Light modulating material and method for preparing same
Assignee: Kent State University
•
Filing: 1990-11-16
•
Granted: 1992-02-11
•
Expires: 2010-11-16
Abstract
Abstract An improved light modulating material for use in electro-optic and thermo-optic display devices is produced by forming a homogeneous solution comprising an acrylic resin containing active hydrogen groups, a liquid crystal material, a diisocyanate or epoxide, and a solvent. The homogeneous solution is preferably applied to a conductive substrate and the solvent is then evaporated, causing phase separation resulting in formation of a liquid crystal phase dispersed within a solid polymer matrix. Application of an electric field to the substrate causes the liquid crystal material to align, which in turn causes the coating to switch from substantially translucent to substantially transparent. If the electric field is removed the light modulating material again becomes substantially translucent. Switching times can be improved by incorporating a titanate or zirconate organometallic material into the light modulating material.
Inventors
- 👤 Patrick W. Mullen
- 👤 Frederick E. Nobile
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 12:28
CPC Classifications
C; C09; C09K; C09K19/00; C09K19/52; C09K19/54; C09K19/542; C09K19/544
Claims Analysis
Total Claims: 41
Claim 1
Independent Claim
99 words
A light modulating material comprising a liquid crystal phase formed within a polymer matrix, the polymer matrix comprising: an acrylic resin having active hydrogen groups selected from the group consisting of hydroxy-functional acrylic resins; an organometallic material selected from the group consisting of titanates, zirconates and mixtures thereof; and a cross-linking agent selected from the group consisting of diisocyanates for reacting with the hydroxy-functional acrylic resin to form a urethane acrylic copolymer; the light modulating material being capable of reversibly switching between a substantially translucent state and a substantially transparent state when subjected to an electric or magnetic field.
Claim 2
Dependent Claim
99 words
A light modulating material comprising a liquid crystal phase formed within a polymer matrix, the polymer matrix comprising: an acrylic resin having active hydrogen groups selected from the group consisting of hydroxy-functional acrylic resins; an organometallic material selected from the group consisting of titanates, zirconates and mixtures thereof; and a cross-linking agent selected from the group consisting of diisocyanates for reacting with the hydroxy-functional acrylic resin to form a urethane acrylic copolymer; the light modulating material being capable of reversibly switching between a substantially translucent state and a substantially transparent state when subjected to an electric or magnetic field.
Claim 3
Dependent Claim
37 words
The light modulating material of claim 1, wherein the organometallic material comprises a titanate selected from the group consisting of neopentyl (diallyl) oxy, tri (dodecyl) benzene-sulfonyl titanate; neopentyl (diallyl) oxy, tri (N-ethylenediamino) ethyl titanate; and mixtures thereof.
Claim 4
Dependent Claim
38 words
The light modulating material of claim 1, wherein the organometallic material comprises a zirconate selected from the group consisting of neopentyl (diallyl) oxy, tri (dodecyl) benzene-sulfonyl zirconate; neopentyl (diallyl) oxy, tri (N-ethylene diamino) ethyl zirconate; and mixtures thereof.
Claim 5
Dependent Claim
58 words
A light modulating material comprising a liquid crystal phase formed within a polymer matrix comprising a urethane-acrylic copolymer, and an organometallic material selected from the group consisting of titanates, zirconates and mixtures thereof, the material being capable of reversibly switching between a substantially translucent state and a substantially transparent state when subjected to an electrical or magnetic field.
Claim 6
Dependent Claim
58 words
A light modulating material comprising a liquid crystal phase formed within a polymer matrix comprising a urethane-acrylic copolymer, and an organometallic material selected from the group consisting of titanates, zirconates and mixtures thereof, the material being capable of reversibly switching between a substantially translucent state and a substantially transparent state when subjected to an electrical or magnetic field.
Claim 7
Dependent Claim
83 words
A light modulating material comprising a liquid crystal phase formed within a polymer matrix, the polymer matrix comprising: an acrylic resin having active hydrogen groups selected from the group consisting of carboxy-functional acrylic resins; and a cross-linking agent selected from the group consisting of epoxides for reacting with the carboxy-functional acrylic resin to form an epoxy-acrylic copolymer; the light modulating material being capable of switching between a substantially translucent state and a substantially transparent state when subjected to an electrical or magnetic field.
Claim 8
Dependent Claim
83 words
A light modulating material comprising a liquid crystal phase formed within a polymer matrix, the polymer matrix comprising: an acrylic resin having active hydrogen groups selected from the group consisting of carboxy-functional acrylic resins; and a cross-linking agent selected from the group consisting of epoxides for reacting with the carboxy-functional acrylic resin to form an epoxy-acrylic copolymer; the light modulating material being capable of switching between a substantially translucent state and a substantially transparent state when subjected to an electrical or magnetic field.
