Zircon refractories with improved thermal shock resistance
Assignee: Saint Gobain Ceramics and Plastics Inc
•
Filing: 1990-10-31
•
Granted: 1992-06-23
•
Expires: 2010-10-31
Abstract
Abstract Dense zircon refractories having improved thermal shock damage resistance for use in glass melt or high alkali vapor contact applications comprise, and, consist essentially of, about fifty percent by weight or more ZrSiO 4 , at least about one percent zirconia in particle form distributed substantially uniformly throughout the composition of the refractory, and optionally, a zircon grain growth enhancing composition, preferably TiO 2 .
Inventors
- 👤 Thomas M. Wehrenberg
- 👤 Charles N. McGarry
- 👤 Sylvie Mahe
- 👤 Douglas A. Drake
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 21:36
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/48; C04B35/481; C03; C03B; C03B5/00; C03B5/16; C03B5/42; C03B5/43; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3231; C04B2235/3232; C04B2235/3244; C04B2235/3248; C04B2235/50; C04B2235/52; C04B2235/528; C04B2235/54; C04B2235/5409; C04B2235/5418; C04B2235/5427; C04B2235/5436; C04B2235/5463; C04B2235/5472; C04B2235/70; C04B2235/72; C04B2235/726; C04B2235/727; C04B2235/74; C04B2235/77; C04B2235/96; C04B2235/9669
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
108 words
A dense zircon refractory with high glass corrosion resistance having improved thermal shock resistance produced by a method comprising the steps of: forming into a shape a green composition of mixed sinterable components in particle form, the mixed sinterable components consisting essentially of about 75% to 95% by weight zircon and about 5% to 25% by weight zirconia with one or more zircon grain growth enhancing agents including TiO 2 , the sinterable components collectively including at least 0.10% by weight TiO 2 ; and firing the shape to a temperature throughout of between about 1400° C. and 1650° C. for a time sufficient to sinter the zircon.
Claim 2
Dependent Claim
108 words
A dense zircon refractory with high glass corrosion resistance having improved thermal shock resistance produced by a method comprising the steps of: forming into a shape a green composition of mixed sinterable components in particle form, the mixed sinterable components consisting essentially of about 75% to 95% by weight zircon and about 5% to 25% by weight zirconia with one or more zircon grain growth enhancing agents including TiO 2 , the sinterable components collectively including at least 0.10% by weight TiO 2 ; and firing the shape to a temperature throughout of between about 1400° C. and 1650° C. for a time sufficient to sinter the zircon.
Claim 3
Dependent Claim
47 words
The refractory produced by the method of claim 1 wherein the zircon grain growth enhancing composition comprises particles of titania added to the mixture in addition to the zircon and zirconia components in an amount between about 0.1% and 4% of the weight of the zircon component.
Claim 4
Dependent Claim
43 words
The refractory produced by the method of claim 1 wherein the zircon component includes aggregated zircon particles in an amount up to 15% by weight of the sinterable components, the aggregated zircon particles having a median particle size greater than 325 Tyler mesh.
Claim 5
Dependent Claim
24 words
The refractory produced by the method of claim 1 wherein the zircon constitutes between about 85% and 95% by weight of the sinterable components.
Claim 6
Dependent Claim
48 words
The refractory produced by the method of claim 1 wherein the sinterable components collectively consist of, by weight, about 72 to 94% ZrSiO 4 , about 5 to 25% ZrO 2 and HfO 2 , 0.10 to about 4% TiO 2 and about 5% or less other materials.
Claim 7
Dependent Claim
26 words
The refractory produeced by the method of claim 1 wherein the median particle size of the zirconia is more than 1 and less than 8 microns.
Claim 8
Dependent Claim
48 words
The refractory produced by the method of claim 6 wherein the sinterable components collectively consist of, by weight, about 72 to 94% ZrSiO 4 , about 5 to 25% ZrO 2 and HfO 2 , 0.10 to about 4% TiO 2 and about 5% or less other materials.
Claim 9
Dependent Claim
27 words
The refractory produced by the method of claim 7 wherein the median particle size of the zircon is greater than the median particle size of the zirconia.
