Components made from continuous fiber reinforced polyamide molding compositions and rubber, and a process for their preparation
Assignee: Huels AG
•
Filing: 1990-08-28
•
Granted: 1992-06-16
•
Expires: 2010-08-28
Abstract
Abstract Components made from at least two molded materials A and B which are firmly bonded together, and in which a) the molded material A is composed of a matrix of polyamide or of a polyamide-containing molding composition and of a continuous, fibrous reinforcement embedded therein, and b) the molded material B is the rubber obtained after peroxidic vulcanization of a rubber composition which is applied to A, the rubber composition containing the following components: i) about 100 parts by weight of a rubber having carboxyl or anhydride functional groups; ii) about 10 to 300 parts by weight of fillers; and iii) about 1 to 10 parts by weight of peroxidic vulcanizing agents.
Inventors
- 👤 Christian Baron
- 👤 Thomas Grosse-Puppendahl
- 👤 Hans Jadamus
- 👤 Klaus-Peter Richter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 09:19
CPC Classifications
B; B32; B32B; B32B25/00; B32B25/04; B32B25/08; B32B27/00; B32B27/34; C; C08; C08J; C08J5/00; C08J5/12; C08L; C08L23/00; C08L23/26; B32B2305/00; B32B2305/07; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31725; Y10T428/31826; Y10T428/31855; Y10T428/31931; Y10T428/31935
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
113 words
Components made from at least two molded materials A and B which are firmly bonded together, and in which a) the molded material A is composed of a matrix of polyamide or of a polyamide-containing molding composition and of a continuous, non-metallic fibrous reinforcement embedded therein, and b) the molded material B is the rubber obtained after peroxidic vulcanization of a rubber composition which is applied to A, the rubber composition containing the following components: i) about 100 parts by weight of a rubber having carboxyl or anhydride functional groups; ii) about 10 to 300 parts by weight of fillers; and iii) about 1 to 10 parts by weight of peroxidic vulcanizing agents.
Claim 2
Dependent Claim
113 words
Components made from at least two molded materials A and B which are firmly bonded together, and in which a) the molded material A is composed of a matrix of polyamide or of a polyamide-containing molding composition and of a continuous, non-metallic fibrous reinforcement embedded therein, and b) the molded material B is the rubber obtained after peroxidic vulcanization of a rubber composition which is applied to A, the rubber composition containing the following components: i) about 100 parts by weight of a rubber having carboxyl or anhydride functional groups; ii) about 10 to 300 parts by weight of fillers; and iii) about 1 to 10 parts by weight of peroxidic vulcanizing agents.
Claim 3
Dependent Claim
36 words
The components according to claim 1, wherein the polyamide used is PA 46, PA 6, PA 66, PA 610, PA 612, PA 1010, PA 1012, PA 11, PA 12 or PA 1212 or a mixture thereof.
Claim 4
Dependent Claim
23 words
The components according to claim 1, wherein the polyamides contain COOH and NH 2 terminal groups in a ratio of 1:x where 100>x>1.
Claim 5
Dependent Claim
31 words
The components according to claim 1, wherein the polyamide-containing molding composition contains up to 70% by weight of a polyphenylene ether, relative to the total amount of polyphenylene ether and polyamide.
Claim 6
Dependent Claim
43 words
The components according to claim 1, wherein the reinforcements are composed of glass fibers, aramid fibers or carbon fibers or a mixture thereof which are present in the form of yarns, fabrics, mats, webs, UD tapes, laid fabrics, rovings or as individual fibers.
Claim 7
Dependent Claim
19 words
The components according to claim 1, wherein the rubber composition contains a carboxyl- or anhydride-containing EP(D)M or NBR rubber.
Claim 8
Dependent Claim
30 words
The components according to claim 1, wherein the fillers used int he rubber composition are carbon black, silica, silicates, calcium carbonate, zinc oxide or stearic acid or a mixture thereof.
Claim 9
Dependent Claim
26 words
The components according to claim 1, wherein said rubber composition of molded material B further contains from 0 to 4 parts by weight of vulcanization activators.
Claim 10
Dependent Claim
25 words
The components according to claim 1, wherein said rubber composition of molded material B further contains from 0 to 150 parts by weight of plasticizer.
Claim 11
Dependent Claim
28 words
The components according to claim 9, wherein the plasticizer used is up to 50 parts by weight of naphthenic oils, relative to 100 parts by weight of rubber.
Claim 12
Dependent Claim
48 words
A process for the preparation of the components according to claim 1, which comprises completely enclosing said fibrous reinforcements with polyamide or with a polyamide-containing molding composition, applying the rubber composition to the molded material A which has been prepared in this manner and vulcanizing the rubber composition.
Claim 13
Dependent Claim
25 words
The process according to claim 11, wherein the vulcanization is carried out at temperatures of between 140° and 200° C. for 3 to 30 minutes.
Claim 14
Dependent Claim
25 words
The process according to claim 12 wherein the vulcanization is carried out at temperatures of between 150° and 180° C. for 5 to 15 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-16 | 1995-12-16 | 1996-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-16 | 1999-12-16 | 2000-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-16 | 2003-12-16 | 2004-06-16 | $7700.00 | Window Closed / Lapsed |