Process for preparation of dental crown restoration and kit for use in carrying out said process
Assignee: Kyocera Corp
•
Filing: 1988-10-06
•
Granted: 1992-07-07
•
Expires: 2008-10-06
Abstract
Abstract Disclosed is a process for the preparation of a dental crown restoration, which comprises preparing a plurality of dental crown-restoring glass materials comprising 100 parts by weight of a glass component and 0.01 to 17.0 parts by weight of an incorporated coloring component and giving colored glass ceramics differing in the value or the combination of the value and chroma in the glass-crystallized state, selecting a shade guide having a color equal or closely akin to the color of a tooth adjacent to the tooth to be restored among a plurality of shade guides classified accord- to a plurality of values or combinations of the value and chroma as one index and a plurality of hues as another index, selecting a glass material giving a predetermined value or a predetermined combination of the value and chroma among said glass materials according to the color of the selected shade guide, preparing a dental crown restoration from the selected glass material, and applying a shading giving a predetermined hue or a predetermined combination of the hue, value and chroma according to the color of the selected shade guide to the surface of the dental crown restoration.
Inventors
- 👤 Koichi Yamaguchi
- 👤 Shingo Masuda
- 👤 Keiji Mishima
- 👤 Michinori Akase
- 👤 Takahiko Asano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 21:59
CPC Classifications
A; A61; A61C; A61C13/00; A61C13/0003; A61C5/00; A61C5/70; A61C5/77
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
182 words
A process for the preparation of a dental crown restoration, which comprises preparing a plurality of dental crown-restoring glass materials comprising 100 parts by weight of a glass component and 0.01 to 17.0 parts by weight of an incorporated coloring component and giving colored glass ceramics differing in the value or the combination of the value and chroma in the glass-crystallized state, selecting a shade guide having a color equal or closely akin to the color of a tooth adjacent to the tooth to be restored among a plurality of shade guides classified accord- to a plurality of values or combinations of the value and chroma as one index and a plurality of hues as another index, selecting a glass material giving a predetermined value or a predetermined combination of the value and chroma among said glass materials according to the color of the selected shade guide, preparing a dental crown restoration from the selected glass material, and applying a shading giving a predetermined hue or a predetermined combination of the selected shade guide to the surface of the dental crown restoration.
Claim 2
Dependent Claim
182 words
A process for the preparation of a dental crown restoration, which comprises preparing a plurality of dental crown-restoring glass materials comprising 100 parts by weight of a glass component and 0.01 to 17.0 parts by weight of an incorporated coloring component and giving colored glass ceramics differing in the value or the combination of the value and chroma in the glass-crystallized state, selecting a shade guide having a color equal or closely akin to the color of a tooth adjacent to the tooth to be restored among a plurality of shade guides classified accord- to a plurality of values or combinations of the value and chroma as one index and a plurality of hues as another index, selecting a glass material giving a predetermined value or a predetermined combination of the value and chroma among said glass materials according to the color of the selected shade guide, preparing a dental crown restoration from the selected glass material, and applying a shading giving a predetermined hue or a predetermined combination of the selected shade guide to the surface of the dental crown restoration.
Claim 3
Dependent Claim
16 words
A process according to claim 1, wherein the glass component is a calcium phosphate type glass.
Claim 4
Dependent Claim
21 words
A process according to claim 1, wherein the glass component has a composition of CaO-P 2 O 5 -MgO-SiO 2 .
Claim 5
Dependent Claim
21 words
A process according to claim 1, wherein the dental crown restoration consists of a colored crystallized glass composed mainly of apatite.
Claim 6
Dependent Claim
101 words
A process according to claim 1, wherein the transparency (Ts), defined by the following formula, of the colored crystallized glass is 20 to 70%: Ts=(Ys/Yo)×100 wherein Ys stands for Y value of the tristimulus values of the transmitted light in the standard colorimetric system CIE, measured at a visual field angle 2° by using standard illuminant C with respect to a disk-shaped colored crystallized glass having a thickness of 1.25 mm, and Yo stands for Y value determined with respect to the above-mentioned standard illuminant in the same manner as described above except that the colored crystallized glass is not placed.
Claim 7
Dependent Claim
37 words
A process according to claim 1, wherein of the colored crystallized glasses, one having a smallest value has a transparency of 30 to 70% and another having a largest value has a transparency of 20 to 60%.
Claim 8
Dependent Claim
49 words
A process according to claim 1, wherein the crystallized glass is composed of a composition comprising 40 to 80% by weight of a CaO-P 2 O 5 component having a Ca/P atomic ratio of 2.5 to 4.0 and 20 to 60% by weight of an SiO 2 -MgO component.
Claim 9
Dependent Claim
29 words
A process according to claim 4, wherein the coloring component is at least one member selected from the group consisting of rare earth metal oxides and transition metal oxides.
Claim 10
Dependent Claim
22 words
A process according to claim 8, wherein the rare earth metal is selected from the group consisting of Ce, Pr and Eu.
Claim 11
Dependent Claim
30 words
A process according to claim 8, wherein the transition metal is selected from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Zr, Nb, Mo, Ag and W.