Claim 9
Dependent Claim
34 words
The light modulating material of claim 5, wherein the liquid crystal phase is formed upon phase separation resulting from evaporation or cooling of a homogeneous solution comprising liquid crystal material and the acrylic resin.
Claim 10
Dependent Claim
53 words
The light modulating material of claim 6, wherein the liquid crystal phase has optic axes which are normally randomly oriented to scatter light and provide a substantially translucent appearance for said light modulating material, the optic axes being aligned by the application of a field to render the light modulating material substantially transparent.
Claim 11
Dependent Claim
19 words
The light modulating material of claims 5, 6, or 7 wherein the polymer matrix further comprises an epoxy-acrylic copolymer.
Claim 12
Dependent Claim
23 words
The light modulating material of claim 5, further comprising an organometallic material selected from the group consisting of titanates, zirconates and mixtures thereof.
Claim 13
Dependent Claim
11 words
An electro-optic device comprising the light modulating material of claim 8.
Claim 14
Dependent Claim
14 words
A thermo-optic device comprising the light modulating material of claims 5, 6, or 7.
Claim 15
Dependent Claim
62 words
A light modulating material comprising a liquid crystal phase formed within a polymer matrix, the polymer matrix comprising an epoxy-acrylic copolymer formed by reacting a carboxy-functional acrylic resin with an epoxide within the polymer matrix, the light modulating material being capable of reversibly switching between a substantially translucent state and a substantially transparent state when subjected to an electrical or magnetic field.
Claim 16
Dependent Claim
62 words
A light modulating material comprising a liquid crystal phase formed within a polymer matrix, the polymer matrix comprising an epoxy-acrylic copolymer formed by reacting a carboxy-functional acrylic resin with an epoxide within the polymer matrix, the light modulating material being capable of reversibly switching between a substantially translucent state and a substantially transparent state when subjected to an electrical or magnetic field.
Claim 17
Dependent Claim
69 words
A light modulating material comprising a liquid crystal phase interspersed with a urethane cross-linked hydroxy functionalized polymer, said polymer being formed by reacting hydroxy functional groups pendent from the polymeric chain with a cross-linking agent selected from the group consisting of isocyanates, the light modulating material being capable of reversibly switching between a translucent state and a transparent state when subjected to an electrical field or a magnetic field.
Claim 18
Dependent Claim
69 words
A light modulating material comprising a liquid crystal phase interspersed with a urethane cross-linked hydroxy functionalized polymer, said polymer being formed by reacting hydroxy functional groups pendent from the polymeric chain with a cross-linking agent selected from the group consisting of isocyanates, the light modulating material being capable of reversibly switching between a translucent state and a transparent state when subjected to an electrical field or a magnetic field.
Claim 19
Dependent Claim
37 words
The light modulating material of claim 13, wherein the liquid crystal phase is formed by phase separation resulting from removal of solvent from a solution including liquid crystal, the hydroxy functionalized polymer and the isocyanate cross-linking agent.
Claim 20
Dependent Claim
35 words
The light modulating material of claim 13, wherein the liquid crystal phase is formed by phase separation resulting from cooling of a solution including liquid crystal, the hydroxy functionalized polymer and the isocyanate cross-linking agent.
Claim 21
Dependent Claim
45 words
The light modulating material of claim 13, wherein the liquid crystal phase has optic axes which are normally randomly oriented for scattering light, the optic axes being alignable by the application of a magnetic or electric field to render the light modulating material light transmissive.
Claim 22
Dependent Claim
20 words
The light modulating material of claim 13, wherein the hydroxy functionalized polymer comprises an acrylic polymer with pendent hydroxy groups.
Claim 23
Dependent Claim
16 words
The light modulating material of claim 13, wherein the liquid crystal phase comprises a nematic material.
Claim 24
Dependent Claim
21 words
The light modulating material of claim 13, wherein the liquid crystal phase comprises a nematic material and a chiral mesogenic material.
Claim 25
Dependent Claim
16 words
The light modulating material of claim 13, wherein the liquid crystal phase comprises a smectic material.
Claim 26
Dependent Claim
11 words
The electro-optic device comprising the light modulating material of claim 13.
Claim 27
Dependent Claim
11 words
A thermo-optic device comprising the light modulating material of claim 13.
Claim 28
Dependent Claim
22 words
The light modulating material of claim 13, further comprising an organometallic material selected from the group of titanates, zirconates and mixtures thereof.
Claim 29
Dependent Claim
22 words
The light modulating material of claim 13 wherein the liquid crystal phase comprises microdroplets dispersed in the urethane cross-linked hydroxy functionalized polymer.
