Method of manufacturing photo-mask and photo-mask manufactured thereby
Assignee: Sharp Corp
•
Filing: 1987-02-27
•
Granted: 1992-02-11
•
Expires: 2007-02-27
Abstract
Abstract A photo-mask and a method of manufacturing a photo-mask, which includes the steps of applying a resist film onto a substrate of quartz, glass and the like, subjecting the resist film to light exposure and development to form a fine resist pattern, etching the mask substrate covered by the fine resist pattern causing a non-light transmitting thin film of Cr, Ta, etc. to adhere thereon by vapor deposition, sputtering and the like, and removing the thin film on the resist pattern together with the resist film, thereby to form the photo-mask.
Inventors
- 👤 Junji Hirokane
- 👤 Hiroyuki Katayama
- 👤 Akira Takahashi
- 👤 Tetsuya Inui
- 👤 Kenji Ohta
- 👤 Junichi Washo
- 👤 Tomoyuki Miyake
- 👤 Kazuo Van
- 👤 Michinobu Mieda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 21:17
CPC Classifications
G; G03; G03F; G03F1/00; G03F1/54; G03F1/68; G11; G11B; G11B7/00; G11B7/24; G11B7/26; G11B7/261; Y; Y10; Y10S; Y10S430/00; Y10S430/146
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
148 words
A method of manufacturing a photo-mask for an optical disc, which comprises the steps of: forming a light-transmitting first thin film on a mask substrate, applying a resist film on said first thin film; subjecting said resist film to light exposure and development so as to form a fine resist pattern, subjecting said first thin film to dry isotropic etching so as to form grooves in a portion of said first thin film not covered by said resist pattern and so as to widen said groove in said mask substrate, applying on said fine resist pattern and said groove a light-shielding second thin film, and removing said light-shielding second thin film formed on said fine resist pattern together with said resist film so as to form said photo-mask having a mask pattern of said light-shielding second thin film formed in said grooves on said light-transmitting first thin film.
Claim 2
Independent Claim
148 words
A method of manufacturing a photo-mask for an optical disc, which comprises the steps of: forming a light-transmitting first thin film on a mask substrate, applying a resist film on said first thin film; subjecting said resist film to light exposure and development so as to form a fine resist pattern, subjecting said first thin film to dry isotropic etching so as to form grooves in a portion of said first thin film not covered by said resist pattern and so as to widen said groove in said mask substrate, applying on said fine resist pattern and said groove a light-shielding second thin film, and removing said light-shielding second thin film formed on said fine resist pattern together with said resist film so as to form said photo-mask having a mask pattern of said light-shielding second thin film formed in said grooves on said light-transmitting first thin film.
Claim 3
Independent Claim
137 words
A method of manufacturing a photo-mask for an optical disc, which comprises the steps of: applying a resist film onto a mask substrate, subjecting said resist film to light exposure and development to form a fine resist pattern, subjecting said mask substrate not covered by said fine resist pattern to anisotropic etching so as to form grooves in a portion not covered by said fine resist pattern, further subjecting said mask substrate to isotropic etching so as to widen said grooves in said mask substrate, forming a light-shielding thin film on said fine resist pattern and said grooves, and removing said light-shielding thin film formed on said resist pattern together with said resist film so as to form said photo-mask having a mask pattern of said light-shielding thin film formed in said grooves on said mask substrate.
Claim 4
Independent Claim
137 words
A method of manufacturing a photo-mask for an optical disc, which comprises the steps of: applying a resist film onto a mask substrate, subjecting said resist film to light exposure and development to form a fine resist pattern, subjecting said mask substrate not covered by said fine resist pattern to anisotropic etching so as to form grooves in a portion not covered by said fine resist pattern, further subjecting said mask substrate to isotropic etching so as to widen said grooves in said mask substrate, forming a light-shielding thin film on said fine resist pattern and said grooves, and removing said light-shielding thin film formed on said resist pattern together with said resist film so as to form said photo-mask having a mask pattern of said light-shielding thin film formed in said grooves on said mask substrate.
