Vitreous compositions based on Li3 PO4 and LiPO3 as network formers and network modifiers

Claim 2

A precursor mixture corresponding to the formula: xLi.sub.2 S, yP.sub.2 S.sub.5, (1-x-y)A, zLiX; wherein: A is either Li 3 PO 4 or LiPO 3 ; X is a halide; x is a real number greater than or equal to 0 and less than or equal to 0.68; y is a real number greater than or equal to 0 and less than or equal to 0.33; x+y is a real number greater than 0 and less than 1; and z is a real number greater than or equal to 0.55 and less than or equal to 1.2.

Claim 3

The mixture of claim 1, wherein the Lix is selected from the group consisting of LiCl, LiBr, LiI, and LiF.

Claim 4

A vitreous solid composition at 25° C. formed by fusing and cooling the precursor mixture of claim 1.

Claim 5

The composition of claim 3, wherein the precursor mixture is selected from the group consisting of the formulae: a. 0.66 Li 2 S, 0.26 P 2 S 5 , 0.08 Li 3 PO 4 , 0.57 LiX; b. 0.61 Li 2 S, 0.31 P 2 S 5 , 0.08 Li 3 PO 4 , 0.62 LiX; c. 0.67 Li 2 S, 0.28 P 2 S 5 , 0.05 Li 3 PO 4 , 0.65 LiX; d. 0.14 Li 2 S, 0.23 P 2 S 5 , 0.63 Li 3 PO 4 , 0.96 LiX; e. 0.25 Li 2 S, 0.25 P 2 S 5 , 0.50 Li 3 PO 4 , 1.0 LiX; f. 0 Li 2 S, 0.20 P 2 S 5 , 0.80 Li 3 PO 4 , 1.2 LiI; g. 0.61 Li 2 S, 0.31 P 2 S 5 , 0.08 LiPO 3 , 0.62 LiX; h. 0.57 Li 2 S, 0.29 P 2 S 5 , 0.14 LiPO 3 , 0.57 LiX; i. 0.65 Li 2 S, 0.31 P 2 S 5 , 0.04 LiPO 3 , 0.58 LiX; j. 0.50 Li 2 S, 0.17 P 2 S 5 , 0.33 LiPO 3 , 0.58 LiX.

Claim 6

In an electrochemical cell employing an active anode material, an active cathode material and a vitreous solid composition at 25° C. as an electrolyte, the improvement wherein the electrolyte comprises the vitreous solid composition of claim 3.

Claim 7

The electrochemical cell of claim 5, wherein the active anode material is selected from the group consisting of lithium, silver, sodium, potassium and rubidium.

Claim 8

The electrochemical cell of claim 6, wherein the anode is lithium foil or lithium powder.

Claim 9

The electrochemical cell of claim 5, wherein the active cathode material is selected from TiS 2 , FeS 2 , Sb 2 S 3 , MoS 3 , TiS 2 +MoS 3 , poly(N-vinylpyrrolidone) (PVP)+iodine, PVP+iodine+TiS 2 , organic charge transfer complexes with halogens, and MnO 2 .

Claim 10

The electrochemical cell of claim 8, wherein the active anode material is lithium, and the cathode is a mixture of TiS 2 , a conductive agent.

Claim 11

The electrochemical cell of claim 9, wherein the anode is lithium foil or lithium powder.

Claim 12

The electrochemical cell of claim 5, wherein Li 2 S is employed as a network modifier for the vitreous composition.

Claim 13

The electrochemical cell of claim 5, wherein P 2 S 5 is employed as a network former for the vitreous composition.

Claim 14

The electrochemical cell of claim 11, wherein P 2 S 5 is employed as a network former for the vitreous composition.

Claim 15

The electrochemical cell of claim 5, wherein the cell is a microbattery having a thickness of less than 100 microns.

Claim 16

The electrochemical cell of claim 14, wherein the cell is comprised of a sputtered metal film contact supported on a substrate, a sputtered film cathode layer in contact with the metal film contact, a sputtered electrolyte layer over the cathode and contact, and a vapor deposited anode layer deposited over the electrolyte layer and a separate metal film contact.

Claim 17

The electrochemical cell of claim 15, wherein a protective layer is deposited over the electrolyte layer, and the anode layer is vapor deposited in contact with the protective layer.

Claim 18

The electrochemical cell of claim 16, wherein the contact is chromium, the cathode is comprised of TiS 2 as the active material, the anode is comprised of lithium metal as the active material, the protective layer is comprised of LiI, and the electrolyte is formed under glass-forming conditions from a precursor mixture that corresponds to the formula: 0 Li.sub.2 S, 0.20 P.sub.2 S.sub.5, 0.80 Li.sub.3 PO.sub.4, 1.2 LiI.

Claim 19

A device employing the microbattery of claim 16 as a power source.

Claim 20

A device employing the microbattery of claim 17 as a power source.

Claim 21

A vitreous composition corresponding to the formula: xLi.sub.2 S, yP.sub.2 S.sub.5, (1-x-y)Li.sub.3 PO.sub.4,zLiX; wherein: X is a halide; x is a real number greater than or equal to 0 and less than or equal to 0.68; y is a real number greater than or equal to 0.15 and less than or equal to 0.33; z is a real number greater than or equal to 0.55 and less than or equal to 1.2; and wherein, either: y is less than 0.2x+0.2, or z is greater than 1.75(1-x+y).

Claim 22

A vitreous composition corresponding to the formula: xLi.sub.2 S, yP.sub.2 S.sub.5, (1-x-y)Li.sub.3 PO.sub.4,zLiX; wherein: X is a halide; x is a real number greater than or equal to 0 and less than or equal to 0.68; y is a real number greater than or equal to 0.15 and less than or equal to 0.33; z is a real number greater than or equal to 0.55 and less than or equal to 1.2; and wherein, either: y is less than 0.2x+0.2, or z is greater than 1.75(1-x+y).

Claim 23

A vitreous composition corresponding to the formula: xLi.sub.2 S, yP.sub.2 S.sub.5, (1-x-y)LiPO.sub.3, zLiX; wherein: X is a halide; x is a real number greater than or equal to 0 and less than or equal to 0.68; y is a real number greater than or equal to 0.15 and less than or equal to 0.33; z is a real number greater than or equal to 0.55 and less than or equal to 1.2; and wherein, either: y is less than x-0.33, or z is greater than 1.75(1-x+y).

Claim 24

A vitreous composition corresponding to the formula: xLi.sub.2 S, yP.sub.2 S.sub.5, (1-x-y)LiPO.sub.3, zLiX; wherein: X is a halide; x is a real number greater than or equal to 0 and less than or equal to 0.68; y is a real number greater than or equal to 0.15 and less than or equal to 0.33; z is a real number greater than or equal to 0.55 and less than or equal to 1.2; and wherein, either: y is less than x-0.33, or z is greater than 1.75(1-x+y).