Process for separating polyethylene terephthalate from polyvinyl chloride
Assignee: Corpus Christi Polymers LLC
•
Filing: 1991-05-09
•
Granted: 1992-06-09
•
Expires: 2011-05-09
Abstract
Abstract Today there is a growing demand to recycle plastics including polyethylene terephthalate. Sources of polyethylene terephthalate for recycling often contain polyvinyl chloride. It is necessary to separate polyvinyl chloride from the polyethylene terephthalate before it can be recycled into useful products. This invention reveals a process for recovering polyethylene terephthalate flakes from a recycle stream containing polyethylene terephthalate flakes and polyvinyl chloride flakes which comprises: (1) treating the recycle stream with (a) at least one inorganic base selected from the group consisting of sodium hydroxide and potassium hydroxide and (b) at least one nonionic surfactant under conditions and for a time sufficient to decrease the contact angle of the polyethylene terephthalate flakes with water below a value of 25 DEG while maintaining the contact angle of the polyvinyl chloride flakes above a value of about 45 DEG ; (2) adding the treated recycle stream to water, to form an aqueous mixture containing the treated polyethylene terephthalate flakes and treated polyvinyl chloride flakes; (3) agitating the aqueous mixture to allow the polyvinyl chloride flakes to come in contact with gas bubbles; (4) allowing the polyvinyl chloride flakes to float to the surface of the aqueous mixture and allowing the polyethylene terephthalate flakes to sink to the bottom of the aqueous mixture; and (5) removing the polyvinyl chloride flakes from the surface of the aqueous mixture and removing the polyethylene terephthalate flakes from the bottom of the aqueous mixture.
Inventors
- 👤 Edwin A. Sisson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 14:58
CPC Classifications
C; C08; C08J; C08J11/00; C08J11/04; C08J11/06; B; B03; B03B; B03B1/00; B03B1/04; B03B9/00; B03B9/06; B03B9/061; B03D; B03D1/00; B03D1/02; B29; B29B; B29B17/00; B29B17/02; B29B2017/0203; B29B2017/0213; B29B2017/0217; B29B2017/0248; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2027/00; B29K2027/06; B29K2067/00; B29L; B29L2031/00; B29L2031/712; B29L2031/7158; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
188 words
A process for recovering polyethylene terephthalate flakes from a recycle stream containing polyethylene terephthalate flakes and polyvinyl chloride flakes which comprises: (1) treating the recycle stream with (a) at least one inorganic base selected from the group consisting of sodium hydroxide and potassium hydroxide and (b) at least one nonionic surfactant under conditions and for a time sufficient to decrease the contact angle of the polyethylene terephthalate flakes below a value of 25° while maintaining the contact angle of the polyvinyl chloride flakes above a value of about 45°; (2) adding the treated recycle stream to water, to form an aqueous mixture containing the treated polyethylene terephthalate flakes and treated polyvinyl chloride flakes; (3) agitating the aqueous mixture to allow the polyvinyl chloride flakes to come in contact with gas bubbles; (4) allowing the polyvinyl chloride flakes to float to the surface of the aqueous mixture and allowing the polyethylene terephthalate flakes to sink to the bottom of the aqueous mixture; and (5) removing the polyvinyl chloride flakes from the surface of the aqueous mixture and removing the polyethylene terephthalate flakes from the bottom of the aqueous mixture.
Claim 2
Dependent Claim
188 words
A process for recovering polyethylene terephthalate flakes from a recycle stream containing polyethylene terephthalate flakes and polyvinyl chloride flakes which comprises: (1) treating the recycle stream with (a) at least one inorganic base selected from the group consisting of sodium hydroxide and potassium hydroxide and (b) at least one nonionic surfactant under conditions and for a time sufficient to decrease the contact angle of the polyethylene terephthalate flakes below a value of 25° while maintaining the contact angle of the polyvinyl chloride flakes above a value of about 45°; (2) adding the treated recycle stream to water, to form an aqueous mixture containing the treated polyethylene terephthalate flakes and treated polyvinyl chloride flakes; (3) agitating the aqueous mixture to allow the polyvinyl chloride flakes to come in contact with gas bubbles; (4) allowing the polyvinyl chloride flakes to float to the surface of the aqueous mixture and allowing the polyethylene terephthalate flakes to sink to the bottom of the aqueous mixture; and (5) removing the polyvinyl chloride flakes from the surface of the aqueous mixture and removing the polyethylene terephthalate flakes from the bottom of the aqueous mixture.
