Heat resistant adhesive composition and bonding method using the same
Assignee: Resonac Corp
•
Filing: 1990-03-16
•
Granted: 1992-02-18
•
Expires: 2010-03-16
Abstract
Abstract A heat resistant adhesive composition comprising a specific polyamic acid solution and a bis-maleimide compound exhibits flexibility and excellent heat resistance after bonding two material bodies, and therefore, it can be suitably used for producing of flexible metal-clad laminates, double-sided flexible metal-clad laminates, and multilayer printed circuit boards, and for attaching coverlay films to printed circuit boards.
Inventors
- 👤 Junichi Imaizumi
- 👤 Hiroshi Nomura
- 👤 Kouichi Nagao
- 👤 Masakatsu Suzuki
- 👤 Koushi Sakairi
- 👤 Eikichi Satou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 07:35
CPC Classifications
B; B32; B32B; B32B7/00; B32B7/04; B32B7/12; B32B15/00; B32B15/04; B32B15/08; B32B27/00; B32B27/28; B32B27/281; B32B38/00; B32B38/0008; C; C08; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/12; C08L; C08L79/00; C08L79/04; C08L79/08; C08L79/085; H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/303; H01B3/306; H05; H05K; H05K3/00; H05K3/22; H05K3/28; H05K3/281; H05K3/38; H05K3/386; B32B2310/00; B32B2310/14; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/0353; H05K1/036; H05K1/0393; H05K2201/00; H05K2201/01; H05K2201/0137; H05K2201/0154; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K2201/0358; H05K2203/00; H05K2203/07; H05K2203/0756; H05K2203/0759; H05K2203/09; H05K2203/095; H05K3/46; H05K3/4611; H05K3/4626; H05K3/4635; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678; Y10T428/31681
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
210 words
A method of bonding two material bodies to each other comprising (a) coating a surface of at least one of the material bodies with a heat resistant adhesive composition, the heat resistant adhesive composition comprising (A) a polyamic acid solution comprising a polyamic acid and a solvent, the polyamic acid being capable of being converted into a polyimide having a glass transition temperature not higher than 260° C. by heating the polyamic acid to dehydrate the polyamic acid and (B) a bis-maleimide compound in an amount of from 20 to 60 parts by weight per 100 parts by weight of the polyamic acid, (b) heating the heat resistant adhesive composition coating the surface of the at least one of the material bodies so that the solvent is removed from the heat resistant adhesive composition and conversion of the polyamic acid into the polyimide starts and proceeds, (c) bringing the coated surface of the at least one of the material bodies into contact with a surface of the other material body to form a composite, and (d) thermopressing the composite by simultaneously pressing the composite and heating the composite at a temperature not lower than the temperature for thermosetting of the bis-maleimide compound to convert the bis-maleimide compound into a poly-bis-maleimide.
Claim 2
Independent Claim
210 words
A method of bonding two material bodies to each other comprising (a) coating a surface of at least one of the material bodies with a heat resistant adhesive composition, the heat resistant adhesive composition comprising (A) a polyamic acid solution comprising a polyamic acid and a solvent, the polyamic acid being capable of being converted into a polyimide having a glass transition temperature not higher than 260° C. by heating the polyamic acid to dehydrate the polyamic acid and (B) a bis-maleimide compound in an amount of from 20 to 60 parts by weight per 100 parts by weight of the polyamic acid, (b) heating the heat resistant adhesive composition coating the surface of the at least one of the material bodies so that the solvent is removed from the heat resistant adhesive composition and conversion of the polyamic acid into the polyimide starts and proceeds, (c) bringing the coated surface of the at least one of the material bodies into contact with a surface of the other material body to form a composite, and (d) thermopressing the composite by simultaneously pressing the composite and heating the composite at a temperature not lower than the temperature for thermosetting of the bis-maleimide compound to convert the bis-maleimide compound into a poly-bis-maleimide.
Claim 3
Dependent Claim
34 words
The method as claimed in claim 1, wherein the thermopressing of the composite is carried out by passing the composite through a pair of rolls at least one of which is a heating roll.
Claim 4
Dependent Claim
28 words
The method as claimed in claim 1, wherein one of the material body is a sheet of metal foil and the other material body is a polyimide film.
Claim 5
Dependent Claim
34 words
The method as claimed in claim 3, wherein the thermopressing of the composite is carried out by passing the composite through a pair of rolls at least one of which is a heating roll.
