135; B41J2/16; B41J2/1621; B41J2/1626; B41J2/1629; B41J2/1601; B41J2/1604; B41J2/1628; B41J2/1632; B41J2/164; B41J2/1642; H; H10; H10P; H10P50/00; H10P50/69; H10P50/691; H10P50/693; H10P50/694
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
266 words
A method of making a silicon body having fine and large structures formed therein by etching, comprising: applying a first layer of masking material to a surface of the body; applying a second layer of a protective masking material different from the first layer of masking material, on the first masking layer; forming a first pattern on the protective masking layer, including the fine and large structures, for forming the desired finished structures on said body surface; removing the portions of the first and protective layers in the first pattern to expose portions of said body surface in said first pattern in a first mask forming step; applying a third layer of a masking material on the first and second layers of masking material and on portions of said body surface exposed in the first mask removal step; forming a second pattern on the third layer of masking material to form a second pattern formed within the boundaries of the first pattern; removing portions of the third layer of masking material in the second pattern to expose portions of said body surface in a second mask forming step; exposing said body surface to an etchant for said body surface through the second pattern to form a precursor structure on the body surface, in a first etching step; removing from said body surface any portions of the third layer of masking material which remained after the second mask forming step; exposing said body surface including said precursor structure, to an etchant for the body surface to form structures through the first pattern, in a second etching step.
Claim 2
Independent Claim
266 words
A method of making a silicon body having fine and large structures formed therein by etching, comprising: applying a first layer of masking material to a surface of the body; applying a second layer of a protective masking material different from the first layer of masking material, on the first masking layer; forming a first pattern on the protective masking layer, including the fine and large structures, for forming the desired finished structures on said body surface; removing the portions of the first and protective layers in the first pattern to expose portions of said body surface in said first pattern in a first mask forming step; applying a third layer of a masking material on the first and second layers of masking material and on portions of said body surface exposed in the first mask removal step; forming a second pattern on the third layer of masking material to form a second pattern formed within the boundaries of the first pattern; removing portions of the third layer of masking material in the second pattern to expose portions of said body surface in a second mask forming step; exposing said body surface to an etchant for said body surface through the second pattern to form a precursor structure on the body surface, in a first etching step; removing from said body surface any portions of the third layer of masking material which remained after the second mask forming step; exposing said body surface including said precursor structure, to an etchant for the body surface to form structures through the first pattern, in a second etching step.
Claim 3
Dependent Claim
21 words
A method as in claim 1, wherein the steps of exposing the body surface to an etchant comprise orientation dependent etching.
Claim 4
Dependent Claim
22 words
A method as in claim 1, wherein the steps of applying the first and third layers comprise vapor deposition of a nitride.
Claim 5
Dependent Claim
20 words
A method as in claim 3, wherein the step of applying the protective layer comprises depositing a low temperature oxide.
Claim 6
Dependent Claim
14 words
A method as in claim 4, wherein the low temperature oxide is silicon dioxide.
Claim 7
Dependent Claim
20 words
A method as in claim 5, wherein the steps of exposing the surface to an etchant comprise orientation dependent etching.
Claim 8
Dependent Claim
13 words
A method as in claim 6, wherein the body is a silicon wafer.
Claim 9
Dependent Claim
14 words
A method as in claim 7, wherein the silicon body is a <1-0-0> silicon.
Claim 10
Dependent Claim
23 words
A method as in claim 1, wherein the steps of exposing the surface to an etchant form a through hole in the body.
Claim 11
Dependent Claim
23 words
A method as in claim 1, wherein the protective layer of masking forming the first pattern, is removed before the second etching step.
Claim 12
Dependent Claim
38 words
A method as in claim 7, wherein the steps of applying the first, second and third layers of masking material take place at temperatures below those at which there is substantial redistribution of oxygen within the silicon body.
Claim 13
Dependent Claim
21 words
A method as in claim 11, wherein the first, second and third layers are applied at temperatures below about 1000° C.
Claim 14
Independent Claim
269 words
A method of forming a channel plate for an ink jet printer having a plurality of channels and a reservoir from a silicon wafer comprising: applying a firs layer of a masking material to a surface of the wafer; applying a protective second layer of masking material of a material different from the first layer on the first layer; forming a first pattern on the second masking layer, for forming the reservoir and said plurality of channels; removing a portion of the first layer and the second layer of masking material from the wafer surface to expose the wafer surface in said first pattern in a first mask removal step; applying a third masking layer of a material different from the protective masking layer on the first and second masking layers and the portion of said wafer surface exposed in said first mask removal step; forming a second pattern on the third masking layer overlying and spaced from edges of the reservoir in the first pattern; removing a portion of the third masking layer to expose said surface of the water in a second pattern; exposing the wafer to an etchant through the second pattern to form a portion of the reservoir in the wafer; removing from said wafer surface any portion of the third layer of masking material which remained after the second mask forming step to expose the portions of said surface in the first pattern for forming the reservoir and the channels; and exposing the wafer to an etchant through said first pattern to form said channels and portions of the reservoir in said first pattern.
Claim 15
Independent Claim
269 words
A method of forming a channel plate for an ink jet printer having a plurality of channels and a reservoir from a silicon wafer comprising: applying a firs layer of a masking material to a surface of the wafer; applying a protective second layer of masking material of a material different from the first layer on the first layer; forming a first pattern on the second masking layer, for forming the reservoir and said plurality of channels; removing a portion of the first layer and the second layer of masking material from the wafer surface to expose the wafer surface in said first pattern in a first mask removal step; applying a third masking layer of a material different from the protective masking layer on the first and second masking layers and the portion of said wafer surface exposed in said first mask removal step; forming a second pattern on the third masking layer overlying and spaced from edges of the reservoir in the first pattern; removing a portion of the third masking layer to expose said surface of the water in a second pattern; exposing the wafer to an etchant through the second pattern to form a portion of the reservoir in the wafer; removing from said wafer surface any portion of the third layer of masking material which remained after the second mask forming step to expose the portions of said surface in the first pattern for forming the reservoir and the channels; and exposing the wafer to an etchant through said first pattern to form said channels and portions of the reservoir in said first pattern.
Claim 16
Dependent Claim
20 words
A method as in claim 13, wherein the steps of exposing the wafer to an etchant comprise orientation dependent etching.
Claim 17
Dependent Claim
23 words
A method as in claim 13, wherein the step of applying the first and third masking layers comprises vapor deposition of a nitride.
Claim 18
Dependent Claim
22 words
A method as in claim 15, wherein the step of applying the second masking layer comprises deposition of a low temperature oxide.
Claim 19
Dependent Claim
12 words
A method as in claim 16, wherein the oxide is silicon dioxide.
Claim 20
Dependent Claim
20 words
A method as in claim 17, wherein the step of exposing the wafer to an etchant comprises orientation dependent etching.
Claim 21
Dependent Claim
22 words
A method as in claim 13, wherein the etchant exposure steps comprise forming the reservoir as a through hole in the wafer.
Claim 22
Dependent Claim
38 words
A method as in claim 13, wherein the steps of applying the first, second and third layers of masking material take place at temperatures below those at which there is substantial redistribution of oxygen within the silicon body.
Claim 23
Dependent Claim
21 words
A method as in claim 20 wherein the first, second and third layers are applied at temperatures below about 1000° C.
Claim 24
Dependent Claim
16 words
A method as in claim 13, wherein the etching step through the first pattern is isotropic.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-07-21 | 1996-01-20 | 1996-07-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-07-21 | 2000-01-20 | 2000-07-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-07-21 | 2004-01-20 | 2004-07-21 | $7700.00 | Window Closed / Lapsed |