Claim 30
Independent Claim
66 words
A method of making a light modulating material comprising the steps of: forming a solution of liquid crystal, hydroxy functionalized polymer and isocyanate cross-linking agent; phase separating a liquid crystal phase from the polymer phase; and, allowing the isocyanate cross-linking agent to react with the hydroxy groups of the hydroxy functionalized polymer to form a urethane cross-linked hydroxy functionalized polymer interspersed with the liquid crystal phase.
Claim 31
Independent Claim
66 words
A method of making a light modulating material comprising the steps of: forming a solution of liquid crystal, hydroxy functionalized polymer and isocyanate cross-linking agent; phase separating a liquid crystal phase from the polymer phase; and, allowing the isocyanate cross-linking agent to react with the hydroxy groups of the hydroxy functionalized polymer to form a urethane cross-linked hydroxy functionalized polymer interspersed with the liquid crystal phase.
Claim 32
Dependent Claim
34 words
The method of claim 25, wherein the isocyanate cross-linking agent, liquid crystal, and hydroxy functionalized polymer are dissolved in a solvent and the liquid crystal phase is phase separated by removal of the solvent.
Claim 33
Dependent Claim
34 words
The method of claim 25, wherein the hydroxy functionalized polymer, liquid crystal and isocyanate cross-linking agent are heated to form a solution and then allowed to cool to phase separate the liquid crystal phase.
Claim 34
Independent Claim
64 words
The method of making a light modulating material comprising the steps of: forming a solution of liquid crystal, carboxy functionalized polymer and epoxide cross-linking agent; phase separating the liquid crystal phase from the polymer phase; and allowing the epoxide cross-linking agent to react with the carboxy groups of the polymer to form an epoxy cross-linked carboxy functionalized polymer interspersed with the liquid crystal phase.
Claim 35
Independent Claim
64 words
The method of making a light modulating material comprising the steps of: forming a solution of liquid crystal, carboxy functionalized polymer and epoxide cross-linking agent; phase separating the liquid crystal phase from the polymer phase; and allowing the epoxide cross-linking agent to react with the carboxy groups of the polymer to form an epoxy cross-linked carboxy functionalized polymer interspersed with the liquid crystal phase.
Claim 36
Dependent Claim
33 words
The method of claim 28, wherein the epoxy cross-linking agent, liquid crystal, and carboxy functionalized polymer are dissolved in a solvent and the liquid crystal is phase separated by removal of the solvent.
Claim 37
Dependent Claim
33 words
The method of claim 28, wherein the epoxy cross-linking agent, liquid crystal, and carboxy functionalized polymer are heated to form a solution and then allowed to cool to phase separate the liquid crystal.
Claim 38
Dependent Claim
69 words
A light modulating material comprising a liquid crystal phase interspersed with an epoxy cross-linked carboxy functionalized polymer, said polymer being formed by reacting carboxy functional groups pendent from the polymeric chain with a cross-linking agent selected from the group consisting of epoxides, the light modulating material being capable of reversibly switching between a translucent state and a transparent state when subjected to an electric field or a magnetic field.
Claim 39
Dependent Claim
69 words
A light modulating material comprising a liquid crystal phase interspersed with an epoxy cross-linked carboxy functionalized polymer, said polymer being formed by reacting carboxy functional groups pendent from the polymeric chain with a cross-linking agent selected from the group consisting of epoxides, the light modulating material being capable of reversibly switching between a translucent state and a transparent state when subjected to an electric field or a magnetic field.
Claim 40
Dependent Claim
23 words
The light modulating material of claim 31, further comprising an organometallic material selected from the group consisting of titanates, zirconates and mixtures thereof.
Claim 41
Dependent Claim
22 words
The light modulating material of claim 31, wherein the liquid crystal phase comprises microdroplets dispersed in the epoxy cross-linked carboxy functionalized polymer.
References Cited (Backward Citations)
US3578844A
Cited
US3585381A
Cited
US3697297A
Cited
US3720623A
Cited
US3852092A
Cited
US3872050A
Cited
US3935337A
Cited
US4101207A
Cited
US4182700A
Cited
US4268126A
Cited
US4456335A
Cited
US4707080A
Cited
US4605284A
Cited
US4616903A
Cited
WO1985004262A1
Cited
US4688900A
Cited
EP0156615A2
Cited
EP0168180A1
Cited
EP0165063A1
Cited
US4672089A
Cited
US4742097A
Cited
US4623738A
Cited
EP0202067A2
Cited
EP0204537A2
Cited
WO1987001822A1
Cited
US4685771A
Cited
US4671618A
Cited
US4673255A
Cited
EP0282963A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-02-10 | 1995-08-12 | 1996-02-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-02-10 | 1999-08-12 | 2000-02-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-02-10 | 2003-08-12 | 2004-02-11 | $7700.00 | Window Closed / Lapsed |