Flowable, pressure-compensating material and process for producing same

Claim 2

A flowable, pressure-compensating composition comprising: (a) water, (b) a material for increasing the viscosity of water, said material having an affinity for the water, and (c) substantially spherical particles having a diameter less than about 300 micrometers.

Claim 3

The composition as claimed in claim 1 wherein said material comprises gum, cellulose-based materials, soluble oxide polymers or mixtures thereof.

Claim 4

The composition as claimed in claim 1 wherein said material is selected from the group consisting of guar, agar, carboxymethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose, polyethyleneoxide and mixtures thereof.

Claim 5

The composition as claimed in claim 1 further comprising an outer enclosure for containing said composition.

Claim 6

The composition as claimed in claim 4 wherein said outer enclosure is constructed of a material selected from the group consisting of polyvinyl- and polyethylene-based materials.

Claim 7

A composition as claimed in claim 4 wherein said outer enclosure is constructed of polyvinylchloride material.

Claim 8

The composition as claimed in claim 4 wherein said outer enclosure is substantially non-flammable.

Claim 9

The composition as claimed in claim 1 wherein: (a) said water is present in an amount from about 20% by weight to about 75% by weight, (b) said material is present in an amount from about 0.5% by weight to about 10% by weight, and (c) said substantially spherical particles are present in an amount from about 0.1% by weight to about 32% by weight.

Claim 10

The composition as claimed in claim 1 wherein: (a) said water is present in an amount from about 50% by weight to about 60% by weight, (b) said material is present in an amount from about 2% by weight to about 4% by weight, (c) said substantially spherical particles are present in an amount from about 20% by weight to about 31% by weight, and (d) further comprising an antifreeze in an amount of from about 15% by weight to about 30% by weight.

Claim 11

The composition as claimed in claim 1 further comprising a material which provides a viscosity bonus effect.

Claim 12

The composition as claimed in claim 1 further comprising glycerin.

Claim 13

The composition as claimed in claim 11 wherein said glycerin is present in an amount of from about 15% by weight to about 30% by weight.

Claim 14

The composition as claimed in claim 1 further comprising a preservative.

Claim 15

The composition as claimed in claim 1 further comprising acid, benzoate, and sorbate.

Claim 16

The composition as claimed in claim 1 wherein said composition has been treated with radiation and/or heat in order to kill microorganisms present therein.

Claim 17

The composition as claimed in claim 1 wherein said composition has been subjected to x-ray or gamma ray radiation in order to kill microorganisms contained therein.

Claim 18

The composition as claimed in claim 1 wherein said composition has been subjected to heat of approximately 180.F for approximately 30 to 45 minutes to kill microorganisms contained therein.

Claim 19

A flowable, pressure-compensating composition comprising: (a) water in an amount from about 50% by weight to about 60% by weight, (b) a material selected from the group consisting of guar, agar, carboxymethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose and polyethyleneoxide in an amount from about 2% by weight to about 4% by weight, (c) substantially spherical particles in an amount from about 20% by weight to about 31% by weight, (d) glycerin present in an amount from about 15% by weight to about 30% by weight, and (e) acid sufficient to provide a pH for the composition in a range from about pH 4 to about pH 6.

Claim 20

A flowable, pressure-compensating composition comprising: (a) water in an amount from about 50% by weight to about 60% by weight, (b) a material selected from the group consisting of guar, agar, carboxymethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose and polyethyleneoxide in an amount from about 2% by weight to about 4% by weight, (c) substantially spherical particles in an amount from about 20% by weight to about 31% by weight, (d) glycerin present in an amount from about 15% by weight to about 30% by weight, and (e) acid sufficient to provide a pH for the composition in a range from about pH 4 to about pH 6.

Claim 21

The composition as claimed in claim 18 further comprising an effective amount of preservatives to prevent microbiological attack on said composition.

Claim 22

A process for producing a flowable, pressure-compensating composition comprising: (a) selecting a type and amount of viscosity-increasing agent, (b) selecting a type and amount of liquid having an affinity for said agent, (c) selecting a size, type and amount of substantially spherical particles, and (d) mixing the materials until said agent and said particles are distributed throughout said liquid.

Claim 23

A process for producing a flowable, pressure-compensating composition comprising: (a) selecting a type and amount of viscosity-increasing agent, (b) selecting a type and amount of liquid having an affinity for said agent, (c) selecting a size, type and amount of substantially spherical particles, and (d) mixing the materials until said agent and said particles are distributed throughout said liquid.

Claim 24

The process as claimed in claim 20 wherein said agent is selected from the group consisting of agar, guar, carboxymethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose and polyethyleneoxide.

