Method for production of joint sintered article of high-temperature superconductive ceramics and joint sintered article produced thereby
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1990-03-23
•
Granted: 1992-01-14
•
Expires: 2010-03-23
Abstract
Abstract A joint sintered high-temperature superconductive ceramic article is obtained by joining two sintered high-temperature superconductive ceramic masses formed of oriented crystal grains in such a manner that the directions of grain-orientation are different across the interface of union and pressing the joined ceramic masses against each other perpendicularly to the interface of union and, at the same time, heating them.
Inventors
- 👤 Norimitsu Murayama
- 👤 Shuji Sakaguchi
- 👤 Yasuharu Kodama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:44
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/80; C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/645; C04B37/00; C04B37/001; H10N60/01; H10N60/0268; C04B2235/00; C04B2235/65; C04B2235/66; C04B2235/668; C04B2237/00; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/40; C04B2237/50; C04B2237/52; C04B2237/525; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9265; Y10S428/93; Y10S505/00; Y10S505/70; Y10S505/701; Y10S505/702; Y10S505/703; Y10S505/704; Y10T; Y10T428/00; Y10T428/31
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
157 words
A joint sintered high-temperature superconductive ceramic article comprising: a first sintered mass of a high-temperature superconductive ceramic substance formed of crystal grains oriented in a first direction and having a composition of Bi 2-v Pb v Sr w Ca x Cu y O x wherein 0.25≦v≦0.50, 1.40≦w2.20, 1.60≦x≦2.40, 2.80≦y≦3.50, and 9.00≦z≦11.00; and a second sintered mass of high-temperature superconductive ceramic substance formed of crystal grains oriented in a second direction and having a composition of Bi 2-v Pb v Sr w Ca x Cu y O x wherein 0.25≦v≦0.50, 1.40≦w≦2.20, 1.60≦x≦2.40, 2.80≦y≦3.50, and 9.00≦z≦11.00; which are brought into face-to-face contact with each other so that said first and second directions of orientation differ across the interface of contact, pressed against each other in the longitudinal direction relative to the interface of contact under pressure in the range of 10 to 100 kg/cm 2 , and heated at a temperature in the range of 600° to 950° C.
Claim 2
Dependent Claim
157 words
A joint sintered high-temperature superconductive ceramic article comprising: a first sintered mass of a high-temperature superconductive ceramic substance formed of crystal grains oriented in a first direction and having a composition of Bi 2-v Pb v Sr w Ca x Cu y O x wherein 0.25≦v≦0.50, 1.40≦w2.20, 1.60≦x≦2.40, 2.80≦y≦3.50, and 9.00≦z≦11.00; and a second sintered mass of high-temperature superconductive ceramic substance formed of crystal grains oriented in a second direction and having a composition of Bi 2-v Pb v Sr w Ca x Cu y O x wherein 0.25≦v≦0.50, 1.40≦w≦2.20, 1.60≦x≦2.40, 2.80≦y≦3.50, and 9.00≦z≦11.00; which are brought into face-to-face contact with each other so that said first and second directions of orientation differ across the interface of contact, pressed against each other in the longitudinal direction relative to the interface of contact under pressure in the range of 10 to 100 kg/cm 2 , and heated at a temperature in the range of 600° to 950° C.
Claim 3
Dependent Claim
38 words
A joint sintered high-temperature superconductive ceramic article according to claim 1, wherein at least one of said values v, w, x, y and z of said first sintered mass differs from said value of said second sintered mass.
Claim 4
Dependent Claim
32 words
A joint sintered high-temperature superconductive ceramic article according to claim 1, wherein the interface of contact between said first and second sintered masses has a surface roughness of 1 μm at most.
Claim 5
Dependent Claim
31 words
A joint sintered high-temperature superconductive ceramic article according to claim 1, wherein said sintered high-temperature superconductive ceramic masses for union into said joint sintered article posses one and the same composition.
References Cited (Backward Citations)
US4975411A
Cited
US4990493A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-13 | 1995-07-15 | 1996-01-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-13 | 1999-07-15 | 2000-01-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-13 | 2003-07-15 | 2004-01-14 | $7700.00 | Window Closed / Lapsed |