Bonding base and method of making same for a ceramic orthodontic bracket
Assignee: American Orthodontics Corp
•
Filing: 1991-09-30
•
Granted: 1992-04-28
•
Expires: 2011-09-30
Abstract
Abstract A bonding base and method of making a base for a ceramic orthodontic bracket to provide mechanical retention between the bracket and the tooth so that the bracket may be debonded by the failure of the mechanical bond at the bracket/bond interface when the shear strength of the bond is exceeded. The bracket bonding base includes a glass frit fired to the tooth-attaching side of the bracket and a layer of textured aluminum oxide fired to the frit. The method of making the bonding base includes controlled preparation of a glass ceramic glaze (frit) to have a coefficient of thermal expansion slightly less than that of the bracket and application of the glaze to the bracket base. Thereafter, a proper firing sequence transforms the glaze into a sintered glass ceramic. A specially prepared textured substance is then applied to the sintered ceramic glaze and the bracket is again fired under controlled conditions in order to fuse the textured substance with the glaze.
Inventors
- 👤 Lee H. Tuneberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 20:56
CPC Classifications
A; A61; A61C; A61C7/00; A61C7/12; A61C7/14; A61C7/16
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
117 words
A method of making a mechanical lock means for the tooth-attaching side of a ceramic orthodontic bracket so the bracket may be mechanically bonded to a tooth with a bonding adhesive, which method comprises the step of preparing a glass frit having a coefficient of thermal expansion slightly lower than that of the bracket, applying the frit to the tooth-attaching side of the bracket, firing the bracket and frit to fuse it to the bracket, applying a water-soluble contact adhesive to the fired frit, preparing a textured substance in the form of aluminum oxide, applying the substance to the adhesive, firing the bracket to allow the substance to settle in the molten glaze, and cooling the bracket.
Claim 2
Independent Claim
117 words
A method of making a mechanical lock means for the tooth-attaching side of a ceramic orthodontic bracket so the bracket may be mechanically bonded to a tooth with a bonding adhesive, which method comprises the step of preparing a glass frit having a coefficient of thermal expansion slightly lower than that of the bracket, applying the frit to the tooth-attaching side of the bracket, firing the bracket and frit to fuse it to the bracket, applying a water-soluble contact adhesive to the fired frit, preparing a textured substance in the form of aluminum oxide, applying the substance to the adhesive, firing the bracket to allow the substance to settle in the molten glaze, and cooling the bracket.
Claim 3
Dependent Claim
25 words
The method of claim 1, wherein the frit is composed of a dry glass-ceramic blend mixed into a liquid comprised of various binders and solvents.
Claim 4
Dependent Claim
18 words
The method of claim 2, wherein the various binders and solvents include carbowax, methylcellulose, methanol and de-ionized water.
Claim 5
Dependent Claim
45 words
The method of claim 3, wherein the dry glass-ceramic blend includes by weight 60 to 70 percent SiO 2 , 5 to 13 percent Al 2 O 2 , 8 to 13 percent Ca, 10 to 17 percent Na, and 1 to 5 percent K.
Claim 6
Dependent Claim
35 words
The method of claim 3, wherein the dry glass-ceramic blend includes by weight 65 percent SiO 2 , 9 percent Al 2 O 2 , 10 percent Ca, 14 percent Na, and 2 percent K.
Claim 7
Dependent Claim
17 words
The method of claim 3, wherein the frit thickness is about 0.002 to 0.004 inches before firing.
Claim 8
Dependent Claim
15 words
The method of claim 6, wherein the frit is applied to the bracket by spraying.
Claim 9
Dependent Claim
17 words
The method of claim 7, wherein the bracket is preheated prior to the application of the frit.
Claim 10
Dependent Claim
80 words
The method of claim 8, wherein the firing of the bracket and frit includes heating the bracket and frit to about 225° C. and holding that temperature for about twenty minutes, heating the bracket and frit to 1020° C. by raising the temperature about 7° per minute, holding the temperature at 1020° C. for about sixty minutes, and thereafter cooling the bracket and frit to 20° C. at the rate of 5° C. per minute thereby providing a sintered glaze.
Claim 11
Dependent Claim
33 words
The method of claim 9, wherein the textured substance comprises sharp multi-edged shards of high purity aluminum oxide having a mesh size of 220 and a minimum density of 3.9 grams per cc.
Claim 12
Dependent Claim
73 words
The method of claim 10, wherein the bracket is refired by heating to about 500° C. at the rate of 5° C. per minute, holding the temperature at 500° C. for about 15 minutes, increasing the temperature to about 1040° C. at the rate of 7° C. per minute, holding the temperature at 1040° C. for 240 minutes, and cooling the bracket to 20° C. at the rate of 5° C. per minute.
Claim 13
Dependent Claim
28 words
The method of claim 9, wherein the textured substance comprises a mixture of shards of alpha-alumina and randomly dispersed micro-glass spheres having a mesh size of about 220.
Claim 14
Dependent Claim
16 words
The method of claim 12, wherein the spheres are 25 percent by volume of the mixture.
Claim 15
Dependent Claim
73 words
The method of claim 12 wherein the bracket is refired by heating to about 500° C. at the rate of 5° C. per minute, holding the temperature at 500° C. for about 15 minutes, increasing the temperature to about 1040° C. at the rate of 7° C. per minute, holding the temperature at 1040° C. for 240 minutes, and cooling the bracket to 20° C. at the rate of 5° C. per minute.
Claim 16
Dependent Claim
17 words
A mechanical lock means for a ceramic orthodontic bracket made according to the method of claim 1.
Claim 17
Dependent Claim
74 words
A polycrystalline ceramic bracket having a mechanical lock on the tooth-attaching side, which mechanical lock comprises a layer of glass ceramic glaze fired to the tooth-attaching side, and a layer of high purity alumina shards fired to the glaze to produce a multiplicity of undercuts and projections capable of coacting with a mechanical bonding material to bond the bracket to a tooth, whereby debonding results from exceeding the bonding strength of the bonding material.
Claim 18
Dependent Claim
74 words
A polycrystalline ceramic bracket having a mechanical lock on the tooth-attaching side, which mechanical lock comprises a layer of glass ceramic glaze fired to the tooth-attaching side, and a layer of high purity alumina shards fired to the glaze to produce a multiplicity of undercuts and projections capable of coacting with a mechanical bonding material to bond the bracket to a tooth, whereby debonding results from exceeding the bonding strength of the bonding material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-04-28 | 1995-10-28 | 1996-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-04-28 | 1999-10-28 | 2000-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-04-28 | 2003-10-28 | 2004-04-28 | $7700.00 | Window Closed / Lapsed |