US5084334A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Void-containing polyester-type film, and its laminate
Assignee: Toyobo Co Ltd
•
Filing: 1991-04-09
•
Granted: 1992-01-28
•
Expires: 2011-04-09
Abstract
Abstract A void-containing polyester-type film is obtained by drawing a resin composition sheet consisting of a polyester, and a thermoplastic resin which is not compatible with the polyester in at least one direction. The film of this invention has a film base material consisting mainly of the polyester, fine particles consisting mainly of the thermoplastic resin which are dispersed into the film base material, and fine voids formed around the fine particles. The film of this invention has a surface layer having 3 μm or more thickness, a void percentage of 4% by volume or less in an area having 3 μm thickness from its surface, and an average void percentage of 8% by volume to 50% by volume. The film of this invention has excellent softeness, lightness, and hiding power, and excellent surface strength. The film can be used as a base material for a label, etc.
Inventors
- 👤 Akito Hamano
- 👤 Katsufumi Kumano
- 👤 Katsuya Ito
- 👤 Atsushi Taga
- 👤 Katsuaki Kuze
- 👤 Tadashi Okudaira
- 👤 Kazuhiro Hattori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 14:49
CPC Classifications
B; B29; B29C; B29C55/00; B29C55/02; B29C55/04; B32; B32B; B32B27/00; B32B27/06; B32B27/065; B32B27/16; B32B27/18; B32B27/36; B32B38/00; B32B38/0008; B32B5/00; B32B5/18; C; C08; C08J; C08J5/00; C08J5/18; C08J7/00; C08J7/04; C08J7/12; C08J7/123; B32B2305/00; B32B2305/02; B32B2305/026; B32B2367/00; C08J2367/00; C08J2367/02; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/249991
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
113 words
A void-containing polyester-type film obtained by drawing a resin composition sheet containing at least a polyester, and at least a thermoplastic resin which is not compatible with said polyester in at least one direction, wherein said polyester-type film has a film base material consisting mainly of said polyester, fine particles consisting mainly of said thermoplastic resin which are dispersed into said film base material, and fine voids formed around said fine particles, wherein the void percentage of surface layer having 3 μm thickness from the surface of said polyester-type film is 4% by volume or less, and the average void percentage of said polyester-type film is 8% by volume to 50% by volume.
Claim 2
Dependent Claim
113 words
A void-containing polyester-type film obtained by drawing a resin composition sheet containing at least a polyester, and at least a thermoplastic resin which is not compatible with said polyester in at least one direction, wherein said polyester-type film has a film base material consisting mainly of said polyester, fine particles consisting mainly of said thermoplastic resin which are dispersed into said film base material, and fine voids formed around said fine particles, wherein the void percentage of surface layer having 3 μm thickness from the surface of said polyester-type film is 4% by volume or less, and the average void percentage of said polyester-type film is 8% by volume to 50% by volume.
Claim 3
Dependent Claim
19 words
The void-containing polyester-type film of claim 1, wherein the void percentage of said surface layer is 0-3% by volume.
Claim 4
Dependent Claim
19 words
The void-containing polyester-type film of claim 1, wherein the average void percentage of said film is 8-30% by volume.
Claim 5
Dependent Claim
17 words
The void-containing polyester-type film of claim 1, wherein the thickness of said surface layer is 4-30 μm.
Claim 6
Dependent Claim
57 words
The void-containing polyester-type film of claim 1, wherein said fine particles are extended in the direction of the drawing of said sheet, the longitudinal diameter, the thickness, and the ratio of said longitudinal diameter to said thickness of said fine particles are 1 to 50 μm, 10 μm or less, and 2 μm to 100 μm, respectively.
Claim 7
Dependent Claim
35 words
The void-containing polyester-type film of claim 5, wherein the longitudinal diameter, the thickness, and the ratio of said longitudinal diameter to said thickness of said fine particles are 3-40 μm, 1-7 μm, and 3-30, respectively.
Claim 8
Dependent Claim
35 words
The void-containing polyester-type film of claim 1, wherein the average particle size of the fine particles present in said surface layer is less than that of fine particles present in other parts of said film.
Claim 9
Dependent Claim
31 words
The void-containing polyester-type film of claim 1, wherein said thermoplastic resin is contained in the amount of 1 to 40% by weight based on the total amount of said resin composition.
Claim 10
Dependent Claim
29 words
The void-containing polyester-type film of claim 8, wherein said thermoplastic resin is contained in the amount of 5-30% by weight based on the total amount of said resin composition.
Claim 11
Dependent Claim
46 words
The void-containing polyester-type film of claim 1, wherein said thermoplastic resin is at least one selected from the group consisting of polystyrene-type resins, polyolefin-type resins, polyamide-type resins, polyacrylic-type resins, cellulose-type resins, petroleum resins, synthetic rubber, natural rubber, polycarbonate resins, polysulfone-type resins, polyacrylate-type resins, and polyether-type resins.
Claim 12
Dependent Claim
25 words
The void-containing polyester-type film of claim 1, wherein said thermoplastic resin is a polystyrene-type resin having 5.0% by weight or less of a n-hexane extract.
Claim 13
Dependent Claim
24 words
The void-containing polyester-type film of claim 1, wherein said polyester is obtained by reacting mainly ethylene glycol with terephthalic acid or a derivatives thereof.
Claim 14
Dependent Claim
46 words
A laminate having an outer surface layer placed on at least one side of the void-containing polyester film of claim 1, wherein said outer surface layer is formed by applying a resin solution, a resin emulsion or a resin dispersion to said void containing polyester film.
Claim 15
Dependent Claim
59 words
The laminate of claim 13, wherein said outer surface layer is formed by treating the surface of said film with an active energy radiation treatment so that a contact angle of said treated surface with water can be 90° or less, and applying a resin solution, a resin emulsion or a resin dispersion to said void containing polyester film.
Claim 16
Dependent Claim
38 words
The laminate of claim 14, wherein said active energy radiation treatment is at least one selected from the group consisting of a corona discharge treatment, an ultraviolet radiation treatment, a plasma treatment, and an electron beam radiation treatment.
Claim 17
Dependent Claim
23 words
The laminate of claim 13, wherein said void-containing polyester film or said outer surface layer contains an antistatic agent or a conductive material.
Claim 18
Dependent Claim
82 words
A laminate having an outer surface layer placed on at least one side of the void-containing polyester-ester film of claim 1, wherein said outer surface layer is formed by treating the surface of said film with an active energy radiation treatment so that a contact angle of said treated surface with water can be 90° or less, and applying a resin solution to said treated surface, wherein the resulting film having said outer surface layer is drawn in one or two directions.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-27 | 1995-07-29 | 1996-01-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-27 | 1999-07-29 | 2000-01-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-27 | 2003-07-29 | 2004-01-28 | $7700.00 | Window Closed / Lapsed |