Low compression set, oil and fuel resistant, liquid injection moldable, silicone rubber

Claim 2

A liquid, injection moldable silicone composition comprising: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a platinum catalyst; (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes; (C) magnesium oxide; (E) cerium hydroxide or tetramethyldivinyldisilazane; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.

Claim 3

A composition according to claim 1 wherein the high viscosity vinyl-containing polysiloxane has no more than 25 mole percent phenyl radicals and has the formula ##STR4## wherein Vi stands for vinyl, R 1 is selected from the class consisting of lower alkenyl, alkyl, and aryl radicals and R is selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, R 2 is selected from the class consisting of alkyl, alkenyl, and aryl radicals, "a" varies from 100 to 10,000 and "b" varies from 0 to 300; and the low viscosity vinyl-containing has no more than 25 mole percent phenyl radicals and has the formula ##STR5## wherein R, R 1 , and R 2 are as previously defined, R 3 is selected from the class consisting of alkyl, aryl, and alkenyl radicals, "c" varies from 0 to 500 and "d" varies from 0 to 200.

Claim 4

A composition according to claim 1 wherein the magnesium oxide is present at from about 1 to about 8 parts by weight of component (A).

Claim 5

A liquid, injection moldable silicone composition comprising: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a peroxide catalyst; and (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes; (C) magnesium oxide; (E) cerium hydroxide or tetramethyldivinyldisilazane; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.

Claim 6

A liquid, injection moldable silicone composition comprising: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a peroxide catalyst; and (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes; (C) magnesium oxide; (E) cerium hydroxide or tetramethyldivinyldisilazane; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.

Claim 7

A composition according to claim 4 wherein the high viscosity vinyl-containing polysiloxane has no more than 25 mole percent phenyl radicals and has the formula ##STR6## wherein Vi stands for vinyl, R 1 is selected from the class consisting of lower alkenyl, alkyl, and aryl radicals and R is selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, R 2 is selected from the class consisting of alkyl, alkenyl, and aryl radicals, "a" varies from 100 to 10,000 and "b" varies from 0 to 300; and the low viscosity vinyl-containing has no more than 25 mole percent phenyl radicals and has the formula ##STR7## wherein R, R 1 , and R 2 are as previously defined, R 3 is selected from the class consisting of alkyl, aryl, and alkenyl radicals, "c" varies from 0 to 500 and "d" varies from 0 to 200.

Claim 8

A composition according to claim 4 wherein the magnesium oxide is present at from about 1 to about 8 parts by weight of component (A).

Claim 9

A liquid, injection moldable silicone composition comprising: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a dual peroxide catalyst system comprising a high temperature peroxide and a low temperature peroxide, the high temperature peroxide being a peroxide having a ten hour half-life of greater than 110° C. and the low temperature peroxide being a peroxide having a ten hour half-life of 100° C. or below; (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes; (C) magnesium oxide; (E) cerium hydroxide or tetramethyldivinyldisilazane; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.

Claim 10

A liquid, injection moldable silicone composition comprising: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a dual peroxide catalyst system comprising a high temperature peroxide and a low temperature peroxide, the high temperature peroxide being a peroxide having a ten hour half-life of greater than 110° C. and the low temperature peroxide being a peroxide having a ten hour half-life of 100° C. or below; (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes; (C) magnesium oxide; (E) cerium hydroxide or tetramethyldivinyldisilazane; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.

Claim 11

A composition according to claim 7 wherein the high viscosity vinyl-containing polysiloxane has no more than 25 mole percent phenyl radicals and has the formula ##STR8## wherein Vi stands for vinyl, R 1 is selected from the class consisting of lower alkenyl, alkyl, and aryl radicals and R is selected from the class consisting of monovalent hydrocarbon radicals and halogenated monovalent hydrocarbon radicals, R 2 is selected from the class consisting of alkyl, alkenyl, and aryl radicals, "a" varies from 100 to 10,000 and "b" varies from 0 to 300; and the low viscosity vinyl-containing has no more than 25 mole percent phenyl radicals and has the formula ##STR9## wherein R, R 1 , and R 2 are as previously defined, R 3 is selected from the class consisting of alkyl, aryl, and alkenyl radicals, "c" varies from 0 to 500 and "d" varies from 0 to 200.

Claim 12

A composition according to claim 7 wherein the high temperature peroxide is 2,5-dimethyl-2,5-di(T-butyl peroxy) hexane and the low temperature peroxide is 1,1-Bis(T-butyl peroxy)-3,3,3-trimethylcyclohexane.

Claim 13

A composition according to claim 7 wherein the magnesium oxide is present at from about 1 to about 8 parts by weight of component (A).

Claim 14

A process for making a liquid injection moldable silicone composition oil resistant comprising adding (C) magnesium oxide to the liquid injection moldable silicone composition, wherein the liquid injection moldable silicone composition comprises: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a catalyst selected from a platinum catalyst, a peroxide catalyst or dual peroxide catalyst system comprising a high temperature peroxide and a low temperature peroxide, the high temperature peroxide being a peroxide having a ten hour half-life of greater than 110° C. and the low temperature peroxide being a peroxide having a ten hour half-life of 100° C. or below; (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes: (E) cerium hydroxide or tetramethyldivinyldisilazane; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.