Claim 25

The process as claimed in claim 20 wherein said liquid comprises water.

Claim 26

The process as claimed in claim 20 wherein: (a) the amount of said agent is in a range of from about 0.5 weight percent to about 10 weight percent, (b) the amount of said liquid is in a range of from about 20 weight percent to about 75 weight percent, and (c) the amount of said particles is in a range from about 0.1 weight percent to about 32 weight percent.

Claim 27

The process as claimed in claim 20 wherein said particles have a size of less than 300 micrometers.

Claim 28

The process as claimed in claim 20 further comprising the step of adding a material which provides a viscosity bonus effect.

Claim 29

The process as claimed in claim 20 further comprising the step of adding glycerin.

Claim 30

The process as claimed in claim 20 further comprising the step of adding acid.

Claim 31

The process as claimed in claim 20 further comprising the step of adding a preservative.

Claim 32

The process as claimed in claim 20 further comprising the step of sealing said pressure-compensating composition within an enclosure.

Claim 33

The process as claimed in claim 29 wherein a portion of said enclosure is sealed by heat.

Claim 34

The process as claimed in claim 29 wherein said enclosure comprises a polyvinylchloride material.

Claim 35

The process as claimed in claim 20 further comprising a step of treating said composition with radiation and/or heat in order to kill microorganisms contained within said composition.

Claim 36

The process as claimed in claim 20 further comprising the step of sterilizing said composition by exposing it to x-ray or gamma radiation.

Claim 37

The process as claimed in claim 20 further comprising the step of sterilizing said composition by exposing it to heat of at least about 180.F for a period of time of at least about 30 minutes.

Claim 38

The process as claimed in claim 20 wherein said substantially spherical particles are less dense than said liquid.

Claim 39

The process as claimed in claim 20 wherein said substantially spherical particles have a density greater than the density of said liquid.

Claim 40

A process for producing a padding device containing a flowable, pressure-compensating composition, said process comprising the steps of: (a) providing a first slurry comprising a viscosity-increasing agent selected from the group consisting of guar, agar, carboxymethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose and polyethyleneoxide in an amount from about 0.5% by weight of the total composition to about 4% by weight together with from about 15% by weight to about 30% by weight glycerin, (b) preparing a second slurry comprising from about 50% by weight to about 60% by weight water, from about 20% by weight to about 31% by weight spherical particles and an amount of acid sufficient to provide a composition pH in a range from about pH 4 to about pH 6, (c) mixing together said first slurry and second slurry, (d) placing said mixture within an enclosure, (e) sealing said enclosure, and (f) treating said composition in order to prevent microbiological attack.

Claim 41

A process for producing a padding device containing a flowable, pressure-compensating composition, said process comprising the steps of: (a) providing a first slurry comprising a viscosity-increasing agent selected from the group consisting of guar, agar, carboxymethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose and polyethyleneoxide in an amount from about 0.5% by weight of the total composition to about 4% by weight together with from about 15% by weight to about 30% by weight glycerin, (b) preparing a second slurry comprising from about 50% by weight to about 60% by weight water, from about 20% by weight to about 31% by weight spherical particles and an amount of acid sufficient to provide a composition pH in a range from about pH 4 to about pH 6, (c) mixing together said first slurry and second slurry, (d) placing said mixture within an enclosure, (e) sealing said enclosure, and (f) treating said composition in order to prevent microbiological attack.

Claim 42

A padding device comprising a flexible enclosure and a flowable, pressure-compensating composition substantially filling said enclosure, said flowable, pressure-compensating composition comprising: (a) water in an amount from about 50% by weight to about 60% by weight, (b) a material selected from the group consisting of guar, agar, carboxymethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose and polyethyleneoxide in an amount from about 0.5% by weight to about 4.0% by weight, (c) substantially spherical particles in an amount from about 20% by weight to about 31% by weight, and (d) glycerin present in an amount from about 15% by weight to about 30% by weight.

Claim 43

A padding device comprising a flexible enclosure and a flowable, pressure-compensating composition substantially filling said enclosure, said flowable, pressure-compensating composition comprising: (a) water in an amount from about 50% by weight to about 60% by weight, (b) a material selected from the group consisting of guar, agar, carboxymethylcellulose, hydroxypropylcellulose, hydroxyethylcellulose and polyethyleneoxide in an amount from about 0.5% by weight to about 4.0% by weight, (c) substantially spherical particles in an amount from about 20% by weight to about 31% by weight, and (d) glycerin present in an amount from about 15% by weight to about 30% by weight.