Claim 12
Dependent Claim
94 words
A process according to claim 8, wherein the coloring component is composed of a composition comprising 10 to 70% by weight, based on the coloring component, of Ce 2 O 3 , 30 to 70% by weight, based on the coloring component, of Mn 3 O 4 , up to 40% by weight, based on the coloring component, of TIO 2 , up to 15% by weight, based on the coloring component, of Fe 3 O 4 and up to 10% by weight, based on the coloring component, of V 2 O 5 .
Claim 13
Dependent Claim
43 words
A process according to claim 1, wherein the preparation of the dental crown restoration is performed by casting a melt of the glass material in a mold having a cavity corresponding to the dental crown and heat-treating the cast product to effect crystallization.
Claim 14
Dependent Claim
29 words
A process according to claim 1, wherein the shading is formed by coating a shading composition on the surface of the dental crown restoration and calcining the coated restoration.
Claim 15
Dependent Claim
43 words
A process according to claim 13, wherein the shading composition is a composition comprising 60 to 95% by weight of a sodium silicate glass having a melting point of 500° to 1000° C. and 5 to 40% by weight of a coloring agent.
Claim 16
Dependent Claim
169 words
A kit for the restoration of dental crowns, which comprises shade guides classified by a plurality of values or a plurality of combinations of the value and chroma as one index and a plurality of hues as another index, a package comprising plurality of crown-restoring glass materials comprising 100 parts by weight of a glass component and 0.01 to 17 parts by weight of an incorporated coloring component and giving colored glass ceramics differing in the value or the combination of the value and chroma in the crystallized state, said glass materials being filled in vessels corresponding to the respective value indexes, and a package comprising a plurality of shading compositions comprising 60 to 95% by weight of a sodium silicate having a melting point of 500° to 1000° C. and 5 to 40% by weight of a coloring agent and differing in the hue or the combination of the hue, value and chroma, said shading compositions being filled in vessels corresponding to the respective hue or value-hue indexes.
Claim 17
Dependent Claim
169 words
A kit for the restoration of dental crowns, which comprises shade guides classified by a plurality of values or a plurality of combinations of the value and chroma as one index and a plurality of hues as another index, a package comprising plurality of crown-restoring glass materials comprising 100 parts by weight of a glass component and 0.01 to 17 parts by weight of an incorporated coloring component and giving colored glass ceramics differing in the value or the combination of the value and chroma in the crystallized state, said glass materials being filled in vessels corresponding to the respective value indexes, and a package comprising a plurality of shading compositions comprising 60 to 95% by weight of a sodium silicate having a melting point of 500° to 1000° C. and 5 to 40% by weight of a coloring agent and differing in the hue or the combination of the hue, value and chroma, said shading compositions being filled in vessels corresponding to the respective hue or value-hue indexes.
Claim 18
Dependent Claim
39 words
A kit as set forth in claim 15, wherein the dental crown-restoring glass material is filled in the form of tablets in the vessel and the shading composition is filled in the form of a powder in the vessel.
Claim 19
Dependent Claim
28 words
A kit as set forth in claim 15, wherein the vessel for filling the dental crown-restoring glass material also acts as a crucible for melting the glass material.
Claim 20
Dependent Claim
107 words
An artificial tooth consisting of a colored crystallized glass composed mainly of apatite, said colored glass comprising 100 parts by weight of a glass component and 0.01 to 17 parts by weight of a coloring component, said glass component comprising 40 to 80% by weight of a CaO-P 2 O 5 component having a Ca/P atomic ratio of 2.5 to 4.0 and 20 to 60% by weight of an SiO 2 -MgO component, and said coloring component being an oxide of at least one metal selected from the group consisting of Ce, Pr, Eu, Ti, V, Cr, Mn, Fe, Co, Ni, Zr, Nb, Mo, Ag and W.
Claim 21
Dependent Claim
107 words
An artificial tooth consisting of a colored crystallized glass composed mainly of apatite, said colored glass comprising 100 parts by weight of a glass component and 0.01 to 17 parts by weight of a coloring component, said glass component comprising 40 to 80% by weight of a CaO-P 2 O 5 component having a Ca/P atomic ratio of 2.5 to 4.0 and 20 to 60% by weight of an SiO 2 -MgO component, and said coloring component being an oxide of at least one metal selected from the group consisting of Ce, Pr, Eu, Ti, V, Cr, Mn, Fe, Co, Ni, Zr, Nb, Mo, Ag and W.
Claim 22
Dependent Claim
104 words
An artificial tooth as set forth in claim 18, wherein the transparency (Ts), defined by the following formula, of the colored crystallized glass is 20 to 70%: Ts=(Ys/Yo)×100 wherein Ys stands for Y value of the tristimulus values of the transmitted light in the standard colorimetric system CIE, measured at a visual field angle 2° by using standard illuminant C with respect to a disk-shaped colored crystallized glass having a thickness of 1.25 mm, and Yo stands for Y value determined with respect to the above-mentioned standard illuminant in the same manner as described above except that the colored crystallized glass is not placed.
Claim 23
Dependent Claim
24 words
An artificial tooth as set forth in claim 18, wherein a shading layer is formed on the outer surface of the artificial tooth substrate.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-07-07 | 1996-01-06 | 1996-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-07-07 | 2000-01-06 | 2000-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-07-07 | 2004-01-06 | 2004-07-07 | $7700.00 | Window Closed / Lapsed |