High temperature ceramic particulate filter
Assignee: Virginia Tech Intellectual Properties Inc
•
Filing: 1991-03-28
•
Granted: 1992-02-11
•
Expires: 2011-03-28
Abstract
Abstract A high temperature ceramic filter is produced from a composition containingefractory cement, aggregate, pore forming additives, and sintering agents. The pore forming additives are synthetic or organic powders or fibers which sublimate, melt, or otherwise disintegrate to produce in situ pores in the cement during the refractory treatment of a cast filter. The filters produced are permeable to high temperature gases commonly found in a coal furnace and can be used to collect particulate matter present in those gases.
Inventors
- 👤 Sandra Gonzalez
- 👤 Nancy Brown
- 👤 Jesse J. Brown
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 08:25
CPC Classifications
B; B01; B01D; B01D39/00; B01D39/14; B01D39/20; B01D39/2068; B01D39/2072; B01D39/2075; C; C04; C04B; C04B28/00; C04B28/02; C04B28/06; C04B2111/00; C04B2111/00474; C04B2111/00793
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
172 words
A method of forming a high temperature ceramic filter, comprising the steps of: preparing a mixture of (i) refractory calcium aluminate cement, (ii) ceramic aggregate granules, and (iii) pore forming additives, said pore forming additives being sized so as to enable the creation of continuous pores from a first side to a second side of a high temperature ceramic filter, said pore forming additives constituting a small enough weight percentage of said mixture that gases will pass through said continuous pores of said high temperature ceramic filter but particulate matter in said gases will be stopped, said pore forming additives having a temperature for melting, sublimating, or otherwise disintegrating below a temperature used for firing a case of said high temperature ceramic filter; forming a cast of said high temperature ceramic filter from said mixture; and firing said case of said high temperature ceramic filter at an elevated temperature, whereby pores are formed in situ in said high temperature ceramic filter by the melting, sublimating, or disintegrating of said pore forming additives.
Claim 2
Independent Claim
172 words
A method of forming a high temperature ceramic filter, comprising the steps of: preparing a mixture of (i) refractory calcium aluminate cement, (ii) ceramic aggregate granules, and (iii) pore forming additives, said pore forming additives being sized so as to enable the creation of continuous pores from a first side to a second side of a high temperature ceramic filter, said pore forming additives constituting a small enough weight percentage of said mixture that gases will pass through said continuous pores of said high temperature ceramic filter but particulate matter in said gases will be stopped, said pore forming additives having a temperature for melting, sublimating, or otherwise disintegrating below a temperature used for firing a case of said high temperature ceramic filter; forming a cast of said high temperature ceramic filter from said mixture; and firing said case of said high temperature ceramic filter at an elevated temperature, whereby pores are formed in situ in said high temperature ceramic filter by the melting, sublimating, or disintegrating of said pore forming additives.
Claim 3
Dependent Claim
17 words
A method as recited in claim 1 wherein said mixture further comprises at least on sintering agent.
Claim 4
Dependent Claim
26 words
A method as recited in claim 1 wherein said mixture further comprises a reinforcing material selected from the group consisting of metal fibers and graphite fibers.
Claim 5
Dependent Claim
15 words
A method as recited in claim 1 wherein said pore forming additives include polymer fibers.
Claim 6
Dependent Claim
15 words
A method as recited in claim 4 wherein said pore forming additives further include naphthalene.
Claim 7
Dependent Claim
48 words
A method as recited in claim 1 wherein said step of forming a cast of said high temperature ceramic filter comprises the steps of wetting said mixture, molding said mixture in the form of sd high temperature ceramic filter, and during the wet mixture to form said cast.
Claim 8
Dependent Claim
105 words
A method as recited in claim 1 wherein said step of firing includes the steps of: heating said cast to an intermediate temperature capable of melting, sublimating or otherwise disintegrating said pore forming additives; holding said cast at said intermediate temperature for a sufficient period of time to melt, sublimate or disintegrate said pore forming additives to form a porous cast; heating said porous cast to an elevated temperature above 1000° C.; holding said porous cast at said elevated temperature for an extended period of time; and cooling said high temperature ceramic filter from said elevated temperature at a rate slow enough to prevent cracking.
Claim 9
Dependent Claim
170 words
A high temperature ceramic filter formed by the following process: preparing a mixture of (i) refractory calcium aluminate cement, (ii) ceramic aggregate granules, and (iii) pore forming additives, said pore forming additives being sized so as to enable the creation of continuous pores from a first side to a second side of a high temperature ceramic filter, said pore forming additives constituting a small enough weight percentage of said mixture that gases will pass through said continuous pores of said high temperature ceramic filter but particulate matter in said gases will be stopped, said pore forming additives having a temperature for melting, sublimating, or other wise disintegrating below a temperature used for firing a cast of said high temperature ceramic filter; forming a cast of said high temperature ceramic filter from said mixture; and firing said cast of said high temperature ceramic filter at an elevated temperature, whereby pores are formed in situ in said high temperature ceramic filter by the melting, sublimating, or disintegrating of said pore forming additives.
Claim 10
Dependent Claim
170 words
A high temperature ceramic filter formed by the following process: preparing a mixture of (i) refractory calcium aluminate cement, (ii) ceramic aggregate granules, and (iii) pore forming additives, said pore forming additives being sized so as to enable the creation of continuous pores from a first side to a second side of a high temperature ceramic filter, said pore forming additives constituting a small enough weight percentage of said mixture that gases will pass through said continuous pores of said high temperature ceramic filter but particulate matter in said gases will be stopped, said pore forming additives having a temperature for melting, sublimating, or other wise disintegrating below a temperature used for firing a cast of said high temperature ceramic filter; forming a cast of said high temperature ceramic filter from said mixture; and firing said cast of said high temperature ceramic filter at an elevated temperature, whereby pores are formed in situ in said high temperature ceramic filter by the melting, sublimating, or disintegrating of said pore forming additives.
Claim 11
Dependent Claim
18 words
A high temperature ceramic filter as recited in claim 8 formed in the shape of a candle filter.
References Cited (Backward Citations)
US907328A
Cited
US4563432A
Cited
US4629483A
Cited
US4692176A
Cited
DD246921A1
Cited
US4946487A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-02-10 | 1995-08-12 | 1996-02-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-02-10 | 1999-08-12 | 2000-02-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-02-10 | 2003-08-12 | 2004-02-11 | $7700.00 | Window Closed / Lapsed |