Claim 5
Independent Claim
161 words
A method of manufacturing a photo-mask for an optical disc, which comprises the steps of: applying onto a mask substrate a first thin film in which isotropic etching will proceed in a dry etching process, applying a resist film on said first thin film, subjecting said resist film to light exposure and development to form a fine resist pattern, subjecting said mask substrate covered by said fine resist pattern to dry etching so as to form grooves in portions not covered by said fine resist pattern, wherein isotropic etching proceeds to widen said grooves in said first thin film, applying a non-light transmitting second thin film on said fine resist pattern and said mask substrate, removing said second thin film formed on said fine resist pattern together with said resist film and subsequently removing said first thin film so as to form said photo-mask having a mask pattern of said second thin film formed in said grooves on said mask substrate.
Claim 6
Independent Claim
161 words
A method of manufacturing a photo-mask for an optical disc, which comprises the steps of: applying onto a mask substrate a first thin film in which isotropic etching will proceed in a dry etching process, applying a resist film on said first thin film, subjecting said resist film to light exposure and development to form a fine resist pattern, subjecting said mask substrate covered by said fine resist pattern to dry etching so as to form grooves in portions not covered by said fine resist pattern, wherein isotropic etching proceeds to widen said grooves in said first thin film, applying a non-light transmitting second thin film on said fine resist pattern and said mask substrate, removing said second thin film formed on said fine resist pattern together with said resist film and subsequently removing said first thin film so as to form said photo-mask having a mask pattern of said second thin film formed in said grooves on said mask substrate.
Claim 7
Independent Claim
157 words
A method of manufacturing a photo-mask for an optical disc, which comprises the steps of: forming a resist layer on a light-transmitting mask substrate, forming a desired resist pattern on said resist layer by light exposure and development, forming grooves of a desired pattern on said mask substrate by anisotropic etching, removing said resist layer from said mask substrate, forming a light-shielding first layer on said mask substrate having said grooves so as to form an undulated surface, forming a height-supplementing second layer on said light-shielding first layer so as to make the surface of said second layer generally uniform, and removing said height-supplementing second layer and said light-shielding first layer so as to expose the surface of said mask substrate at portions other than the portions covered by said light-shielding first layer in said grooves thereby forming said photo-mask having a mask pattern of said light-shielding first layer formed in said grooves of said mask substrate.
Claim 8
Independent Claim
157 words
A method of manufacturing a photo-mask for an optical disc, which comprises the steps of: forming a resist layer on a light-transmitting mask substrate, forming a desired resist pattern on said resist layer by light exposure and development, forming grooves of a desired pattern on said mask substrate by anisotropic etching, removing said resist layer from said mask substrate, forming a light-shielding first layer on said mask substrate having said grooves so as to form an undulated surface, forming a height-supplementing second layer on said light-shielding first layer so as to make the surface of said second layer generally uniform, and removing said height-supplementing second layer and said light-shielding first layer so as to expose the surface of said mask substrate at portions other than the portions covered by said light-shielding first layer in said grooves thereby forming said photo-mask having a mask pattern of said light-shielding first layer formed in said grooves of said mask substrate.
Claim 9
Dependent Claim
60 words
The method as defined in claim 1, wherein said light-transmitting first thin film and said light-shielding second thin film are formed by vapor deposition or sputtering, and wherein said second thin film is formed so as to be discontinuous between said fine resist pattern and said groove so as to facilitate removing said second thin film and said resist film.
Claim 10
Dependent Claim
36 words
The method as defined in claim 5, wherein said mask substrate comprises quartz or glass, said light-transmitting first thin film comprises Si 3 N 4 , and said light-shielding second thin film comprises Cr or Ta.
Claim 11
Dependent Claim
25 words
The method as defined in claim 6, wherein said mask pattern is formed to be lower than the surface of said light-shielding second thin film.
Claim 12
Dependent Claim
36 words
The method as defined in claim 2, wherein said anisotropic etching comprises a dry etching method, said isotropic etching comprises a wet etching method and said light-shielding thin film is formed by vapor deposition or sputtering.
Claim 13
Dependent Claim
24 words
The method as defined in claim 8, wherein said mask substrate comprises quartz or glass and said light-shielding thin film comprises Cr or Ta.