Claim 3
Dependent Claim
15 words
A process as specified in claim 1 wherein the nonionic surfactant is a fatty alcohol.
Claim 4
Dependent Claim
18 words
A process as specified in claim 2 wherein the fatty alcohol contains from 10 to 18 carbon atoms.
Claim 5
Dependent Claim
18 words
A process as specified in claim 2 wherein the fatty alcohol contains from 12 to 14 carbon atoms.
Claim 6
Dependent Claim
26 words
A process as specified in claim 1 wherein the nonionic surfactant has a HLB number which is within the range of about 8 to about 16.
Claim 7
Dependent Claim
26 words
A process as specified in claim 1 wherein the nonionic surfactant has a HLB number which is within the range of about 10 to about 14.
Claim 8
Dependent Claim
45 words
A process as specified in claim 1 wherein the nonionic surfactant has a structural formula: ##STR3## wherein n is an integer which is within the range of 1 to 40 and wherein m is an integer which is within the range of 6 to 12.
Claim 9
Dependent Claim
28 words
A process as specified in claim 7 wherein n is an integer which is within the range of 6 to 10 and wherein m is 8 or 9.
Claim 10
Dependent Claim
34 words
A process as specified in claim 1 wherein the recycle stream is treated in step (1) with an aqueous solution which contains from about 2 to about 15 weight percent of the inorganic base.
Claim 11
Dependent Claim
22 words
A process as specified in claim 9 wherein from about 5 to about 10 weight percent of the inorganic base is present.
Claim 12
Dependent Claim
24 words
A process as specified in claim 9 wherein the aqueous solution contains from about 0.005 to about 0.1 weight percent of the nonionic surfactant.
Claim 13
Dependent Claim
24 words
A process as specified in claim 9 wherein the aqueous solution contains from about 0.01 to about 0.05 weight percent of the nonionic surfactant.
Claim 14
Dependent Claim
12 words
A process as specified in claim 1 wherein the gas is air.
Claim 15
Dependent Claim
42 words
A process as specified in claim 1 wherein the contact angle of the PET flakes is reduced to a value of below about 15° and wherein the contact angle of the PVC flakes is increased to a value of above about 50°.
Claim 16
Dependent Claim
42 words
A process as specified in claim 1 wherein the contact angle of the PET flakes is reduced to a value of below about 5° and wherein the contact angle of the PVC flakes is increased to a value of above about 55°.
Claim 17
Dependent Claim
14 words
A process as specified in claim 1 wherein the inorganic base is sodium hydroxide.
Claim 18
Dependent Claim
14 words
A process as specified in claim 1 wherein the inorganic base is potassium hydroxide.
Claim 19
Dependent Claim
24 words
A process as specified in claim 1 wherein the nonionic surfactant is a polyol which is a copolymer of ethylene oxide and propylene oxide.
Claim 20
Dependent Claim
38 words
A process as specified in claim 1 wherein the gas bubbles are selected from the group consisting of air bubbles, nitrogen bubbles, oxygen bubbles, carbon dioxide bubbles, helium bubbles, hydrogen bubbles, argon bubbles, krypton bubbles, and neon bubbles.
References Cited (Backward Citations)
US3703488A
Cited
US3925200A
Cited
US3926791A
Cited
US4046677A
Cited
GB1444831A
Cited
US4132633A
Cited
US3985650A
Cited
US4119533A
Cited
US4386182A
Cited
US4617111A
Cited
US4968741A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-09 | 1995-12-09 | 1996-06-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-09 | 1999-12-09 | 2000-06-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-09 | 2003-12-09 | 2004-06-09 | $7700.00 | Window Closed / Lapsed |