Silicon nitride powder, silicon nitride sintered body and processes for their production
Assignee: Denka Co Ltd
•
Filing: 1990-04-18
•
Granted: 1992-06-30
•
Expires: 2010-04-18
Abstract
Abstract A silicon nitride powder prepared by nitriding a metallic silicon powder and having the following physical characteristics (1) to (3): (1) the oxygen content in the form of a solid solution is at most 0.5% by weight, (2) the specific surface area is from 6 to 16 m 2 /g, and (3) the content of fine powder of at most 0.2 μm is at most 7% by volume.
Inventors
- 👤 Koichi Uchino
- 👤 Yukihiko Nakajima
- 👤 Myuki Nakamura
- 👤 Hideki Hirotsuru
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 10:31
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
118 words
A silicon nitride powder prepared by nitriding a metallic silicon powder in an atmosphere containing nitrogen and/or ammonia, while supplying at least one halide selected from the group consisting of alkali metal halides and alkaline earth metal halides, in a gas state, continuously, intermittently or at once, to obtain a silicon nitride ingot, followed by grinding of the ingot and having the following physical characteristics ( 1) to (3): (1) the internal oxygen content in the form of a solid solution is at most 0.5% by weight, (2) the specific surface area is from 6 to 16 m 2 /g, and (3) the content of fine powder of at most 0.2 μm is at most 7% by volume.
Claim 2
Dependent Claim
118 words
A silicon nitride powder prepared by nitriding a metallic silicon powder in an atmosphere containing nitrogen and/or ammonia, while supplying at least one halide selected from the group consisting of alkali metal halides and alkaline earth metal halides, in a gas state, continuously, intermittently or at once, to obtain a silicon nitride ingot, followed by grinding of the ingot and having the following physical characteristics ( 1) to (3): (1) the internal oxygen content in the form of a solid solution is at most 0.5% by weight, (2) the specific surface area is from 6 to 16 m 2 /g, and (3) the content of fine powder of at most 0.2 μm is at most 7% by volume.
Claim 3
Dependent Claim
25 words
The silicon nitride powder according to claim 1, wherein the content of fine powder of at most 0.2 μm is at most 3% by volume.
Claim 4
Dependent Claim
20 words
The silicon nitride powder according to claim 1, which has an average particle size of from 0.3 to 0.8 μm.
Claim 5
Dependent Claim
22 words
The silicon nitride powder according to claim 1, having a total content of Fe, Al and Ca of at most 1,000 ppm.
Claim 6
Dependent Claim
20 words
The silicon nitride powder according to claim 1, having an α-phase content of more than 70% and at most 80%.
Claim 7
Dependent Claim
24 words
The silicon nitride powder according to claim 1 having an α-phase content of at most 70% and a β-phase content of at least 30%.
Claim 8
Dependent Claim
22 words
The silicon nitride powder according to claim 4, wherein the total content of Fe, Al and Ca is at most 500 ppm.
Claim 9
Dependent Claim
27 words
The silicon powder according to claim 1, having a surface oxygen content in the form of a hydroxide or oxide of from 0.5 to 2.0% by weight.
Claim 10
Dependent Claim
17 words
A silicon nitride powder composition comprising a silicon nitride powder of claim 1 and a sintering aid.
Claim 11
Dependent Claim
67 words
The silicon nitride powder composition according to claim 9, wherein the sintering aid is at least one member selected from the group consisting of sintering aids of MgO type, MgO-Al 2 O 3 type, MgO-rare earth element oxide type, MgO-al 2 O 3 -rare earth element oxide type, MgO·Al 2 O 3 (spinel)-rare earth element oxide type and Al 2 O 3 -rare earth element oxide type.
Claim 12
Dependent Claim
36 words
The silicon nitride powder composition according to claim 9, wherein the rare earth element oxide is at least one member selected from the group consisting of oxides of Y, La, Ce, Pr, Nd, Sm and Eu.
Claim 13
Dependent Claim
31 words
The silicon nitride powder composition according to claim 10, which comprises at least 88% by weight of the silicon nitride powder and at most 12% by weight of the sintering aid.
Claim 14
Dependent Claim
75 words
A silicon nitride sintered body prepared by sintering the silicon nitride powder composition of claim 9, having β-prismatic crystals (A) having an aspect ratio of from 10 to 25 and a diameter of less than 0.5 micrometers as determined by the scanning electron microscope observation and β-prismatic crystals (B) having an aspect ratio of from 10 to 17 and a diameter of from 0.5 to 3.0 micrometers as determined by the scanning electron microscope observation.
Claim 15
Dependent Claim
43 words
A process for producing a silicon nitride sintered body, which comprises molding a silicon nitride powder composition of claim 9, followed by sintering in an inert gas atmosphere at a temperature of from 1,600° to 1,800° C. for from 2 to 6 hours.
Claim 16
Dependent Claim
25 words
The process for producing a silicon nitride sintered body according to claim 14, wherein the molding method is press molding, injection molding or slip casting.
Claim 17
Dependent Claim
63 words
A process for producing a silicon nitride powder which comprises nitriding a metallic silicon powder in an atmosphere containing nitrogen and/or ammonia while supplying at least one halide selected from the group consisting of alkali metal halides and alkaline earth metal halides, in a gas state, continuously, intermittently, or at once, to obtain a silicon nitride ingot, followed by grinding of the ingot.
Claim 18
Dependent Claim
63 words
A process for producing a silicon nitride powder which comprises nitriding a metallic silicon powder in an atmosphere containing nitrogen and/or ammonia while supplying at least one halide selected from the group consisting of alkali metal halides and alkaline earth metal halides, in a gas state, continuously, intermittently, or at once, to obtain a silicon nitride ingot, followed by grinding of the ingot.
Claim 19
Dependent Claim
28 words
The process for producing a silicon nitride powder according to claim 16, wherein the halide is supplied within a temperature range of from 1,150° C. to 1,450° C.
Claim 20
Dependent Claim
32 words
The process for producing a silicon nitride powder according to claim 16, wherein the halide is at least one member selected from the group consisting of fluorides of Ca, Mg and Li.
Claim 21
Dependent Claim
51 words
The process for producing a silicon nitride powder according to claim 16, wherein the silicon nitride powder obtained by grinding the silicon nitride ingot is further heat-treated at a temperature of from 600° to 1,200° C. in an atmosphere of from 0.05 to 0.8 atm of partial pressure of oxygen gas.
Claim 22
Dependent Claim
38 words
The silicon nitride sintered body according to claim 13, which has a flexural strength at room temperature of at least 900 MPa and a flexural strength at a high temperature of 1,200° C. of at least 700 MPa.
Claim 23
Dependent Claim
22 words
The silicon nitride sintered body according to claim 13, which has a toughness of at least 8.0 MPa·m 1/2 at room temperature.
References Cited (Backward Citations)
US4946630A
Cited
US4640903A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-30 | 1995-12-30 | 1996-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-30 | 1999-12-30 | 2000-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-30 | 2003-12-30 | 2004-06-30 | $7700.00 | Window Closed / Lapsed |