Claim 15

A process for making a liquid injection moldable silicone composition oil resistant comprising adding (C) magnesium oxide to the liquid injection moldable silicone composition, wherein the liquid injection moldable silicone composition comprises: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a catalyst selected from a platinum catalyst, a peroxide catalyst or dual peroxide catalyst system comprising a high temperature peroxide and a low temperature peroxide, the high temperature peroxide being a peroxide having a ten hour half-life of greater than 110° C. and the low temperature peroxide being a peroxide having a ten hour half-life of 100° C. or below; (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes: (E) cerium hydroxide or tetramethyldivinyldisilazane; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.

Claim 16

A process for making a liquid injection moldable silicone composition fuel resistant comprising adding to the liquid injection moldable silicone composition (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups, wherein the liquid injection moldable silicone composition comprises: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a catalyst selected from a platinum catalyst, a peroxide catalyst, or a dual peroxide catalyst system comprising a high temperature peroxide and a low temperature peroxide, the high temperature peroxide being a peroxide having a ten hour half-life of greater than 110° C. and the low temperature peroxide being a peroxide having a ten hour half-life of 100° C. or below; (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes: (C) magnesium oxide; and (E) cerium hydroxide or tetramethyldivinyldisilazane.

Claim 17

A process for making a liquid injection moldable silicone composition fuel resistant comprising adding to the liquid injection moldable silicone composition (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups, wherein the liquid injection moldable silicone composition comprises: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a catalyst selected from a platinum catalyst, a peroxide catalyst, or a dual peroxide catalyst system comprising a high temperature peroxide and a low temperature peroxide, the high temperature peroxide being a peroxide having a ten hour half-life of greater than 110° C. and the low temperature peroxide being a peroxide having a ten hour half-life of 100° C. or below; (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes: (C) magnesium oxide; and (E) cerium hydroxide or tetramethyldivinyldisilazane.

Claim 18

A process for improving the compression set of a liquid injection moldable silicone composition comprising adding (E) either cerium hydroxide or tetramethyldivinyldisilazane to the liquid injection moldable silicone composition, wherein the liquid injection moldable silicone composition comprises: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a catalyst selected from a platinum catalyst, a peroxide catalyst, or a dual peroxide catalyst system comprising a high temperature peroxide and a low temperature peroxide, the high temperature peroxide being a peroxide having a ten hour half-life of greater than 110° C. and the low temperature peroxide being a peroxide having a ten hour half-life of 100° C. or below; (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes; (C) magnesium oxide; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1: or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.

Claim 19

A process for improving the compression set of a liquid injection moldable silicone composition comprising adding (E) either cerium hydroxide or tetramethyldivinyldisilazane to the liquid injection moldable silicone composition, wherein the liquid injection moldable silicone composition comprises: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; (2) filler; and (3) a catalyst selected from a platinum catalyst, a peroxide catalyst, or a dual peroxide catalyst system comprising a high temperature peroxide and a low temperature peroxide, the high temperature peroxide being a peroxide having a ten hour half-life of greater than 110° C. and the low temperature peroxide being a peroxide having a ten hour half-life of 100° C. or below; (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes; (C) magnesium oxide; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1: or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.

Claim 20

A process for improving the compression set of a liquid injection moldable silicone composition comprising curing the composition with a dual peroxide catalytic system comprising a high temperature peroxide and a low temperature peroxide, the high temperature peroxide being a peroxide having a ten hour half-life of greater than 110° C. and the low temperature peroxide being a peroxide having a ten hour half-life of 100° C. or below, the liquid, injection moldable silicone composition comprising: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; and (2) filler: (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes: (C) magnesium oxide; (E) cerium hydroxide or tetramethyldivinyldisilazane; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.

Claim 21

A process for improving the compression set of a liquid injection moldable silicone composition comprising curing the composition with a dual peroxide catalytic system comprising a high temperature peroxide and a low temperature peroxide, the high temperature peroxide being a peroxide having a ten hour half-life of greater than 110° C. and the low temperature peroxide being a peroxide having a ten hour half-life of 100° C. or below, the liquid, injection moldable silicone composition comprising: (A) 100 parts of a first component comprising: (1) a blend of vinyl-containing liquid polysiloxanes comprising: (a) a high viscosity vinyl-containing organopolysiloxane having a viscosity of from 5000 to 1,000,000 centipoise at 25° C.; and (b) a low viscosity vinyl-containing organopolysiloxane having a viscosity of from 50 to 5000 centipoise at 25° C.; and (2) filler: (B) from 1 to 100 parts, based on 100 parts of (A), of a hydrogen silicone composition selected from the class consisting of hydrogen containing silanes and hydrogen containing polysiloxanes: (C) magnesium oxide; (E) cerium hydroxide or tetramethyldivinyldisilazane; and (D) (1) from 1 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units and SiO 2 tetrafunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1; or (2) from 20 to 50 parts by weight of an organopolysiloxane resinous copolymer comprising R 3 7 SiO 0 .5 monofunctional units, SiO 2 tetrafunctional units, and R 2 7 SiO difunctional units, where the ratio of monofunctional units to tetrafunctional units being from 0.5 to 1 to 1 to 1 and the difunctional units are present in an amount equal to about 1 to 10 mole percent based on the total number of moles of siloxy units in the copolymer; wherein R 7 is a member selected from a class of vinyl radicals and monovalent hydrocarbon radicals free of aliphatic unsaturation and wherein the resinous copolymer contains from about 2.5 to 10 mole percent of vinyl groups.