Claim 10
Dependent Claim
24 words
The refractory produced by the method of claim 8 wherein the median particle size of the zirconia is between about 2 and 4 microns.
Claim 11
Dependent Claim
23 words
The refractory produced by the method of claim 9 wherein at least 5% by weight of the sinterable components is monoclinic form zirconia.
Claim 12
Dependent Claim
43 words
The refractory produced by the method of claim 10 wherein at least about 75% by weight of the sinterable components is zircon flour having a median particle size less than 10 microns and being about 97% or more by weight ZrSiO 4 .
Claim 13
Dependent Claim
57 words
The refractory produced by the method of claim 11 wherein the zircon component is a mixture of the zircon flour and aggregated zircon particles, the aggregated zircon particles being present in an amount up to 15% by weight of the sinterable components and the aggregated zircon particles having a median particle size greater than 325 Tyler mesh.
Claim 14
Dependent Claim
25 words
The refractory produced by the method of claim 12 wherein the sinterable components include up to about 2% by weight zircon grain growth enhancing agents.
Claim 15
Dependent Claim
47 words
The refractory produced by the method of claim 11 wherein the sinterable components collectively consist of, by weight, about 82 to 94% ZrSiO 4 , about 5 to 15% ZrO 2 HfO 2 , 0.10 to about 2% TiO 2 and about 1 to 3% other materials.
Claim 16
Dependent Claim
115 words
A dense zircon refractory with high glass corrosion resistance having improved thermal shock resistance produced by the method comprising the steps of: forming into a shape a green composition of mixed sinterable components in particle form, the mixed sinterable components consisting essentially of about 75% to 95% by weight zircon particles and about 5% to 25% by weight zirconia particles with one or more zircon grain growth enhancing agents including TiO 2 , the zircon particles having a median particle size greater than a median particle size of the zirconia particles; and firing the shape to a temperature throughout of between about 1400° C. and 1650° C. for a time sufficient to sinter the zircon.
Claim 17
Dependent Claim
115 words
A dense zircon refractory with high glass corrosion resistance having improved thermal shock resistance produced by the method comprising the steps of: forming into a shape a green composition of mixed sinterable components in particle form, the mixed sinterable components consisting essentially of about 75% to 95% by weight zircon particles and about 5% to 25% by weight zirconia particles with one or more zircon grain growth enhancing agents including TiO 2 , the zircon particles having a median particle size greater than a median particle size of the zirconia particles; and firing the shape to a temperature throughout of between about 1400° C. and 1650° C. for a time sufficient to sinter the zircon.
Claim 18
Dependent Claim
49 words
The refractory produced by the method of claim 15 wherein the sinterable components collectively consist of, by weight, about 72 to 94% ZrSiO 4 , about 5 to 25% ZrO 2 and HfO 2 , 0.10 to about 4% TiO 2 and about 5% or less of other materials.
Claim 19
Dependent Claim
26 words
The refractory produced by the method of claim 16 wherein the median particle size of the zirconia is more than 1 and less than 8 microns.
Claim 20
Dependent Claim
24 words
The refractory produced by the method of claim 17 wherein the median particle size of the zirconia is between about 2 and 4 microns.
Claim 21
Dependent Claim
23 words
The refractory produced by the method of claim 18 wherein at least 5% by weight of the sinterable components is monoclinic form zirconia.
Claim 22
Dependent Claim
43 words
The refractory produced by the method of claim 19 wherein at least about 75% by weight of the sinterable components is zircon flour having a median particle size less than 10 microns and being about 97% or more by weight ZrSiO 4 .
Claim 23
Dependent Claim
51 words
The refractory produced by the method of claim 20 wherein the zircon component further includes aggregated zircon particles, the aggregated zircon particles being present in an amount up to 15% by weight of the sinterable components and the aggregated zircon particles having a median particle size greater than +325 Tyler mesh.
Claim 24
Dependent Claim
48 words
The refractory produced by the method of claim 21 wherein the sinterable components collectively consist of, by weight, about 82 to 94% ZrSiO 4 , about 5 to 15% ZrO 2 and HfO 2 , 0.10 to about 2% TiO 2 and about 3% or less other materials.