Claim 14
Dependent Claim
23 words
The method as defined in claim 9, wherein said mask patter is formed to be lower than the surface of said mask substrate.
Claim 15
Dependent Claim
24 words
The method as defined in claim 3, wherein said first thin film and said second thin film are formed by vapor deposition or sputtering.
Claim 16
Dependent Claim
32 words
The method as defined in claim 3, wherein said first thin film is removed together with said non-light transmitting second thin film formed on said fine resist pattern and said resist film.
Claim 17
Dependent Claim
21 words
The method as defined in claim 11, wherein said first thin film comprises Si, Mo or Si 3 N 4 .
Claim 18
Dependent Claim
26 words
The method as defined in claim 13, wherein said mask substrate comprises quartz or glass and said non-light transmitting second thin film comprises Cr or Ta.
Claim 19
Dependent Claim
23 words
The method as defined in claim 14, wherein said mask pattern is formed to be lower than the surface of said mask substrate.
Claim 20
Dependent Claim
76 words
The method as defined in claim 4, wherein said light-shielding first layer is formed on said mask substrate such that the thickness of said first layer is greater than the depth of said grooves formed in said mask substrate, and wherein and first layer and said height-supplementing second layer are removed by dry etching at an equal rate so as to form a mask pattern which does not protrude from the surface of said mask substrate.
Claim 21
Dependent Claim
49 words
The method as defined in claim 16, wherein said resist film is formed by spin-coating, said resist pattern is formed by employment of an electron beam or a laser, said light-shielding first layer is formed by vapor deposition or sputtering, and said height-supplementing second layer is formed by spin-coating.
Claim 22
Dependent Claim
31 words
The method as defined in claim 17, wherein said mask substrate comprises quartz or glass, said light-shielding first layer comprises Cr or Ta and said height-supplementing second layer comprises a photo-resist.
Claim 23
Dependent Claim
77 words
The method as defined in claim 4, wherein said light-shielding first layer is formed on said mask substrate such that the thickness of said first layer is less than the depth of said grooves formed in said mask substrate, and wherein said first layer and said height-supplementing second layer are removed by dry etching at an equal rate so as to form a mask pattern which is concave with respect to the surface of said mask substrate.
Claim 24
Dependent Claim
49 words
The method as defined in claim 19, wherein said resist film is formed by spin-coating, said resist pattern is formed by employment of an electron beam or a laser, said light-shielding first layer is formed by vapor deposition or sputtering, and said height-supplementing second layer is formed by spin-coating.
Claim 25
Dependent Claim
31 words
The method as defined in claim 20, wherein said mask substrate comprises quartz or glass, said light-shielding first layer comprises Cr or Ta and said height-supplementing second layer comprises a photo-resist.
Claim 26
Dependent Claim
50 words
The method as defined in claim 4, wherein said light-shielding first layer and said height-supplementing second layer are removed by dry etching such that said second layer is removed at a faster rate so as to form a mask pattern which is lower than the surface of said mask substrate.
Claim 27
Dependent Claim
49 words
The method as defined in claim 22, wherein said resist film is formed by spin-coating, said resist pattern is formed by employment of an electron beam or a laser, said light-shielding first layer is formed by vapor deposition or sputtering, and said height-supplementing second layer is formed by spin-coating.
Claim 28
Dependent Claim
31 words
The method as defined in claim 23, wherein said mask substrate comprises quartz or glass, said light-shielding first layer comprises Cr or Ta and said height-supplementing second layer comprises a photo-resist.
Claim 29
Dependent Claim
10 words
A photo-mask formed by the method defined by claim 1.
References Cited (Backward Citations)
US4094347A
Cited
JPS53143204A
Cited
JPS565545A
Cited
US4423137A
Cited
JPS57112727A
Cited
JPS57207256A
Cited
EP0069265A1
Cited
JPS58202526A
Cited
JPS599659A
Cited
JPS5968744A
Cited
US4686162A
Cited
JPS59172648A
Cited
JPS6156349A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-02-10 | 1995-08-12 | 1996-02-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-02-10 | 1999-08-12 | 2000-02-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-02-10 | 2003-08-12 | 2004-02-11 | $7700.00 | Window Closed / Lapsed |