Process for producing fine powders by hot substrate microatomization
Assignee: Global Tungsten and Powders LLC
•
Filing: 1991-05-17
•
Granted: 1992-06-23
•
Expires: 2011-05-17
Abstract
Abstract A process for producing fine powder, which includes entraining a starting powder material in a carrier gas, injecting the starting powder material using the carrier gas into a high temperature jet to form a high velocity stream of molten droplets, fragmenting the resulting high velocity molten droplets by impacting against a substrate wherein the temperature of the substrate is above the melting point of the powder material, to form smaller droplets, and allowing the resulting fragmented smaller droplets to spheroidize and solidify in flight.
Inventors
- 👤 Muktesh Paliwal
- 👤 Robert J. Holland, Sr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:26
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/02; B22F9/06; B22F9/08; B22F9/082; B01; B01J; B01J2/00; B01J2/02; B01J2/04; B22F1/00; B22F1/06; B22F1/065
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
113 words
A process for producing fine powder, said process comprising: a) entraining a starting powder material in a carrier gas; b) injecting said starting powder material using said carrier gas into a high temperature direct current plasma jet to form a high velocity stream of molten droplets; c) fragmenting said high velocity stream of molten droplets by impacting said droplets against a substrate to form smaller droplets wherein the temperature of said substrate is above the melting point of said starting powder material, said temperature being maintained by heating said substrate, said substrate being formed from a tungsten based material; and d) allowing the resulting fragmented smaller droplets to spheroidize and solidify in flight.
Claim 2
Dependent Claim
113 words
A process for producing fine powder, said process comprising: a) entraining a starting powder material in a carrier gas; b) injecting said starting powder material using said carrier gas into a high temperature direct current plasma jet to form a high velocity stream of molten droplets; c) fragmenting said high velocity stream of molten droplets by impacting said droplets against a substrate to form smaller droplets wherein the temperature of said substrate is above the melting point of said starting powder material, said temperature being maintained by heating said substrate, said substrate being formed from a tungsten based material; and d) allowing the resulting fragmented smaller droplets to spheroidize and solidify in flight.
Claim 3
Dependent Claim
27 words
A process of claim 1 wherein said starting powder material is selected from the group consisting of metal powders, metal alloy powders, ceramic based powders, and glasses.
Claim 4
Dependent Claim
25 words
A process of claim 1 wherein said substrate is made of material selected from the group consisting of metals, metal alloys, ceramics and combinations thereof.
Claim 5
Dependent Claim
17 words
A process of claim 1 wherein said powder is copper and said substrate is a tungsten-based material.
Claim 6
Dependent Claim
115 words
A process for producing fine powder, said process comprising: a) entraining a starting powder material in a carrier gas; b) injecting said starting powder material using said carrier gas into a high temperature direct current plasma jet to form a high velocity stream of molten droplets; c) fragmenting said high velocity stream of molten droplets by impacting said droplets against a substrate to form smaller droplets wherein the temperature of said substrate is above the melting point of said starting powder material, said temperature being maintained by heating said substrate including direct heating from said high temperature direct current plasma jet; and d) allowing the resulting fragmented smaller droplets to spheroidize and solidify in flight.
Claim 7
Dependent Claim
115 words
A process for producing fine powder, said process comprising: a) entraining a starting powder material in a carrier gas; b) injecting said starting powder material using said carrier gas into a high temperature direct current plasma jet to form a high velocity stream of molten droplets; c) fragmenting said high velocity stream of molten droplets by impacting said droplets against a substrate to form smaller droplets wherein the temperature of said substrate is above the melting point of said starting powder material, said temperature being maintained by heating said substrate including direct heating from said high temperature direct current plasma jet; and d) allowing the resulting fragmented smaller droplets to spheroidize and solidify in flight.
Claim 8
Dependent Claim
22 words
The process of claim 5 wherein the particle size of said starting powder material is less than about 100 micrometers in diameter.
Claim 9
Dependent Claim
25 words
The process of claim 5 wherein the particle size of the fine powder produced by the process is less than about 20 micrometers in diameter.
References Cited (Backward Citations)
US2699576A
Cited
US2728107A
Cited
US4435342A
Cited
US4592781A
Cited
US4781741A
Cited
US4952144A
Cited
US5076991A
Cited
US4816067A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-23 | 1995-12-23 | 1996-06-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-23 | 1999-12-23 | 2000-06-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-23 | 2003-12-23 | 2004-06-23 | $7700.00 | Window Closed / Lapsed |