Claim 25
Dependent Claim
73 words
A dense zircon refractory composition with high glass corrosion resistance having improved thermal shock resistance consisting essentially of: about 72 to 94% by weight ZrSiO 4 , at least 0.10% by weight TiO 2 , and about 5 to 25% by weight ZrO 2 and HfO 2 ; and the composition being substantially in the form of a matrix of aggregated zircon particles with individual zirconia particles substantially uniformly distributed through the matrix.
Claim 26
Dependent Claim
73 words
A dense zircon refractory composition with high glass corrosion resistance having improved thermal shock resistance consisting essentially of: about 72 to 94% by weight ZrSiO 4 , at least 0.10% by weight TiO 2 , and about 5 to 25% by weight ZrO 2 and HfO 2 ; and the composition being substantially in the form of a matrix of aggregated zircon particles with individual zirconia particles substantially uniformly distributed through the matrix.
Claim 27
Dependent Claim
20 words
The composition of claim 23 wherein the TiO 2 constitutes between about 0.5% and 2% by weight of the composition.
Claim 28
Dependent Claim
20 words
The composition of claim 24 wherein about 2% or more by weight of the composition is monoclinic form zirconia particles.
Claim 29
Dependent Claim
19 words
The composition of claim 24 wherein at least a portion of the zirconia particles are in metastable tetragonal form.
Claim 30
Dependent Claim
27 words
The composition of claim 23 including about 82 to 94% by weight ZrSiO 4 and about 5 to 15% by weight ZrO 2 and HfO 2 .
Claim 31
Dependent Claim
20 words
The composition of claim 23 wherein the median size of the zirconia particles is between about 1 and 8 microns.
Claim 32
Dependent Claim
19 words
The composition of claim 28 wherein the median size of the zirconia particles is about 4 microns or less.
Claim 33
Dependent Claim
34 words
The composition of claim 23 lacking carbides in amounts sufficient to react with molten glass and further lacking zirconia stabilizing agents in amounts sufficient to stabilize all of the zirconia particles in the composition.
Claim 34
Dependent Claim
44 words
The composition of claim 30 consisting of about 82 to 94% by weight ZrSiO 4 , about 5 to 15% by weight ZrO 2 and HfO 2 , 0.10 to about 2% by weight TiO 2 and about 3% or less other refractory components.
Claim 35
Dependent Claim
36 words
The composition of claim 31 in a monolithic block having a bulk density greater than 245 lbs/ft 3 and a weight greater than 245 lbs and being about 0.5 to 2% by weight TiO 2 .
Claim 36
Dependent Claim
36 words
The composition of claim 23 in a monolithic block having a bulk density greater than 245 lbs/ft 3 and a weight greater than 245 lbs. and being about 0.5 to 2% by weight TiO 2 .
Claim 37
Dependent Claim
76 words
A dense zircon refractory composition with a high glass corrosion resistance having improved thermal shock resistance consisting of, by oxide analysis: about 25 to 33% SiO 2 , about 66 to 72% ZrO 2 and HfO 2 , 0.10 to about 4% TiO 2 , and about 5% or less other materials; and the composition being substantially in the form of a matrix of aggregated zircon particles with zirconia particles distributed substantially uniformly through the matrix.
Claim 38
Dependent Claim
76 words
A dense zircon refractory composition with a high glass corrosion resistance having improved thermal shock resistance consisting of, by oxide analysis: about 25 to 33% SiO 2 , about 66 to 72% ZrO 2 and HfO 2 , 0.10 to about 4% TiO 2 , and about 5% or less other materials; and the composition being substantially in the form of a matrix of aggregated zircon particles with zirconia particles distributed substantially uniformly through the matrix.
Claim 39
Dependent Claim
37 words
The refractory composition of claim 34 in a monolithic block having a bulk density greater than 245 lbs/ft 3 and a weight greater than 245 lbs and being about 0.5 to 2% by weight TiO 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-23 | 1995-12-23 | 1996-06-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-23 | 1999-12-23 | 2000-06-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-23 | 2003-12-23 | 2004-06-23 | $7700.00 | Window Closed / Lapsed |