Claim 6
Dependent Claim
32 words
The method as claimed in claim 3, wherein the surface of the polyimide film which is to be bonded to the sheet of metal foil has been subjected to a plasma treatment.
Claim 7
Dependent Claim
34 words
The method as claimed in claim 5, wherein the thermopressing of the composite is carried out by passing the composite through a pair of rolls at least one of which is a heating roll.
Claim 8
Dependent Claim
51 words
The method as claimed in claim 1, wherein the two material bodies are each a two-layer flexible metal-clad laminate which comprises a polyimide layer having an exposed surface and a metal layer, the exposed surfaces of the polyimide layers being subjected to a plasma treatment and being bonded to each other.
Claim 9
Dependent Claim
34 words
The method as claimed in claim 7, wherein the thermopressing of the composite is carried out by passing the composite through a pair of rolls at least one of which is a heating roll.
Claim 10
Dependent Claim
69 words
The method as claimed in claim 1, wherein one of the two material bodies is a sheet of metal foil, and the other material body is a two-layer flexible metal-clad laminate which comprises a polyimide layer having an exposed surface and a metal layer, the exposed surface of the polyimide film being subjected to a plasma treatment and being bonded to a surface of the sheet of metal foil.
Claim 11
Dependent Claim
34 words
The method as claimed in claim 9, wherein the thermopressing of the composite is carried out by passing the composite through a pair of rolls at least one of which is a heating roll.
Claim 12
Dependent Claim
74 words
The method as claimed in claim 1, wherein one of the two material bodies is a sheet of polyimide film, and the other material body is a two-layer flexible printed board which comprises a polyimide layer and a metal circuit layer having an exposed surface, a surface of the polyimide film being subjected to a plasma treatment and being bonded to the exposed surface of the metal circuit layer of the flexible printed board.
Claim 13
Dependent Claim
257 words
The method as claimed in claim 1, wherein the polyamic acid having a repeating unit of the formula ##STR10## wherein R 1 is ##STR11## each R 3 , respectively, being hydrogen, a halogen or an alkyl group of from 1 to 4 carbon atoms and each X and Y, respectively, being ##STR12## each R 4 , respectively, being hydrogen, an alkyl group of from 1 to 4 carbon atoms or --CF 3 , R 2 is ##STR13## the solvent being selected from the group consisting of N-methyl-2-pyrrolidone, N,N-dimethylformamide, N,N-dimethylacetamide, dimethyl sulfoxide, phenol, halogenated phenol, 1,4-dioxane, y-butyrolactone, tetrahydrofuran, diethyleneglycol dimethyl ether and mixtures thereof; the weight ratio of the polyamic acid and the solvent being 5:95 to 25:75; the polyamic acid solution having a rotation viscosity of more than 500 poise; the bis-maleimide compound being selected from the group consisting of N,N'-m-phenylene-bis-maleimide, N,N'-p-phenylene-bis-maleimide, N,N'-(oxy-di-p-phenylene)bis-maleimide, N,N'-(methylene-di-p-phenylene)bis-maleimide, N,N'-(sulfone-di-p-phenylene)bis-maleimide, 2,2-bis(maleimide-phenoxyphenyl)propanes and mixtures thereof; the bis-maleimide compound being in an amount of 30 to 50 parts by weight per 100 parts by weight of the polyamic acid in the polyamic acid solution; the heating being carried out at a temperature lower than the temperature for thermosetting of the bis-maleimide compound; the solvent content after the heating being not more than 5% by weight; the thermopressing being carried out at a temperature not lower than the glass transition temperature of the polyimide converted from the polyamic acid and not lower than the temperature for thermosetting of the bis-maleimide compound; and the pressure for the thermopressing being not lower than 10 kgf/cm 2 .
Claim 14
Dependent Claim
16 words
A double-sided flexible metal-clad laminate which is produced by the method as claimed in claim 7.
Claim 15
Dependent Claim
16 words
A double-sided flexible metal-clad laminate which is produced by the method as claimed in claim 8.
Claim 16
Dependent Claim
16 words
A double-sided flexible metal-clad laminate which is produced by the method as claimed in claim 9.
Claim 17
Dependent Claim
16 words
A double-sided flexible metal-clad laminate which is produced by the method as claimed in claim 10.
Claim 18
Dependent Claim
18 words
A flexible printed board with coverlay film which is produced by the method as claimed in claim 11.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-02-17 | 1995-08-19 | 1996-02-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-02-17 | 1999-08-19 | 2000-02-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-02-17 | 2003-08-19 | 2004-02-18 | $7700.00 | Window Closed / Lapsed |