Resin composition and method of manufacturing the same
Assignee: DIC Corp
•
Filing: 1990-02-15
•
Granted: 1992-03-24
•
Expires: 2010-02-15
Abstract
Abstract Disclosed is a thermosetting resin composition which includes (a) an unsaturated polyester, (b) a polymer having a (meth)acrylate group only at one or both terminals of its main chain, (c) a poly(meth)acrylate oligomer, (d) a styrene monomer, and (e) a methyl methacrylate monomer. Also, a method of molding the resin is disclosed, which includes dividing the thermosetting resin composition into two parts, adding a curing agent to one of the two parts and a curing accelerator to another to form two partial compositions, introducing the two partial compositions into a mold, and allowing the two partial compositions to mix with each other and cure.
Inventors
- 👤 Katsuo Kagaya
- 👤 Tadao Saito
- 👤 Shichinosuke Ito
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 09:24
CPC Classifications
C; C08; C08L; C08L63/00; C08L63/10; C08L67/00; C08L67/06
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
181 words
A thermosetting resin composition comprising (a) an unsaturated polyester derived from an unsaturated dibasic acid, (b) a polymer having a (meth)acrylate group only at one or both terminals of a main chain of said polymer, (c) a poly(meth)acrylate oligomer having at least one isocyanurate ring, of the formula ##STR3## wherein A represents (meth)acrylic acid, Y represents a polybasic acid, X represents a polyhydric alcohol residue comprising a tris(hydroxyalkyl) isocyanurate as an essential component, and n is an integer of 0 to 3, (d) a styrene monomer, and (e) a methyl methacrylate monomer, wherein said components (a) and (b) are present in a weight proportion (a):(b) of 90:10 to 20:80, said components (a), (b) and (c) are present in a weight ratio (a)+(b):(c) of 98:2 to 2 to 60:40, said component (d) is present in an amount of 30 to 150 parts by weight per 100 parts by weight of said component (a), and said component (e) is present in an amount of 30 to 150 parts by weight per 100 parts by weight of sum of said components (b) and (c).
Claim 2
Dependent Claim
181 words
A thermosetting resin composition comprising (a) an unsaturated polyester derived from an unsaturated dibasic acid, (b) a polymer having a (meth)acrylate group only at one or both terminals of a main chain of said polymer, (c) a poly(meth)acrylate oligomer having at least one isocyanurate ring, of the formula ##STR3## wherein A represents (meth)acrylic acid, Y represents a polybasic acid, X represents a polyhydric alcohol residue comprising a tris(hydroxyalkyl) isocyanurate as an essential component, and n is an integer of 0 to 3, (d) a styrene monomer, and (e) a methyl methacrylate monomer, wherein said components (a) and (b) are present in a weight proportion (a):(b) of 90:10 to 20:80, said components (a), (b) and (c) are present in a weight ratio (a)+(b):(c) of 98:2 to 2 to 60:40, said component (d) is present in an amount of 30 to 150 parts by weight per 100 parts by weight of said component (a), and said component (e) is present in an amount of 30 to 150 parts by weight per 100 parts by weight of sum of said components (b) and (c).
Claim 3
Dependent Claim
24 words
A thermosetting resin composition as claimed in claim 1, wherein said component (a) contains 20 to 70% by weight of an unsaturated dibasic acid.
Claim 4
Dependent Claim
33 words
A thermosetting resin composition as claimed in claim 1, wherein said component (b) contains at least 10% by weight of (meth)acrylate group and has a number average molecular weight of 900 to 3,000.
Claim 5
Dependent Claim
24 words
A thermosetting resin composition as claimed in claim 1, wherein said component (b) is selected from the group consisting of epoxy(meth)acrylate and polyester (meth)acrylate.
Claim 6
Dependent Claim
24 words
A thermosetting resin composition as claimed in claim 3, wherein said component (b) is selected from the group consisting of epoxy(meth)acrylate and polyester (meth)acrylate.
Claim 7
Dependent Claim
14 words
A thermosetting resin composition as claimed in claim 1, further comprising a thermoplastic resin.
Claim 8
Dependent Claim
39 words
A thermosetting resin composition as claimed in claim 6, wherein said thermoplastic resin is present in an amount of 5 to 40 parts by weight per 100 parts by weight of sum of said components (a), (b) and (c).
Claim 9
Independent Claim
238 words
A method of molding a thermosetting resin composition comprising dividing said thermosetting resin composition into two parts, adding a curing agent to one of said two parts and a curing accelerator to another to form two partial compositions, introducing said two partial compositions into a mold, and allowing said two partial compositions to mix with each other and cure wherein said composition comprises (a) an unsaturated polyester derived from an unsaturated dibasic acid, (b) a polymer having a (meth)acrylate group only at one or both terminals of a main chain of said polymer, (c) a poly(meth)acrylate oligomer having at least one one isocyanurate ring, of the formula ##STR4## wherein A represents (meth)acrylic acid, Y represents a polybasic acid, X represents a polyhydric alcohol residue comprising a tris(hydroxyalkyl) isocyanurate as an essential component, and n is an integer of 0 to 3, (d) a styrene monomer, and (e) a methyl methacrylate monomer, wherein said components (a) and (b) are present in a weight proportion (a):(b) of 90:10 to 20:80, said components (a), (b) and (c) are present in a weight ratio (a)+(b):(c) of 98:2 to 60:40, said component (d) is present in an amount of 30 to 150 parts by weight per 100 parts by weight of said component (a), and said component (e) is present in an amount of 30 to 150 parts by weight per 100 parts by weight of sum of said components (b) and (c).
Claim 10
Independent Claim
238 words
A method of molding a thermosetting resin composition comprising dividing said thermosetting resin composition into two parts, adding a curing agent to one of said two parts and a curing accelerator to another to form two partial compositions, introducing said two partial compositions into a mold, and allowing said two partial compositions to mix with each other and cure wherein said composition comprises (a) an unsaturated polyester derived from an unsaturated dibasic acid, (b) a polymer having a (meth)acrylate group only at one or both terminals of a main chain of said polymer, (c) a poly(meth)acrylate oligomer having at least one one isocyanurate ring, of the formula ##STR4## wherein A represents (meth)acrylic acid, Y represents a polybasic acid, X represents a polyhydric alcohol residue comprising a tris(hydroxyalkyl) isocyanurate as an essential component, and n is an integer of 0 to 3, (d) a styrene monomer, and (e) a methyl methacrylate monomer, wherein said components (a) and (b) are present in a weight proportion (a):(b) of 90:10 to 20:80, said components (a), (b) and (c) are present in a weight ratio (a)+(b):(c) of 98:2 to 60:40, said component (d) is present in an amount of 30 to 150 parts by weight per 100 parts by weight of said component (a), and said component (e) is present in an amount of 30 to 150 parts by weight per 100 parts by weight of sum of said components (b) and (c).
References Cited (Backward Citations)
US3793398A
Cited
EP0189987A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-24 | 1995-09-23 | 1996-03-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-24 | 1999-09-23 | 2000-03-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-24 | 2003-09-23 | 2004-03-24 | $7700.00 | Window Closed / Lapsed |