Abstract A method of producing a chilled iron camshaft is described, wherein the iron has a white iron structure adjacent chill inserts in a casting mould and a grey iron structure in substantially all other regions remote from the chills. The method comprises the steps of assembling a sand casting mould having a camshaft shaped cavity and also having chill inserts adjacent the cavity regions where while iron is desired, preparing a molten metal charge of cast iron having a carbon equivalent lying in the range from 3.3 to 3.85 wt % and adding sufficient nucleant prior to pouring to fill the mould cavity to ensure that undercooling of residual liquid remaining after solidification of the white iron structure adjacent the chills remains above the iron-cementite eutectic temperature prior to solidfication into grey iron.
A method of producing a chilled iron camshaft, the iron having a white iron structure adjacent chill inserts in a casting mould and a grey iron structure in substantially all other regions remote from the chills, the method comprising the steps of assembling a sand casting mould having a camshaft shaped cavity and also having chill inserts adjacent the cavity regions where white iron is desired, preparing a molten metal charge of cast iron having a carbon equivalent lying in the range from 3.3 to 3.85 wt% and adding nucleant prior to pouring, and pouring the molten metal to fill the mould cavity to form the camshaft, wherein said range of carbon equivalent and said nucleant addition are sufficient to ensure that undercooling of residual liquid remaining after solidification of the white iron structure adjacent the chills remains above the iron-cementite eutectic temperature prior to solidification into grey iron.
Claim 2
Independent Claim
149 words
A method of producing a chilled iron camshaft, the iron having a white iron structure adjacent chill inserts in a casting mould and a grey iron structure in substantially all other regions remote from the chills, the method comprising the steps of assembling a sand casting mould having a camshaft shaped cavity and also having chill inserts adjacent the cavity regions where white iron is desired, preparing a molten metal charge of cast iron having a carbon equivalent lying in the range from 3.3 to 3.85 wt% and adding nucleant prior to pouring, and pouring the molten metal to fill the mould cavity to form the camshaft, wherein said range of carbon equivalent and said nucleant addition are sufficient to ensure that undercooling of residual liquid remaining after solidification of the white iron structure adjacent the chills remains above the iron-cementite eutectic temperature prior to solidification into grey iron.
Claim 3
Dependent Claim
18 words
A method according to claim 1 wherein the carbon equivalent includes from 2.9 to 3.4 wt% of carbon.
Claim 4
Dependent Claim
14 words
A method according to claim 2 wherein the carbon equivalent remainder is substantially silicon.