Catalyst for purifying exhaust gases from internal combustion engines and gas turbines operated at above the stoichiometric ratio

Claim 2

A catalyst for purifying exhaust gases comprising a full solid, one-piece exhaust-gas purifying reduction catalyst in honeycomb form for selective reduction of nitrogen oxides contained in said exhaust gases by ammonia gas or by an ammonia producing compound said honeycomb having a trailing-edge portion which is coated with an oxidation catalyst capable of oxidizing components in said exhaust gases, and said coated portion amounts to 20-50% of the total volume of said catalyst.

Claim 3

The catalyst according to claim 1, wherein the full solid reduction catalyst comprises an intimate mixture of the following components: (A) titanium in the form of oxides, (B) at least one metal from the following group; B.1 iron and vanadium in the form of oxides and/or sulfates and/or the group B.2 molybdenum, tungsten, niobium, copper or chromium in the form of oxides, and/or (C) tin in the form of oxides, and/or (D) metals from the group beryllium, magnesium, zinc, boron, aluminum, yttrium, rare earth elements, silicon, antimony, bismuth and manganese in the form of oxides, the components being present in the atomic ratios; A : B : C : D=1 : 0.01 to 10 : 0 to 0.2 : 0 to 0.15.

Claim 4

The catalyst according to claim 1 wherein the full solid reduction catalyst comprises an intimate mixture of titanium dioxide as a component A), tungsten oxide as a component B 1 and at least one oxide of vanadium, iron, niobium, copper, chromium or molybdenum as a component B 2 , the atomic ratio of the metals in components A) and B) being from 1 : 001 to 1, the component A) being a finely divided oxide obtainable by flame hydrolysis of TiCl 4 and having a mainly anatase X-ray structure, a BET surface area of 50±15 m 2 /g, a density of 3.8 g/cm 3 , an average primary particle size of 30 nm, a pH of 3-4 measured in 4% aqueous dispersion and an isoelectric point at pH 6.6, the substance having a TiO 2 content of 99.5 wt.%, an Al 2 O 3 content of 0.3 wt.%, an SiO 2 content of 0.2 wt.%, an Fe 2 O 3 content of 0.01 wt.% and an HCl content of 0.3 wt.% after calcining at 1000° C. for 2 hours, and having a weight loss of 1.5 wt.% after drying at 105° C. for 2 hours and of 2 wt.% after calcining at 1000° C. for 2 hours.

Claim 5

The catalyst according to claim 1, characterized in that the reduction catalyst contains the following components; A) titanium oxide B 1 ) at least one oxide of tungsten, silicon, boron, aluminum, phosphorus, zirconium, barium, yttrium, lanthanum or cerium and B 2 ) at least one oxide of vanadium, niobium, molybdenum, iron, copper or chromium, the atomic ratio of the elements in components A) and B) being from 1 : 0.001 to 1, and the component A) being present in the form of a reactive high surface-area titanium oxide having a BET surface area of 40-500 m 2 /g and completely or mainly in the anatase modification.

Claim 6

The catalyst according to claim 4, wherein the atomic ratio of the elements in components A) and B) are 1 : 0.002 to 0.4.

Claim 7

The catalyst according to claim 4, wherein the BET surface area is 50-300 m 2 /g.

Claim 8

The catalyst according to claim 4, wherein the BET surface area is 60-150 m 2 /g.

Claim 9

The catalyst according to claim 1, wherein the full solid reduction catalyst is an acid-resistant mordenite catalyst, containing copper and/or iron and, optionally, cerium or molybdenum.

Claim 10

The catalyst according to claim 1, wherein said coated portion amounts to 25 to 35% of the total volume of the catalyst.

Claim 11

The catalyst according to claim 9, wherein the extrudate has the composition of an intimate mixture of the following components: (A) titanium in the form of oxides, (B) at least one metal from the following group; B.1 iron and vanadium in the form of oxides and/or sulfates and/or the group B.2 molybdenum, tungsten, niobium, copper or chromium in the form of oxides, and/or (C) tin in the form of oxides, and/or (D) metals from the group beryllium, magnesium, zinc, boron, aluminum, yttrium, rare earth elements, silicon, antimony, bismuth and manganese in the form of oxides, the components being present in the atomic ratios; A : B : C : D=1 : 0.01 to 10 : 0 to 0.2 : 0 to 0.15.

Claim 12

The catalyst according to claim 1, wherein said oxidation catalyst comprises 2 to 70 wt.% CeO 2 and 0 to 20 wt % ZrO 2 and, optionally, iron oxide, alkaline earth metal oxides and/or aluminum oxide of the transition series containing rare earth-metal oxides as the carrier and an active phase applied to the carrier and comprising 0.01 to 3 wt.% of platinum, palladium and/or rhodium, the ratio by weight of platinum, palladium and/or palladium to rhodium, if present, being from 2 : 1 to 30 : 1.

Claim 13

The catalyst according to claim 1, wherein the honeycomb carrier is coated in the amount of 20 to 50% of its volume with oxidation catalyst.